Synthesis, characterization and life cycle assessment of electrochemically exfoliated KOH-activated holey graphene

  • Research Article
  • Published:
Frontiers of Environmental Science & Engineering Aims and scope Submit manuscript

Abstract

Graphene materials have drawn tremendous attention in recent years. The formation of holes and pores on graphene sheets can provide transfer channels and facilitate the ion/electron transport kinetics. In this study, graphene nanosheets were prepared electrochemically, and then, they were used as the starting material for the preparation of holey graphene (HG) through the KOH activation process. The weight ratio of initial electrochemically exfoliated graphene (EEG) to KOH was optimized according to the morphological features, BET surface area examination, graphene number of layers calculated from XRD patterns, and the ID/IG ratio obtained from Raman analysis. Results showed that increasing the KOH amount led to the achievement of higher values of ID/IG and surface area and less re-stacking of graphene sheets which occurs because of the heat treatment process. The environmental burdens of the production routes for the preparation of EEG and HG were investigated by cradle-to-gate life cycle assessment (LCA). The LCA results of EEG production indicated that electricity with the contributions of 94%, 91%, 82%, and 75% of the total impact in four environmental categories, including fossil fuel depletion, ozone depletion, global warming, and smog was the main environmental weakness. In the pore generation process, KOH was recognized as the biggest contributor (about 51% to 83% of the total impact) in six impact categories, including ozone depletion, non-carcinogenics, smog, global warming, carcinogenics, and eutrophication which could be attributed to its high consumption amount (21.9 kg). This work offers environmental considerations for the development of sustainable graphene materials.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  • Aghamohammadi H, Eslami-Farsani R (2020). An experimental investigation on the sulfur and nitrogen co-doping and oxidation of prepared graphene by electrochemical exfoliation of pencil graphite rods. Ceramics International, 46(18): 28860–28869

    Article  CAS  Google Scholar 

  • Aghamohammadi H, Hassanzadeh N, Eslami-Farsani R (2021a). A review study on titanium niobium oxide-based composite anodes for Li-ion batteries: synthesis, structure, and performance. Ceramics International, 47(19): 26598–26619

    Article  CAS  Google Scholar 

  • Aghamohammadi H, Hassanzadeh N, Eslami-Farsani R (2021b). A review study on the recent advances in developing the heteroatom-doped graphene and porous graphene as superior anode materials for Li-ion batteries. Ceramics International, 47(16): 22269–22301

    Article  CAS  Google Scholar 

  • Arvidsson R, Kushnir D, Sandén B A, Molander S (2014). Prospective life cycle assessment of graphene production by ultrasonication and chemical reduction. Environmental Science & Technology, 48(8): 4529–4536

    Article  CAS  Google Scholar 

  • Bare J C (2012). Tool for the reduction and assessment of chemical and other environmental impacts (TRACI) TRACI version 2.1. Washington, DC: United States Environmental Protection Agency

    Google Scholar 

  • Bare J C, Hofstetter P, Pennington D W, Udo de Haes H A (2000). Midpoints versus endpoints: the sacrifices and benefits. International Journal of Life Cycle Assessment, 5(6): 319–326

    Article  Google Scholar 

  • Chen Z, Zhang M, Wang Y, Yang Z, Hu D, Tang Y, Yan K (2021). Controllable synthesis of nitrogen-doped porous carbon from metal-polluted miscanthus waste boosting for supercapacitors. Green Energy & Environment, 6(6): 929–937

    Article  CAS  Google Scholar 

  • Coroş M, Pogăcean F, Roşu M C, Socaci C, Borodi G, Mageruşan L, Biriş A R, Pruneanu S (2016). Simple and cost-effective synthesis of graphene by electrochemical exfoliation of graphite rods. RSC Advances, 6(4): 2651–2661

    Article  Google Scholar 

  • Cossutta M, McKechnie J, Pickering S J (2017). Comparative LCA of different graphene production routes. Green Chemistry, 19(24): 5874–5884

    Article  CAS  Google Scholar 

  • Ferrari A C, Basko D M (2013). Raman spectroscopy as a versatile tool for studying the properties of graphene. Nature Nanotechnology, 8(4): 235–246

    Article  CAS  Google Scholar 

  • Ferrari A C, Meyer J C, Scardaci V, Casiraghi C, Lazzeri M, Mauri F, Piscanec S, Jiang D, Novoselov K S, Roth S, Geim A K (2006). Raman spectrum of graphene and graphene layers. Physical Review Letters, 97(18): 187401

    Article  CAS  Google Scholar 

  • Guinée J B, Heijungs R, Huppes G, Zamagni A, Masoni P, Buonamici R, Ekvall T, Rydberg T (2011). Life cycle assessment: past, present, and future. Environmental Science & Technology, 45(1): 90–96

    Article  Google Scholar 

  • Hassanzadeh N, Sadrnezhaad S K (2021). Magnetic stirring assisted hydrothermal synthesis of Na3MnCO3PO4 cathode material for sodium-ion battery. Ceramics International, 47(19): 26929–26934

    Article  CAS  Google Scholar 

  • Hassanzadeh N, Sadrnezhaad S K, Chen G (2016a). Ball mill assisted synthesis of Na3MnCO3PO4 nanoparticles anchored on reduced graphene oxide for sodium ion battery cathodes. Electrochimica Acta, 220: 683–689

    Article  CAS  Google Scholar 

  • Hassanzadeh N, Sadrnezhaad S K, Chen G (2016b). In-situ hydrothermal synthesis of Na3MnCO3PO4/rGO hybrid as a cathode for Na-ion battery. Electrochimica Acta, 208: 188–194

    Article  CAS  Google Scholar 

  • Li Y, Zhang Y, Xia G, Zhan J, Yu G, Wang Y (2021). Evaluation of the technoeconomic feasibility of electrochemical hydrogen peroxide production for decentralized water treatment. Frontiers of Environmental Science & Engineering, 15(1): 1

    Article  Google Scholar 

  • Lillo-Ródenas M A, Juan-Juan J, Cazorla-Amorós D, Linares-Solano A (2004). About reactions occurring during chemical activation with hydroxides. Carbon, 42(7): 1371–1375

    Article  Google Scholar 

  • Liu J, Poh C K, Zhan D, Lai L, Lim S H, Wang L, Liu X, Sahoo N G, Li C, Shen Z, et al. (2012). Improved synthesis of graphene flakes from the multiple electrochemical exfoliation of graphite rod. Nano Energy, 2(3): 337–386

    Google Scholar 

  • Liu T, Zhang L, Cheng B, Hu X, Yu J (2020). Holey graphene for electrochemical energy storage. Cell Reports. Physical Science, 1(10): 100215

    CAS  Google Scholar 

  • Liu X, You S, Ma F, Zhou H (2021). Characterization of electrode fouling during electrochemical oxidation of phenolic pollutant. Frontiers of Environmental Science & Engineering, 15(4): 53

    Article  CAS  Google Scholar 

  • Lokhande A C, Qattan I A, Lokhande C D, Patole S P (2020). Holey graphene: an emerging versatile material. Journal of Materials Chemistry. A, Materials for Energy and Sustainability, 8(3): 918–977

    CAS  Google Scholar 

  • Mozaffarpour F, Hassanzadeh N, Vahidi E (2022). Comparative life cycle assessment of synthesis routes for cathode materials in sodium-ion batteries. Clean Technologies and Environmental Policy, 24(10): 3319–3330

    Article  CAS  Google Scholar 

  • Muhsan A A, Lafdi K (2019). Numerical study of the electrochemical exfoliation of graphite. SN Applied Sciences, 1(3): 276

    Article  CAS  Google Scholar 

  • Munuera J, Britnell L, Santoro C, Cuéllar-Franca R, Casiraghi C (2022). A review on sustainable production of graphene and related life cycle assessment. 2D Materials, 9(1): 012002

    Article  CAS  Google Scholar 

  • Nanaji K, Sarada B V, Varadaraju U V, N Rao T, Anandan S (2021). A novel approach to synthesize porous graphene sheets by exploring KOH as pore inducing agent as well as a catalyst for supercapacitors with ultra-fast rate capability. Renewable Energy, 172: 502–513

    Article  CAS  Google Scholar 

  • Pishgahinejad S, Aghamohammadi H, Hassanzadeh N (2023). Copper-coated graphite electrodes for the facile preparation of copper oxide particles anchored on functionalized holey graphene sheets. Journal of Electroanalytical Chemistry (Lausanne, Switzerland), 931: 117204

    CAS  Google Scholar 

  • Rajput N S, Al Zadjali S, Gutierrez M, Esawi A M K, Al Teneiji M (2021). Synthesis of holey graphene for advanced nanotechnological applications. RSC Advances, 11(44): 27381–27405

    Article  CAS  Google Scholar 

  • Su C Y, Lu A Y, Xu Y, Chen F R, Khlobystov A N, Li L J (2011). High-quality thin graphene films from fast electrochemical exfoliation. ACS Nano, 5(3): 2332–2339

    Article  CAS  Google Scholar 

  • Wang J, Kaskel S (2012). KOH activation of carbon-based materials for energy storage. Journal of Materials Chemistry, 22(45): 23710–23725

    Article  CAS  Google Scholar 

  • Wang Y, Liu Y, Chen Z, Zhang M, Liu B, Xu Z, Yan K (2022). In situ growth of hydrophilic nickel-cobalt layered double hydroxides nanosheets on biomass waste-derived porous carbon for high-performance hybrid supercapacitors. Green Chemical Engineering, 3(1): 55–63

    Article  Google Scholar 

  • Xu L, Lv W, Shi K, Xiao S, You C, He Y B, Kang F, Yang Q H (2019). Holey graphenes as the conductive additives for LiFePO4 batteries with an excellent rate performance. Carbon, 149: 257–262

    Article  CAS  Google Scholar 

  • Yan K, Li R, Yang Z, Li X, Wang Y, Wu G (2021). Biomass waste-derived porous carbon efficient for simultaneous removal of chlortetracycline and hexavalent chromium. iScience, 24(5): 102421

    Article  CAS  Google Scholar 

  • Yu P, Lowe S E, Simon G P, Zhong Y L (2015). Electrochemical exfoliation of graphite and production of functional graphene. Current Opinion in Colloid & Interface Science, 20(5–6): 329–338

    Article  CAS  Google Scholar 

  • Zeng G, Liu Y, Ma X, Fan Y (2021). Fabrication of magnetic multi-template molecularly imprinted polymer composite for the selective and efficient removal of tetracyclines from water. Frontiers of Environmental Science & Engineering, 15(5): 107

    Article  CAS  Google Scholar 

  • Zhang W, Han B, Tufa R A, Tang C, Liu X, Zhang G, Chang J, Zhang R, Mu R, Liu C, et al. (2022). Tracing the impact of stack configuration on interface resistances in reverse electrodialysis by in situ electrochemical impedance spectroscopy. Frontiers of Environmental Science & Engineering, 16(4): 46

    Article  Google Scholar 

  • Zhao S, Chen C, Ding J, Yang S, Zang Y, Ren N (2022). One-pot hydrothermal fabrication of BiVO4/Fe3O4/rGO composite photocatalyst for the simulated solar light-driven degradation of Rhodamine B. Frontiers of Environmental Science & Engineering, 16(3): 36

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Faculty of Materials Science and Engineering, K.N. Toosi University of Technology, Tehran, 1969764499, Iran

    Fatemeh Mozaffarpour & Nafiseh Hassanzadeh

  2. Department of Mining and Metallurgical Engineering, Mackay School of Earth Sciences and Engineering, University of Nevada, Reno, NV, 89557, USA

    Ehsan Vahidi

Authors
  1. Fatemeh Mozaffarpour
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Nafiseh Hassanzadeh
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Ehsan Vahidi
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Nafiseh Hassanzadeh.

Additional information

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Highlights

• Electrochemically exfoliated graphene (EEG) was prepared from pencil graphite rods.

• Holey graphene (HG) was prepared from EEG via the KOH activation process.

• SSA was increased with the increase of KOH amount, because of pore generation.

• In EEG production, electricity and H2SO4 have the highest environmental impact.

• In HG production, KOH and graphene have the highest environmental impact.

Supporting Materials

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Mozaffarpour, F., Hassanzadeh, N. & Vahidi, E. Synthesis, characterization and life cycle assessment of electrochemically exfoliated KOH-activated holey graphene. Front. Environ. Sci. Eng. 17, 155 (2023). https://doi.org/10.1007/s11783-023-1755-4

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s11783-023-1755-4

Keywords

Search

Navigation