Abstract
The temperature limit for GP zone formation, Tlimit was determined for an Al-5 pct Zn-2 pct Mg alloy by examining the formation process of the intermediate phase. Studies of changes in hardness and electrical resistivity, together with electron metallography permitted a conclusion that the Tlimit for this alloy is 125 °C. The nucleation mechanism of the intermediate phase is also discussed. Two types of precipitation mode were found the partly coherent phase;i.e. heterogeneous nucleation on GP zones and homogeneous nucleation respectively. It is concluded that the dominant nucleation mode is determined by the quenching conditions.
Similar content being viewed by others
References
G. W. Lorimer:Precipitation Process in Solids, ed. K. C. Rüssel and H. I. Aaronson, p. 109, AIME, 1978.
G. W. Lorimer and R. B. Nicholson:Acta Metall., 1966, vol. 14, p. 1009.
K. Asano, M. Abe and A. Fujiwara:Mater. Sci. Eng., 1976, vol. 22, p. 61.
H. A. Holl:Met. Sci. J., 1967, vol. 1, p. 111.
N. Ryum:Z. Metallkd., 1975, vol. 66, p. 338.
I. L. Polmear:J. Inst. Met., 1958-59, vol. 87, p. 24.
K. H. Dūnkeloh, G. Kralik and V. Gerold:Z. Metallkd., 1974, vol. 65, p. 291.
T. Ungar, J. Lendvai and I. Kovács:Aluminium, 1979, vol. 10, p. 663.
G. J. C. Carpenter and R. D. Garwood:J. Inst. Met., 1966, vol. 94, p. 301.
M. Murakami, O. Kawano and Y. Murakami:J. Inst. Met., 1971, vol. 99, p. 160.
T. Sato, Y. Kojima and T. Takahashi:Trans. JIM., 1979, vol. 20, p. 475.
G. Groma, E. Kovacs-Csetenyi, I. Kovács, J. Lendvai and T. Ungar:Z. Metallkd., 1976, vol. 67, p. 404.
T. Takahashi and Y. Kojima:J. Jpn. Inst. Light Met., 1970, vol. 20, p. 504.
Author information
Authors and Affiliations
Additional information
formerly with Graduate School of Tokyo Institute of Technology, is now with Kobe Steel Ltd., Nagoya
formerly with Tokyo Institute of Technology, is now Associate Professor, The Technological University of Nagaoka, Nagaoka.
Rights and permissions
About this article
Cite this article
Inoue, H., Sato, T., Kojima, Y. et al. The Temperature Limit for GP Zone Formation in an Al-Zn-Mg Alloy. Metall Trans A 12, 1429–1434 (1981). https://doi.org/10.1007/BF02643687
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF02643687