Molecular-weight dependence of the glass transition temperatures of rigid SIS triblock copolymers studied by DSC

Abstract

Differential scanning calorimetry (DSC) measurements have been carried out on a series of ABA poly(styrene-b-isoprene) triblock copolymers with 30% polyisoprene content and various molecular weights. The DSC data show an inward shift for the glass transition temperatures (T _g) of the blocks compared to the corresponding homopolymers. As a function of the molecular weight, one to three transitions were found. The additional thirdT _g gives some further evidence of the existence of an interphase between the microdomains.

Zusammenfassung

DSC wurden an einer Reihe von ABA Poly(styrol-b-isopren) Dreiblock-Kopolymeren mit 30% Polyisoprengehalt und verschiedenen Molekulargewichten durchgeführt. Die DSC-Daten zeigen eine innere Verschiebung der Glas-Übergangstemperaturen (T _g) der Blöcke im Vergleich zu den entsprechenden Homopolymeren. Als Funktion des Molekulargewichts wurden ein bis drei Übergänge gefunden. Die zusätzliche dritteT _gerbringt weitere Beweise bezüglich der Existenz einer Interphase zwischen den Mikrodomänen.

Резюме

Проведены ДСК-измере ния ряда АБА поли(стирол-Ь-изопрен) трехблочных сополимеров с различ ным молекулярным вес ом и содержащих 30% полиизоп рена. Данные ДСК показали внутрен ний сдвиг температур ы стеклообразования (T _g) блочных сополимеров по сравнению с соотве тствующими гомополи мерами. В зависимости от молек улярного веса полимеров было н айдено от одного до тр ех переходов. Наличие до полнительного третьегоТ _g перехода служит дальнейшим доказательством сущ ествования какого-ли бо межфазного состояни я между микродоменам и.