Abstract
This article investigated the saturated solubility of MgO in converter vanadium slag and its influencing factors. The experimental results of MgO dissolution equilibrium are consistent with the theoretical calculation results. The results show that in MgO saturated vanadium slag, MgO mainly exists in MgV2O4 and MgSiO3. The increase of V2O3 content or the decrease of the FeO/SiO2 ratio is beneficial to increasing the saturated solubility of MgO in the FeO-SiO2-V2O3 slag system. The saturated solubility of MgO in vanadium slag increases from 7.5 to 8.0 wt.% when the temperature increases from 1633 to 1753 K. In addition, the solubility of MgO also increases with the increase of TiO2 and Al2O3 content and decreases with the increase of MnO content.
Similar content being viewed by others
References
T.S. Su and LL, Converter Slag Splashing Protection Technology, 1st ed. (Beijing: Metallurgical Industry Press, 1999), pp. 7–14.
K.C. Mills, Y.C. Su, A.B. Fox, Z. LI, and R.P. Thackray, ISIJ Int. 45, 620 (2005).
B.T., Z.Y. Zhao, H.B. Li, X.F. Ren, B.L. H.C. Chen, J.W., Y.L. Zhang. Earth and Environmental Science.199, 2 (2018).
F. Du, Shanghai Metal. 22, 55 (2000).
J.C. Wang, H.S. Chen, G.S. Li, Q.L. Xie, and X.B. Deng, Iron Steel Vanadium Titanium. 19, 43 (1998).
S.L. Zeng and W.L. Zeng, Metal Mine. 5, 61 (2008).
D. Huang, Vanadium Extraction and Steelmaking, 1st ed. (Beijing: Metallurgical Industry Press, 2000), pp. 24–25.
Q. Zhang, unpublished Research (Chongqing: Chongqing University, 2019).
C.W. Bale, P. Chartrand, S.A. Degterov, G. Eriksson, K. Hack, R. Ben Mahfoud, J. Melançon, A.D. Pelton, and S. Petersen, Calphad Comput. Coupling Phase Diagr. Thermochem. 26, 191 (2002).
German Metal Institute, Slag Atlas, 2nd ed. (Beijing: Metallurgical Industry Press, 1995), p. 47.
Y.Q. Liu, Silicate Ceramic Phase Diagram, 1st ed. (Beijing: Chemical Industry Press, 2011), p. 82.
K. Norihito, T. Makoto, and Y. Yuji, Catal. Lett. 127, 65 (2009).
W.T. Du and I.H. Jung, Calphad. 67, 9 (2019).
J. Diao, B. Xie, C. Ji, X. Guo, Y. Wang, and X.J. Li, Cryst. Res. Technol. 44, 707 (2009).
J. Diao, Y. Qiao, X. Zhang, C.Q. Ji, and B. Xie, Cryst Eng Comm. 17, 7302 (2015).
M. Nohair, D. Aymes, and P. Perriat, Vib. Spectrosc. 9, 181 (1995).
K. Dodd and R.A. Mackay, International Textbook (London: Elsevier, 1981), p. 206.
German Metal Institute, Slag Atlas, 2nd ed. (Beijing: Metallurgical Industry Press, 1995), p. 94.
Acknowledgements
This work was supported by the National Natural Science Foundation of China (no. 51974047).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
On behalf of all authors, the corresponding author states that there is no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Diao, J., Qiu, YY., Lei, J. et al. Study on Saturated Solubility of MgO in Converter Vanadium Slag. JOM 73, 999–1003 (2021). https://doi.org/10.1007/s11837-020-04450-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-020-04450-8