Abstract
Conversion versus time curves were measured for poly(N-isopropylacrylamide) microgel latexes prepared by polymerization in water with sodium dodecyl sulfate, SDS. Polymerization rates increased with temperature with methylenebisacrylamide crosslinking monomer consumed faster thanN-isopropylacrylamide. The particle diameter decreased with increasing concentrations of SDS in the polymerization recipe and there was evidence that the rate of polymerization increased somewhat with SDS concentration. Particle formation occurred by homogeneous nucleation as micelles were absent.
Comparison of particle size distributions from dynamic light scattering to those from a centrifugal sizer led to the conclusion that larger particles within a specific latex were less swollen with acetonitrile than were the smaller ones. This was interpreted as evidence for the polymer in larger particles having a higher crosslink density. Particle swelling was estimated from swelling ratios defined as the particle volume at 25 °C divided by the volume at 50 °C. In the absence of crosslinking poly(N-isopropylacrylamide) linear chains would disolve at 25 °C. The swelling results indicated that the average crosslink density in the particles decreased with conversion. This was explained by the observation that the methylenebisacrylamide was consumed more quickly and is typical of crosslinking in emulsion polymerization where polymer particles have high polymer concentrations at their birth.
Similar content being viewed by others
References
Schild HG (1992) Prog Polym Sci 17:163
Pelton RH, Chibante P (1986) Colloids and Surfaces 20:247
Pelton RH, Pelton HM, Morfesis A, Rowell RL (1989) Langmuir 5:816
McPhee W, Tam KC, Pelton RH (1993) J Colloid Interface Sci 156:24
Kawaguchi H, Fujimoto K, Mizuhara Y (1992) Colloid and Polymer Sci 270:53
Thomas DG (1965) J Colloid Sci 20:267
Thomson RAM, Ong CK, Rosser CM, Holt JM (1983) Makromol Chem 184:1885
Goodwin JW, Hearn J, Ho CC, Ottewill RH (1974) Br Polym J 5:347
Sewell JH (1973) J Appl Polym Sci 17:1714
Chiklis CK, Grasshoff JM (1970) J Polym Sci, Part A2 8:1617
Snyder WD, Klotz IM (1975) J Amer Chem Soc 97(17): 4999
Feeney PJ, Napper DH, Gilbert RG (1987) Macromolecules 20:2922
Wu XY, Pelton RH, Tam KC, Woods DR, Hamielec AE (1993) J Polymer Sci Part A 31:957
Barrett KEJ (1975) Dispersion Polymerization in Organic Media. John Wiley & Sons, London
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wu, X., Pelton, R.H., Hamielec, A.E. et al. The kinetics of poly(N-isopropylacrylamide) microgel latex formation. Colloid Polym Sci 272, 467–477 (1994). https://doi.org/10.1007/BF00659460
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00659460