The low thermal expansion ceramic system, Ca1-xSr{x}Zr4P6O24, for the compositions with x = 0, 0.25, 0.50, 0.75 and 1 was synthesized by solid-state reaction. The sintering characteristics were ascertained by bulk density measurements. The fracture surface microstructure examined by scanning electron microscopy showed the average grain size of 2.47 μm for all the compositions. The thermal expansion data for these ceramic systems over the temperature range 25–800°C is reported. The sinterability of various solid solutions and the hysteresis in dilatometric behaviour are shown to be related to the crystallographic thermal expansion anisotropy. A steady increase in the amount of porosity and critical grain size with increase in x is suggested to explain the observed decrease in the hysteresis.
Similar content being viewed by others
References
Agrawal D K and Stubican V S 1985Mater. Res. Bull. 20 99
Alamo J and Roy R 1984J. Am. Ceram. Soc. 67 C78
Alamo J and Roy R 1986J. Mater. Sci. 21 444
Cleaveland J J and Bradt R C 1978J. Am. Ceram. Soc. 61 478
Goodenough J B, Hong H Y-P and Kofalas J A 1976Mater. Res. Bull. 11 203
Harshe G, Agrawal D K and Limaye S Y 1994J. Am. Ceram. Soc. 77 1965
Hong H Y-P 1976Mater. Res. Bull. 11 173
Huang C-Y 1990Thermal expansion behaviour of sodium zirconium phosphate structure type materials, Ph.D. thesis, Pennsylvania State University, Pennsylvania
Lenain G E, McKinstry H A, Limaye S Y and Woodward A 1984Mater. Res. Bull. 19 1451
Lenain G E, McKinstry H A, Alamo J and Agrawal D K 1987J. Mater. Sci. 22 17
Limaye S Y, Agrawal D K and McKinstry H A 1987J. Am. Ceram. Soc. 70 C232
Limaye S Y, Agrawal D K, Roy R and Mehrotra Y 1991J. Mater. Sci. 26 93
Mendelson M I 1969J. Am. Ceram. Soc. 52 443
Oota T and Yamai 1986J. Am. Ceram. Soc. 69 1
Roy R, Agrawal D K, Alamo J and Roy R A 1984Mater. Res. Bull. 19 471
Srikanth V, Subbarao E C, Agrawal D K, Huang C-Y, Roy R and Rao G V 1991J. Am. Ceram. Soc. 74 365
Umarji A M, Senbhagaraman S and Radhika Rao M V 1997J. Instr. Soc. India 27 109
Wurst J C and Nelson J A 1972J. Am. Ceram. Soc. 55 109
Yamai I and Ota T 1985J. Am. Ceram. Soc. 68 273
Yamai I and Ota T 1993J. Am. Ceram. Soc. 76 487
Yvon R, Wolfgang J and Ervin P 1977J. Appl. Cryst. 10 73
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Angadi, B., Jali, V.M., Lagare, M.T. et al. Synthesis and thermal expansion hysteresis of Ca1-xSrxZr4P6O24 . Bull Mater Sci 25, 191–196 (2002). https://doi.org/10.1007/BF02711152
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02711152