Abstract
Silica sol-gel films were prepared by dipping, starting from an acid catalyzed solution of methyltriethoxysilane (MTES) and tetraethoxysilane (TEOS). Silver metal nanoparticles were produced in the silica layer by introducing in the sol-gel precursor solution AgNO3 or AgClO4·H2O. The silver ions were thermally reduced in air at 800°C, giving an intense yellow coating film. The silver metal particles were observed by transmission electron microscopy and X-ray diffraction. The diameter of the silver particles was found to be about 10 nm. Absorption measurements in the UV-Vis were used to evaluate the volume fraction of silver colloids embedded in the silica layer.
Similar content being viewed by others
References
G. Mie, Ann. Phys. 25, 377, (1908).
J.C. Maxwell-Garnett, Phylos. Trans. R. Soc., London, 203, 385 (1904).
J.C. Maxwell-Garnett, Phylos. Trans. R. Soc., London, 205, 237 (1906).
U. Kreibig and P. Zacharias, Z. Phys. 231, 128 (1970).
K.H. Bennemann and S. Reindl, Ber. Bunsenges. Phys. Chem 88, 278 (1984).
D. Ricard, P. Roussignol, and C. Flytzanis, Opt. Lett. 10, 511 (1985).
F. Hache, D. Ricard, and C. Flytzanis, J. Opt. Soc. Am. B3 1647 (1987).
F. Hache, D. Ricard, C. Flytzanis, and U. Kreibig, Appl. Phys. A 47 347 (1988).
C. Flytzanis, in Materials for Photonic Devices, ed. by A. D'Andrea, A. Lopicciriello, G. Marletta, and S. Viticoli, World Scientific Publishing Co, Singapore (1990), p. 359.
R. Reisfeld, in Sol-Gel Optics II, Proc. SPIE, Vol. 1758, ed. by J.D. Mackenzie, SPIE, Bellingham, 1992, p. 546.
W.A. Weyle, Coulored Glasses, The Society of Glass Technology; Sheffield, 1951.
H. Kozuka and S. Sakka, Chem. Mater. 5, 222 (1993).
J. Matsuoka, R. Mizutami, H. Nasu, and K. Kamiya, J. Ceram. Soc. Jpn. 100, 599 (1992).
J.Y. Tseng, C.Y. Li, T. Takada, C. Lechner, and J.D. Mackenzie, in Sol-Gel Optics II, Proc. SPIE, Vol. 1758, ed. by J.D. Mackenzie, SPIE, Bellingham, 1992, p. 612.
L. Spanhel, M. Mennig, and H. Schmidt, in Proc. of the XVIth Intern. Congr. on Glass, Vol. 7, 1992, p. 9.
J.M.F Navarro and M.A. Villegas, Glastech. Ber. 65, (1992) Nr. 2, p. 32.
P. Innocenzi, H. Kozuka, and S. Sakka, J. Sol-Gel Sci. and Tech., 1, 305 (1994).
H. Kozuka, G. Zhao, and S. Sakka, J. Sol-Gel Sci. and Tech. 2, 741 (1994).
D. Brusilovsky, M. Eyal, and R. Reisfeld, Chem. Phys. Letters 153, 203 (1988).
R. Reisfeld, M. Eyal, and D. Brusilovsky, Chem. Phys. Letters 153, 210, (1988).
R. Reisfeld, H. Hinti, and M. Eyal, in Glasses for Optoelectronics II, Proc. SPIE, Vol. 1513, ed. by G. Righini, SPIE, Bellingham 1991, p. 360.
M. Mennig, J. Spanhel, H. Schmidt, and S. Betzholz, J. Non-Cryst. Solids 146&148, 326 (1992).
A. Hinsch and A. Zastrow, J. Non-Cryst. Solids 146–148, 579 (1992).
P. Innocenzi, M.O. Abdirashid, and M. Guglielmi, J. Sol-Gel Sci. and Techn., in print.
U. Kreibig and C.V. Fragstein, Z. Phys. 224, 307 (1969).
L.G. Shulz, Advanc. Phys. 6, 102 (1957).
R.M. Almeida, and G.C. Pantano, J. Appl. Phys. 68, 4225 (1990).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Innocenzi, P., Kozuka, H. Methyltriethoxysilane-derived sol-gel coatings doped with silver metal particles. J Sol-Gel Sci Technol 3, 229–233 (1994). https://doi.org/10.1007/BF00486561
Issue Date:
DOI: https://doi.org/10.1007/BF00486561