Abstract
High-temperature X-ray line profile measurements were performed to maximal temperatures of 1050 °C on samples of the nickel-base superalloy SRR 99. The samples with rod axes near the [001] direction were investigated in the initially undeformed state and after creep deformation at different temperatures and stresses. For the measurements of the (002) and (020) line profiles, a special X-ray double crystal diffractometer with negligible line broadening was used which was equipped with a high-temperature vacuum chamber. The line profiles were evaluated for the lattice parameters of the matrix phase γ and the precipitated γ′ phase and for values of the lattice mismatch parallel and perpendicular to the stress axis, respectively, which were found to be different. Elastic, tetragonal distortions of the phases γ and γ′ could be determined between room temperature and about 900 °C. These distortions are thermally induced due to the different thermal expansion coefficients of the two phases and deformation induced due to interfacial dislocation networks which were built up during deformation. At the high temperatures of the X-ray measurements, at least partial recovery of the deformation-induced internal stresses occurred, depending on the temperature of the X-ray measurements. The results are discussed and compared with data obtained by complementary techniques.
Similar content being viewed by others
References
R.F. Decker and J.R. Mihalisin:Trans. AIME, 1969, vol. 62, pp. 481–89.
D.A. Grose and G.S. Ansell:Metall. Trans. A, 1981, vol. 12A, pp. 1631–45.
M.V. Nathal, R.A. MacKay, and R.G. Garlick:Mater. Sci. Eng., 1985, vol. 75, pp. 195–205.
M.V. Nathal, R.A. MacKay, and R.G. Garlick:Scripta Metall., 1988, vol. 22, pp. 1421–24.
K. Ohno, H. Harada, T. Yamagata, M. Yamazaki, and K. Ohsumi:Proc. 37th Annual Conf. on Applications of X-Ray Analysis, C.S. Barrett, J.V. Gilfrich, R. Jenkins, T.C. Huang, and P.K. Predecki, eds., Plenum Press, New York, NY, 1989, vol. 32, pp. 365–75.
H.-A. Kuhn, H. Biermann, T. Ungár, and H. Mughrabi:Acta Metall. Mater., 1991, vol. 39, pp. 2783–94.
H. Biermann, H.-A. Kuhn, T. Ungár, J. Hammer, and H. Mughrabi:Proc. 9th Int. Conf. on Strength of Metals and Alloys, Haifa, Israel, D.G. Brandon, R. Chaim, and A. Rosen, eds., Freund Publishing Company Ltd., London, 1991, vol. 1, pp. 421–28; also appeared inHigh Temp. Mater. Proc., 1993, vol. 12, pp. 21-29.
H. Mughrabi, H. Biermann, and T. Ungár:Proc. 7th Int. Symp. on Superalloys, S.D. Antolovich, R.W. Stusrud, R.A. MacKay, D.L. Anton, T. Khan, R.D. Kissinger, and D.L. Klarstrom, eds., TMS, Warrendale, PA, 1992, pp. 599–608.
H. Biermann: Doctorate Thesis, Universität Erlangen-Nürnberg, Erlangen, Germany, 1993;Röntgenographische Bestimmung von inneren Spannungen in der Nickelbasis-Superlegierung SRR 99, Fortschrittberichte VDI, Reihe 5, No. 325, VDI-Verlag, Düsseldorf, 1993.
H. Biermann, M. Strehler, and H. Mughrabi:Scripta Metall. Mater., 1995, vol. 32, pp. 1405–10.
D. Bellet and P. Bastie:Phil. Mag. B, 1991, vol. 64, pp. 143–52.
L. Müller, T. Link, and M. Feller-Kniepmeier:Scripta Metall. Mater., 1992, vol. 26, pp. 1297–1302.
U. Glatzel and A. Müller:Scripta Metall. Mater., 1994, vol. 31, pp. 285–90.
U. Glatzel:Scripta Metall. Mater., 1994, vol. 31, pp. 291–96.
U. Glatzel:Microstructure and Internal Stresses in Undeformed and Creep Deformed Samples of a Nickel-Base Superalloy, Verlag Dr. Köster, Berlin, 1994.
R.C. Ecob, M.P. Shaw, A.J. Porter, and B. Ralph:Phil. Mag. A, 1981, vol. 44, pp. 1117–33.
R.R. Keller, H.J. Maier, H. Renner, and H. Mughrabi:Scripta Metall. Mater., 1992, vol. 27, pp. 1167–72; R.R. Keller, H.J. Maier, H. Renner, and H. Mughrabi:Scripta Metall. Mater., 1993, vol. 28, p. 661.
H. Brooks:Metal Interfaces, ASM, Cleveland, OH, 1952, pp. 20–64.
A. Lasalmonie and J.L. Strudel:Phil. Mag., 1975, vol. 32, pp. 937–49.
D.F. Lahrman, R.D. Field, R. Darolia, and H.L. Fraser:Acta Metall., 1988, vol. 36, pp. 1309–20.
R.R. Keller, H.J. Maier, and H. Mughrabi:Scripta Metall. Mater., 1993, vol. 28, pp. 23–28.
G. Scheunemann-Frerker, L. Müller, and M. Feller-Kniepmeier:Phil. Mag. A, 1993, vol. 68, pp. 193–208.
J. Hammer: Doctorate Thesis, Universität Erlangen-Nürnberg, Erlangen, Germany, 1990.
U. Bayerlein: Doctorate Thesis, Universität Erlangen-Nürnberg, Erlangen, Germany, 1991; Fortschrittberichte VDI, Reihe 5, No. 236, VDI-Verlag, Düsseldorf, 1991.
R. Schmidt and M. Feller-Kniepmeier:Metall. Trans. A, 1992, vol. 23A, pp. 745–57.
M. Wilkens and K. Eckert:Z. Naturf., 1964, vol. 19a, pp. 459–70.
J.F. Ganghoffer, A. Hazotte, S. Denis, and A. Simon:Scripta Metall. Mater., 1991, vol. 25, pp. 2491–96.
T.M. Pollock and A.S. Argon:Acta Metall. Mater., 1992, vol. 40, pp. 1–30.
L. Müller, U. Glatzel, and M. Feller-Kniepmeier:Acta Metall. Mater., 1992, vol. 40, pp. 1321–27.
T. Link and M. Feller-Kniepmeier:Z Metallkd., 1987, vol. 78, pp. 617–21.
H. Mughrabi:Acta Metall., 1983, vol. 31, pp. 1367–79.
H. Mughrabi, T. Ungar, W. Kienle, and M. Wilkens:Phil. Mag. A, 1986, vol. 53, pp. 793–813.
C. Carry, S. Dermarkar, J.L. Strudel, and B.C. Wonsiewicz:Metall. Trans. A, 1979, vol. 10A, pp. 855–60.
H. Feng, H. Biermann, and H. Mughrabi: unpublished research.
R. Ramesh, R. Vasudevan, B. Pathiraj, and B.H. Kolster:J. Mater. Sci., 1992, vol. 27, pp. 270–78.
D. Bellet and P. Bastie:Phil. Mag. B, 1991, vol. 64, pp. 135–41. $
Author information
Authors and Affiliations
Additional information
Formerly with the Institut für Werkstoffwissenschaften, Lehrstuhl I, Universität Erlangen-Nürnberg.
Rights and permissions
About this article
Cite this article
Biermann, H., Strehler, M. & Mughrabi, H. High-temperature measurements of lattice parameters and internal stresses of a creep-deformed monocrystalline nickel-base superalloy. Metall Mater Trans A 27, 1003–1014 (1996). https://doi.org/10.1007/BF02649768
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02649768