Abstract
A complete literature review, critical evaluation, and thermodynamic modeling of the phase diagrams and thermodynamic properties of all oxide phases in the MgO-Al2O3, CaO-MgO-Al2O3, and MgO-Al2O3-SiO2 systems at 1 bar total pressure are presented. Optimized model equations for the thermodynamic properties of all phases are obtained that reproduce all available thermodynamic and phase equilibrium data within experimental error limits from 25 °C to above the liquidus temperatures at all compositions. The database of the model parameters can be used along with software for Gibbs energy minimization to calculate all thermodynamic properties and any type of phase diagram section. The modified quasichemical model was used for the liquid slag phase and sublattice models, based upon the compound energy formalism, were used for the spinel, pyroxene, and monoxide solid solutions. The use of physically reasonable models means that the models can be used to predict thermodynamic properties and phase equilibria in composition and temperature regions where data are not available.
Similar content being viewed by others
References
G. Eriksson, P. Wu, and A.D. Pelton: “Critical Evaluation and Optimization of the Thermodynamic Properties and Phase Diagrams of the Magnesia-Alumina, Manganese(II) Oxide-Al2O3, Ferrous Oxide-Al2O3, Sodium Oxide-Al2O3, and Potassium Oxide-Al2O3 Systems,” Calphad, 1993, 17, pp. 189–205.
B. Hallstedt: “Thermodynamic Assessment of the System MgO-Al2O3,” J. Am. Ceram. Soc., 1992, 75, pp. 1497–1507.
B. Hallstedt: “Thermodynamic Assessment of the CaO-MgO-Al2O3 System,” J. Am. Ceram. Soc., 1995, 78, pp. 193–98.
S.A. Decterov, E. Jak, P.C. Hayes, and A.D. Pelton: “Experimental Study of Phase Equilibria and Thermodynamic Optimization of the Fe-Zn-O System,” Metall. Mater. Trans. B., 2001, 32 B, pp. 643–57.
A.D. Pelton and M. Blander: “Computer-Assisted Analysis of the Thermodynamic Properties and Phase Diagrams of Slags” in Proceedings of the Second International Symposium on Metallurgical Slags and Fluxes, TMS-AIME, Warrendale, PA, 1984.
A.D. Pelton and M. Blander: “Thermodynamic Analysis of Ordered Liquid Solutions by a Modified Quasi-Chemical Approach. Application to Silicate Slags,” Metall. Trans. B, 1986, 17B, pp. 805–15.
A. D. Pelton, S.A. Decterov, G. Eriksson, C. Robelin, and Y. Dessureault: “The Modified Quasichemical Model. I—Binary Solutions,” Metall. Mater. Trans. B, 2000, 31B, pp. 651–59.
A.D. Pelton and P. Chartrand: “The Modified Quasichemical Model. II—Multicomponent Solutions,” Metall. Mater. Trans. A, 2001, 32A, pp. 1355–60.
P. Wu, G. Eriksson, and A.D. Pelton: “Critical Evaluation and Optimization of the Thermodynamic Properties and Phase Diagrams of the Calcia-Iron(II) Oxide, Calcia-Magnesia, Calcia-Manganese(II) Oxide, Iron(II) Oxide-Magnesia, Iron(II) Oxide-Manganese(II) Oxide, and Magnesia-Manganese(II) Oxide Systems,” J. Am. Ceram. Soc., 1993, 76, pp. 2065–75.
G. Eriksson and A.D. Pelton: “Critical Evaluation and Optimization of the Thermodynamic Properties and Phase Diagrams of the CaO-Al2O3, Al2O3-SiO2, and CaO-Al2O3-SiO2 Systems,” Metall. Trans., 1993, 24B, pp. 807–16.
P. Wu, G. Eriksson, A.D. Pelton, and M. Blander: “Prediction of the Thermodynamic Properties and Phase Diagrams of Silicate Systems: Evaluation of the FeO-MgO-SiO2 System,” ISIJ Inter., 1993, 33, pp. 26–35.
A.D. Pelton: “A General ‘Geometric’ Thermodynamic Model for Multicomponent Solutions,” Calphad, 2001, 25, pp. 319–28.
M. Hillert, B. Jansson, and B. Sundman: “Application of the Compound-Energy Model to Oxide Systems,” Z. Metallkd., 1988, 79, pp. 81–87.
H.S.C. O’Neill and A. Navrotsky: “Cation Distributions and Thermodynamic Properties of Binary Spinel Solid Solutions,” Am. Mineral., 1984, 69, pp. 733–53.
S.A. Decterov, I.-H. Jung, Y.-B. Kang, E. Jak, V. Swamy, D. Kevorkov, and A.D. Pelton: “Report for Oxide Database Development,” CRCT, Ecole Polytechnique, Montreal, 2002.
N. Morimoto: “Nomenclature of Pyroxenes,” Mineral. Mag., 1988, 52, pp. 535–50.
P. Shi, S.K. Saxena, Z. Zang, and B. Sundman: “Thermodynamics of the Ca-Mg-Fe-Al-Si-O Pyroxenes: 1. Theoretical Model and Assessment of the Ca-Mg-Si-O System,” Calphad, 1994, 18, pp. 47–69.
I.-H. Jung, S.A. Decterov, and A.D. Pelton: “Critical Thermodynamic Evaluation and Optimization of the CaO-MgO-SiO2 System,” J. Eur. Ceram. Soc., 2003 (in press).
www.factsage.com, 2002.
I.-H. Jung, S.A. Decterov, and A.D. Pelton: “Thermodynamic Modeling of the CaO-MgO-Al2O3-SiO2 System,” in preparation.
G.A. Rankin and H.E. Merwin: “The Ternary System CaO-Al2O3-MgO,” J. Am. Chem. Soc., 1916, 38, pp. 568–88.
A.M. Alper, R.N. McNally, P.H. Ribbe, and R.C. Doman: “The System MgO-MgAl2O4,” J. Am. Ceram. Soc., 1962, 45, pp. 263–68.
D. Viechnicki, F. Schmid, and J.W. Mccauley: “Liquidus-Solidus Determinations in the System MgAl2O4-Al2O3,” J. Am. Ceram. Soc., 1974, 57, pp. 47–48.
W.P. Whitney and V.S. Stubican: “Interdiffusion in the System MgO-MgAl2O4,” J. Am. Ceram. Soc., 1971, 54, pp. 349–52.
V.S. Stubican and R. Roy: “Mechanism of the Precipitation of the Spinel from MgO-Al2O3 Solid Solutions,” J. Phys. Chem. Solids, 1965, 26, pp. 1293–97.
A.F. Henriksen and W.D. Kingery: “The Solid Solubility of Sc2O3, Al2O3, Cr2O3, SiO2 and ZrO2 in MgO,” Ceramurgia Int., 1979, 5, pp. 11–17.
T. Mori: “Solubility of Aluminum Oxide in Magnesium Oxide,” Yogyo Kyokaishi, 1982, 90, pp. 551–52.
A.S. Frenkel, K.M. Shmukler, D.Ya. Sukharevskij, and N.V. Gul’ko: Dokl. Akad. Nauk SSSR, 1960, 130, pp. 1095–98.
H.U.B. Viertel and F.K. Seifert: “Thermal Stability of Defect Spinels in the System MgAl2O4-Al2O3,” N. Jb. Miner. Abh., 1980, 140, pp. 89–101.
A. Navrotsky, B. Wechsler, K. Geisinger, and F. Seifert: “Thermochemistry of MgAl2O4-Al8/3O4 Defect Spinels,” J. Am. Ceram. Soc., 1986, 69, pp. 418–422.
A.M. Lejus: “Sur la Formation à Haute Température de Spinelles non Stoechiométriques et de Phases Dérivées,” Revue Int. Haut. Temp. Refract., 1964, 1, pp. 53–95 (in French).
D.M. Roy, R. Roy, and E.F. Osborn: “The System MgO-Al2O3-H2O and Influence of Carbonate and Nitrate Ions on the Phase Equilibria,” Am. J. Sci., 1953, 251, pp. 337–61.
K. Shirasuka and G. Yamaguchi: “Precise Measurement of the Crystal Data and the Solid Solution Range of the Defective Spinel Magnesium Oxide.n (Aluminum Oxide),” Yogyo Kyokaishi, 1974, 82, pp. 34–37.
H. Saalfeld and H. Jagodzinski: “Segregation of Mg-Al Spinels With an Excess of Al2O3,” Z. Krist., 1957, 109, pp. 87–109.
A.M. Lejus and R. Collongues: “Sur la Formation à Haute Température de Phases Type Alumine δ dans Plusieurs Systemes à Base d’Alumine,” Acad. Sci., 1962, pp. 2780–2781 (in French).
Y. Chiang and W.D. Kingery: “Grain-Boundary Migration in Nonstoichiometric Solid Solutions of Magnesium Aluminate Spinel: Grain Growth Studies,” J. Am. Ceram. Soc., 1989, 72, pp. 271–77.
K. Fujii, T. Nagasaka, and M. Hino: ISIJ Int., 2000, 40, pp. 1059–66.
S.K. Roy and R.L. Coble: “Solubilities of Magnesia, Titania, and Magnesium Titanate in Aluminum Oxide,” J. Am. Ceram. Soc., 1968, 51, pp. 1–6.
K. Ando and M. Momoda: “Solubility of Magnesium Oxide in Single-Crystal Aluminum Oxide,” J. Ceram. Soc. Jpn. Int. Ed., 1987, 95, pp. 343–47.
E.G. King: “Heat Capacities at Low Temperatures and Entropies at 298.16 K of Crystalline Calcium and Magnesium Aluminates,” J. Phys. Chem., 1955, 59, pp. 218–19.
K.R. Bonnickson: “High Temperature Heat Contents of Aluminates of Calcium and Magnesium,” J. Phys. Chem., 1955, 59, pp. 220–21.
Ya.A. Landa and I.A. Naumova: “Determining the Enthalpy and Specific Heat of Magnesia Spinels in the Range 1400–2200 K,” Ogneupory, 1979, pp. 9–12.
P. Richet and G. Fiquet: “High-Temperature Heat Capacity and Premelting of Minerals in the System MgO-CaO-Al2O3-SiO2,” J. Geophys. Res., 1991, 96, pp. 445–56.
T.V. Charlu, R.C. Newton, and O.J. Kleppa: “Enthalpies of Formation of 970 K of Compounds in the System Magnesia-Alumina Silica from High Temperature Solution Calorimetry,” Geochim. Cosmochim. Acta, 1975, 39, pp. 1487–97.
J.A. Shearer and O.J. Kleppa: “Enthalpies of Formation of Spinel (MgAl2O4), Pyroxene (MgSiO3), Olivine (Mg2SiO4). Kyanite (Al2SiO5), and Sillimanite (Al2SiO5) by Oxide Melt Solution Calorimetry,” J. Inorg. Nucl. Chem., 1973, 35, pp. 1073–78.
A. Navrotsky and O.J. Kleppa: “Thermodynamics of Formation of Simple Spinels,” J. Inorg. Nucl. Chem., 1968, 30, pp. 479–98.
K.T. Jacob and K.P.W.Y. Jayadevan: “Electrochemical Determination of the Gibbs Energy of Formation of MgAl2O4,” J. Am. Ceram. Soc., 1998, 81, pp. 209–12.
L. Chamberlin, J.R. Beckett, and E. Stolper: “Palladium Oxide Equilibration and the Thermodynamic Properties of MgAl2O4 Spinel,” Am. Mineral., 1995, 80, pp. 285–96.
R.W. Taylor and H. Schmalzried: “The Free Energy of Formation of Some Titanates, Silicates, and Magnesium Aluminate From Measurements Made With Galvanic Cells Involving Solid Electrolytes,” J. Phys. Chem., 1964, 68, pp. 2444–49.
E. Rosen and A. Muan: “Stability of MgAl2O4 at 1400°C as Derived from Equilibrium Measurements in CoAl2O4-MgAl2O4 Solid Solutions,” J. Am. Ceram. Soc., 1966, 49, pp. 107–08.
K. Grjøtheim, O. Herstad, and J.M. Toguri: Can. J. Chem. 1961, 39, pp. 443–50.
R.L. Altman: “Vaporization of Magnesium Oxide and its Reaction with Alumina,” J. Phys. Chem., 1963, 67, pp. 366–69.
T. Sasamoto, H. Hara, and T. Sata: “Mass-Spectrometric Study of the Vaporization of Magnesium Oxide from Magnesium Aluminate Spinel,” Bull. Chem. Soc. Jpn., 1981, 54, pp. 3327–33.
J.M. McHale, A. Auroux, A.J. Perrotta, and A. Navrotsky: “Surface Energies and Thermodynamic Phase Stability in Nanocrystalline Aluminas,” Science (Washington, DC), 1997, 277, pp. 788–91.
T. Yamanaka and Y. Takeuchi: “Order-Disorder Transition in MgAl2O4 Spinel at High Temperatures up to 1700 °C,” Z. Kristallogr., 1983, 165, pp. 65–78.
R.C. Peterson, G.A. Lager, and R.L. Hitterman: “A Time-of-Flight Neutron Powder Diffraction Study of MgAl2O4 at Temperature up to 1273 K,” Am. Mineral., 1991, 76, pp. 1455–58.
S.A.T. Redfern, R. Harrison, H.St.C. O’Neill, and D.R.R. Wood: “Thermodynamics and Kinetics of Cation Ordering in MgAl2O4 Spinel up to 1600 °C from in Situ Neutron Diffraction.” Am. Mineral., 1999, 84, pp. 299–310.
H. Maekawa, S. Kato, K. Kawamura, and T. Yokokawa: “Cation Mixing in Natural MgAl2O4 Spinel: A High-Temperature 27Al NMR Study,” Am. Mineral., 1997, 82, pp. 1125–32.
B.J. Wood, R.J. Kirkpatrick, and B. Montez: “Order-Disorder Phenomena in MgAl2O4 Spinel,” Am. Mineral., 1986, 71, pp. 999–1006.
R.L. Millard, R. Peterson, and B.K. Hunter: “Temperature Dependence of Cation Disorder in MgAl2O4 Spinel Using 27Al and 17O Magic-Angle Spinning NMR,” Am. Mineral., 1992, 77, pp. 44–52.
G.B. Andreozzi, F. Princivalle, H. Skogby, and A.D. Giusta: “Cation Ordering and Structural Variations With Temperature in MgAl2O4 Spinel: An X-ray Single-Crystal Study,” Am. Mineral., 2000, 85, pp. 1164–71.
A. Navrotsky: “Cation Distribution Energies and Heats of Mixing in MgFe2O4-MgAl2O4-ZnFe2O3-ZnAl2O4. and NiAl2O4-ZnAl2O4 Spinels: Study by High-Temperature Calorimetry,” Am. Mineral., 1986, 71, pp. 1160–69.
K. Grjotheim, O. Herstad, and J.M. Toguri: “The Aluminum Reduction of Magnesium Compounds,” Can. Min. Metall., 1962, pp. 396–99.
J.H. Welch: “Ternary Compound Formation in the System CaO-Al2O3-MgO,” Nature, 1961, 4788, pp. 559–60.
A.J. Majumdar: “The Quaternary Phase in High-Alumina Cement,” Trans. J Br. Ceram. Soc., 1964, 63, pp. 347–64.
M.R. Rao: “Liquidus Relations in the Quaternary Subsystem CaAl2O4-CaAl4O7-Ca2Al2SiO7-MgAl2O4,” J. Am. Ceram. Soc., 1968, 51, pp. 50–54.
M.T. Melnik, A.A. Kachura, and N.V. Mokritskaya: “Phase Diagram of the Calcium Aluminate-Magnesium Aluminate-Magnesia (CaO-Al2O3-MgO-Al2O3-MgO,” Ogneupory, 1989, 4, pp. 27–28.
A.H. De Aza, P. Pena, and S. De Aza: “Ternary System Al2O3-MgO-CaO: I: Primary Phase Field of Crystallization of Spinel in the Subsystem MgAl2O4-CaAl4O7-CaO-MgO,” J. Am. Ceram. Soc., 1999, 82, pp. 2193–203.
A.H. De Aza, J.E. Iglesias, P. Pena, and S. De Aza: “Ternary System Al2O3-MgO-CaO: Part II, Phase Relationships in the Subsystem Al2O3-MgAl2O4-CaAl4O7,” J. Am. Ceram. Soc., 2000, 83, pp. 919–27.
M. Göbbels, E. Woermann, and J. Jung: “The Al-Rich Part of the System CaO-Al2O3-MgO. Part I. Phase Relationships,” J. Solid State Chem., 1995, 120, pp. 358–63.
N. Iyi, M. Göbbels, and Y. Matsui: “The Al-Rich Part of the System CaO-Al2O3-MgO. Part II. Structure Refinement of Two New Magnetoplumbite-Related Phases,” J. Solid State Chem., 1995, 120, pp. 364–71.
H. Ohta and H. Suito: “Activities in CaO-MgO-Al2O3 Slags and Deoxidation Equilibria of Al, Mg, and Ca,” ISIJ, 1996, 36, pp. 983–90.
M. Hino, S. Kinoshita, Y. Ehara, H. Itoh, and S. Ban-Ya: “Activity Measurement of the Constituents in Secondary Steelmaking Slag” in Proc. 5th Int. Sympos. Metall. Slags and Fluxes, 1997, pp. 53–57.
M. Allibert, C. Chatillon, and R. Lourtau: Rev Int. Hautes Temp. Refract., 1979, 16, pp. 33–37.
R.W. Nurse, J.H. Welch, and A.J. Majumdar: “The CaO-Al2O3 System in a Moisture-Free Atmosphere,” Trans. Brit. Ceram. Soc., 1965, 64, pp. 409–18.
J.W. Greig: “Immiscibility in Silicate Melts. Part I,” Am. J. Sci., 5th Ser., 1927, 13, pp. 1–44.
G.A. Rankin and H.E. Merwin: “The Ternary System MgO-Al2O3-SiO2,” Am. J. Sci., 1918, 45, pp. 301–25.
W. Schreyer and J.F. Schairer: “Stable and Metastable Phase Relations in the System MgO-Al2O3-SiO2,” Carnegie Inst. of Washington, 1961, Yb. 60, pp. 144–47.
W.J. Schreyer and J.F. Schairer: “Compositions and Structural States of Anhydrous Mg-Cordierites: A Re-investigation of the Central Part of the System MgO-Al2O3-SiO2,” J. Petrol., 1961, 2, pp. 324–406.
M.L. Keith and J.F. Schairer: “The Stability Field of Sapphirine in the System MgO-Al2O3-SiO2,” J. Geol., 1952, 60, pp. 181–86.
S. Aramaki and R. Roy: “The Mullite-Corundum Boundary in the Systems MgO-Al2O3-SiO2 and CaO-Al2O3-SiO2,” J. Am. Ceram. Soc., 1961, 42, pp. 644–45.
C.M. Schlaudt and D.M. Roy: “Crystalline Solution in the System MgO-Mg2SiO4-MgAl2O4,” J. Am. Ceram. Soc., 1965, 48, pp. 248–51.
K. Onuma and M. Arita: “Magnesium Silicate-Magnesium Aluminum Silicate (MgSiO3-MgAl2SiO6) Join and the Solubility of Aluminum Oxide in Enstatite at Atmospheric Pressure,” Ganseki Kobutsu Kosho Gakkaishi, 1975, 70, pp. 53–60.
P. Anastasiou and F. Seifert: “Solid Solubility of Aluminum Oxide in Enstatite at High Temperatures and 1–5 kbars Water Pressure,” Contrib. Mineral. Petrol., 1972, 34, pp. 272–87.
R.M. Smart and F.P. Glasser: “The Subsolidus Phase Equilibria and Melting Temperatures of MgO-Al2O3-SiO2 Compositions,” Ceram. Int., 1981, 7, pp. 90–97.
E.F. Osborn and A. Muan: Phase Equilibrium Diagrams of Oxide Systems, The American Ceramic Society and the Edward Orton Jr. Ceramic Foundation, Columbus, OH, 1960.
W.R. Foster: “Synthetic Sapphirine and Its Stability Relations in the System MgO-Al2O3-SiO2,” J. Am. Ceram. Soc., 1950, 33, pp. 73–84.
S. Sakai and T. Kawasaki: “Phase Relations for Mg3Al2Si3O12 (Pyrope Composition) in the System MgO-Al2O3-SiO2 at Atmospheric Pressure,” Ganko, 1998, 93, pp. 18–26.
R.M. Smart and F.P. Glasser: “Phase Relations of Cordierite and Sapphirine in the System MgO-Al2O3-SiO2,” J. Mater. Sci., 1976, 11, pp. 1459–64.
W.W. Weller and K.K. Kelley: “Low-Temperature Heat Capacities and Entropies at 298.15 K of Akermanite, Cordierite, Gehlenite, and Merwinite,” U.S. Bureau of Mines, Report of Investigation, 1963.
C.A. Geiger and H. Voigtlander: “The Heat Capacity of Synthetic Anhydrous Mg and Fe Cordierite,” Contrib. Mineral. Petrol., 2000, 138, pp. 46–50.
R. Mueller, R. Naumann, and S. Reinsch: “Surface Nucleation of μ.-Cordierite in Cordierite Glass: Thermodynamic Aspects,” Thermochim. Acta, 1996, 280/281 (Vitrification, Transformation and Crystallization of Glasses), pp. 191–204.
B.N. Roy and A. Navrotsky: “Thermochemistry of Charge-Coupled Substitutions in Silicate Glasses: The Systems MAlO2-SiO2 (M=Li,Na,K.Rb,Cs,Mg,Ca,Sr,Ba,Pb),” J. Am. Ceram. Soc., 1984, 67, pp. 606–10.
P. Courtial and P. Richet: “Heat Capacity of Magnesium Aluminosilicate Melts,” Geochim. Cosmochim. Acta, 1993, 57, pp. 1267–75.
R.H. Rein and J. Chipman: “Activities in the Liquide Solution SiO2-CaO-MgO-Al2O3 at 1600 °C,” TMS-AIME, 1965, 233, pp. 415–25.
D. Henderson and J. Taylor: “Thermodynamic Properties in the CaO-MgO-SiO2 and MgO-Al2O3-SiO2 Systems,” J. Iron Steel Inst., 204, 1966, pp. 41–45.
R.G. Berman: “Internally-Consistent Thermodynamic Data for Minerals in the System Sodium Oxide-Potassium Oxide-Calcium Oxide-Magnesium Oxide-Iron Oxide(FeO)-Iron Oxide(Fe2O3)-Alumina-Silica-Titania-Water-Carbon Dioxide,” J. Petrol., 1988, 29, pp. 445–522.
S. Aramaki and R. Roy: J. Am. Ceram. Soc., 1959, 42, pp. 644–45.
A.T. Prince: “Liquidus Relations on 10% MgO Plane of the System Lime-Magnesia-Alumina-Silica,” J. Am. Ceram. Soc., 1954, 37, pp. 402–08.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Jung, IH., Decterov, S.A. & Pelton, A.D. Critical thermodynamic evaluation and optimization of the MgO-Al2O3, CaO-MgO-Al2O3, and MgO-Al2O3-SiO2 Systems. J Phs Eqil and Diff 25, 329–345 (2004). https://doi.org/10.1007/s11669-004-0151-4
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/s11669-004-0151-4