Abstract
The nature and kinetics of the δ-ferrite transformation in a series of duplex submerged arc 316 L weld metals has been studied under creep conditions at 600° C and an applied stress of 200 MN m−2. The δ-ferrite was found to transform first to M23C6 carbides, these occurring at either the δ/γ interface or within the δ-ferrite laths depending upon the presence of suitable nucleation sites. The remaining δ-ferrite then transforms to the intermetallic σ-phase. The kinetics of the intermetallic phase formation varied between the different welds, and STEM/EDAX analysis indicated that the kinetics were dependent on the localized segregations of chromium, nickel and molybdenum in the δ-ferrite laths. A transformation model has been developed which indicates that chromium diffusion within the γ matrix is the controlling mechanism.
Similar content being viewed by others
References
R. G. Thomas and S. R. Keown, “Mechanical Behaviour and Nuclear Applications of Stainless Steel at Elevated Temperatures” Varese Conference, May 1981 (Metals Society, London, 1982) Book 280.
R. G. Thomas, R. D. Nicholson and R. A. Farrar, submitted to Met. Technol.
S. R. Keown and R. G. Thomas, Met. Sci. 15 (1981) 386.
B. Weiss and R. Stickler, Met. Trans. 3 (1972) 851.
V. G. Rivlin and G. V. Raynor, Int. Met. Rev. 248 (1980) 21.
J. C. Lippold and W. F. Savage, Weld. J. Res. Suppl. 58 (1979) 362s.
T. B. Massalski, A. J. Parkins and J. Jaklovsky, Met. Trans. 6A (1975) 1405.
C. E. Lyman, Weld. J. Res. Suppl. 58 (1979) 189s.
A. F. Smith, Met. Sci. 10 (1975) 375.
F. R. Beckett, J. Iron Steel Inst. 207 (1969) 632.
M. Lewis, Acta Metall. 14 (1966) 1421.
J. K. L. Lai and J. R. Haigh, Weld. J. Res. Suppl. 58 (1979) 1s.
J. Wegrzyn and A. Klimpel, ibid.
P. G. Shewmon, “Diffusion in Solid” (McGraw Hill, New York, 1963).
R. G. Thomas and D. Yapp, Weld. J. Res. Suppl. 57 (1978) 361s.
G. Cliff and G. W. Lorimer, J. Microsc. 103 (1975) 203.
J. I. Goldstein, J. L. Costley, G. W. Lorimer and S. J. B. Reed, “Scanning Electron Microscopy”, Vol. 1, edited by O. Johan (ITRI, Chicago, Illinois, 1977) p. 315.
C. Nockolds, M. J. Nasir, G. Cliff and G. W. Lorimer, “Institute of Physics Conference Series” No. 52 (1980) Chap. 9, p. 417.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Farrar, R.A., Thomas, R.G. The microstructure and phase transformations in duplex 316L submerged arc weld metals. J Mater Sci 18, 3461–3474 (1983). https://doi.org/10.1007/BF00544175
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00544175