Formation mechanism of ZrSiO4 powders

  • Papers
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

The formation mechanism of ZrSiO4 powders from ZrO2 and colloidal SiO2 sols has been studied. The change in the ZrSiO4 yield rate with seeding and non-seeding has also been investigated. The induction period of the ZrSiO4 yield-rate curve corresponded to the n=1 region, a simple nucleation region, on the Avrami plot. The n=1 region was a rather wide range at 1200–1300°C and the nucleation reaction was promoted in this temperature range. It was found that the ZrSiO4 yield rate became high, even if seeding was not used, when the heating rate was controlled at less than 1 °C min−1.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. S. Motoi, Bull. Chem. Soc. Jpn. 7 (1992) 162.

    Google Scholar 

  2. M. Kajiwara, ibid. 23 (1988) 960.

    Google Scholar 

  3. Y. Kakamu, J. Refract. Jpn. 39 (1987) 510.

    CAS  Google Scholar 

  4. K. Ichikawa and N. Tsukamoto, “Zircon, Science and Technology”, edited by S. Somiya (Uchidarokakuho, Japan, 1988) pp. 224–42.

    Google Scholar 

  5. S. Komarneni and R. Roy, “Zircon, Science and Technology”, edited by S. Somiya (Uchidarokakuho, Japan, 1988) pp. 289–98.

    Google Scholar 

  6. T. Suzuki and Y. Kanno, Yogyo-Kyokai-Shi 95 (1987) 1018.

    Article  CAS  Google Scholar 

  7. Y. Kanno and T. Suzuki, Zairyo 37 (1988) 378.

    CAS  Google Scholar 

  8. Idem, Hyomen Kagaku 9 (1988) 207.

    Article  CAS  Google Scholar 

  9. Idem, J. Mater. Sci. Lett. 8 (1989) 41.

    Article  CAS  Google Scholar 

  10. Y. Kanno, J. Mater. Sci. 24 (1989) 2415.

    Article  CAS  Google Scholar 

  11. T. Mori, H. Yamamura, H. Kobayashi and T. Mitamura, J. Am. Ceram. Soc. 75 (1992) 2420.

    Article  CAS  Google Scholar 

  12. G. Vilmin, S. Komarneni and R. Roy, J. Mater. Sci. 22 (1987) 3556.

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Tsukuba laboratory, TOSOH Company Ltd, Tsukuba, 305, Ibaraki, Japan

    T. Mori & H. Yamamura

  2. Department of Applied Chemistry, Faculty of Engineering, Saitama University, Urawa, Saitama, 338, Japan

    H. Kobayashi & T. Mitamura

Authors
  1. T. Mori
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. H. Yamamura
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. H. Kobayashi
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. T. Mitamura
    View author publications

    You can also search for this author in PubMed Google Scholar

Rights and permissions

Reprints and permissions

About this article

Cite this article

Mori, T., Yamamura, H., Kobayashi, H. et al. Formation mechanism of ZrSiO4 powders. JOURNAL OF MATERIALS SCIENCE 28, 4970–4973 (1993). https://doi.org/10.1007/BF00361163

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF00361163

Keywords

Search

Navigation