Abstract
The changes in matrix structure that occur during tempering of an Fe-0.2C martensite at 400° to 700°C have been investigated. Light and electron metallographic observations show that when tempered, the fine martensitic lath structure coarsens while retaining the elongated packet-lath morphology. The as-quenched hardness 504 Khn and total grain boundary area per unit volume 50,800 cm−1 decrease abruptly at the higher tempering temperatures and in seconds reach relatively stable values that decrease slowly with time. The decrease in low angle boundaries accounts for most of the initial grain boundary area change, while the large angle boundary component of total boundary area decreases gradually with tempering time. Recovery processes are responsible for the initial changes in matrix structure, and carbide boundary pinning suppresses recrystallization until grain growth dominates in the later stages of tempering.
Similar content being viewed by others
References
C. S. Roberts, B. L. Averbach, and M. Cohen:Trans. ASM, 1953, vol. 45, pp. 576–604.
B. S. Lement, B. L. Averbach, and M. Cohen:Trans. ASM, 1954, vol. 46, pp. 851–81.
B. S. Lement, B. L. Averbach, and M. Cohen:Trans. ASM, 1955, vol. 47, pp. 291–320.
E. Tekin and P. M. Kelly:Precipitation from Iron-Base Alloys, pp. 173–229, Gordon and Breach, New York, 1965.
G. R. Speich:Trans. TMS-AIME, 1969, vol. 245, pp. 2553–64.
E. D. Hyam and J. Nutting:J. Iron Steel Inst., 1956, vol. 184, pp. 148–65.
A. M. Turkalo:Trans. ASM, 1961, vol. 54, pp. 344–54.
K. J. Irvine and F. B. Pickering:J. Iron Steel Inst., 1960, vol. 194, pp. 137–53.
A. Galibois and A. Dubé:Can. Met. Quart., 1967, vol. 6, pp. 121–36.
A. Galibois and A. Dubé:Can. Met. Quart., 1964, vol. 3, pp. 321–43.
G. P. Airey, T. A. Hughes, and R. F. Mehl:Trans. TMS-AIME, 1968, vol. 242, pp. 1853–63.
T. Mukherjee, W. E. Stumpf, C. M. Sellars, and W. J. McG. Tegart:J. Iron Steel Inst., 1969, vol. 207, pp. 621–31.
F. E. Werner, B. L. Averbach, and M. Cohen:Trans. ASM, 1957, vol. 49, pp. 823–41.
A. R. Marder and G. Krauss:Trans. ASM, 1967, vol. 60, pp. 651–60.
Charles Apple: Ph.D. Dissertation, Lehigh University, 1971.
R. P. Smith:Trans. TMS-AIME, 1962, vol. 224, pp. 105–11.
A. R. Marder: Ph.D. Dissertation, Lehigh University, 1968.
R. N. Caron: Ph.D. Dissertation, Lehigh University, 1970.
G. W. Greenwood:The Mechanism of Phase Transformations in Crystalline Solids, pp. 103–10, Inst. of Metals Mono. No. 33, Institute of Metals, London, 1969.
K. M. Vedula and R. W. Heckel:Met. Trans., 1970, vol. 1, pp. 9–18.
W. E. Stumpf and C. M. Sellars:The Mechanism of Phase Transformations in Crystalline Solids, pp. 120–22, Inst. of Metals Mono. No. 33, Institute of Me- tals, London, 1969.
T. Mukherjee and C. M. Sellars:The Mechanism of Phase Transformations in Crystalline Solids, pp. 122–24, Inst. of Metals Mono. No. 33, Institute of Me- tals, London, 1969.
J. L. Brimhall, M. J. Klein, and R. A. Huggins:Acta Met., 1966, vol. 14, pp. 459–66.
F. J. Humphreys and J. W. Martin:Acta Met., 1966, vol. 14, pp. 775–81.
P. R. Mould:Acta Met., 1967, vol. 15, pp. 1086–87.
J. E. Hilliard:Recrystallization, Grain Growth, and Textures, pp. 267–86, ASM, Metals Park, Ohio, 1966.
D. A. Witmer and G. Krauss:Trans. ASM, 1969, vol. 62, pp. 447–56.
J. C. M. Li:Recrystallization, Grain Growth, and Textures, pp. 45–98, ASM, Metals Park, Ohio, 1966.
G. Langford and M. Cohen:Trans. ASM, 1969, vol. 62, pp. 623–38.
H. Hu:Recovery and Recrystallization of Metals, L. Himmel, ed., pp. 311–78, Gordon and Breach, New York, 1963.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Caron, R.N., Krauss, G. The tempering of Fe-C lath martensite. Metall Trans 3, 2381–2389 (1972). https://doi.org/10.1007/BF02647041
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02647041