Abstract
An investigation into the mechanisms of tempered martensite embrittlement (TME), also know as “500°F” or “350°C” or one-step temper embrittlement, has been made in commercial, ultra-high strength 4340 and Si-modified 4340 (300-M) alloy steels, with particular focus given to the role of interlath films of retained austenite. Studies were performed on the variation of i) strength and toughness, and ii) the morphology, volume fraction and thermal and mechanical stability of retained austenite, as a function of tempering temperature, following oil-quenching, isothermal holding, and continuous air cooling from the austenitizing temperature. TME was observed as a decrease in bothK Ic and Charpy V-notch impact energy after tempering around 300°C in 4340 and 425°C in 300-M, where the mechanisms of fracture were either interlath cleavage or largely transgranular cleavage. The embrittlement was found to be concurrent with the interlath precipitation of cementite during temperingand the consequent mechanical instability of interlath films of retained austenite during subsequent loading. The role of silicon in 300-M was seen to retard these processes and hence retard TME to higher tempering temperatures than for 4340. The magnitude of the embrittlement was found to be significantly greater in microstructures containing increasing volume fractions of retained austenite. Specifically, in 300-M the decrease inK Ic, due to TME, was a 5 MPa√m in oil quenched structures with less than 4 pct austenite, compared to a massive decrease of 70 MPa√m in slowly (air) cooled structures containing 25 pct austenite. A complete mechanism of tempered martensite embrittlement is proposed involving i) precipitation of interlath cementite due to partial thermal decomposition of interlath films of retained austenite, and ii) subsequent deformation-induced transformation on loading of remaining interlath austenite, destabilized by carbon depletion from carbide precipitation. The deterioration in toughness, associated with TME, is therefore ascribed to the embrittling effect of i) interlath cementite precipitates and ii) an interlath layer of mechanically-transformed austenite,i.e., untempered martensite. The presence of residual impurity elements in prior austenite grain boundaries, having segregated there during austenitization, may accentuate this process by providing an alternative weak path for fracture. The relative importance of these effects is discussed.
Similar content being viewed by others
References
J. R. Low , Jr.: inFract. Eng. Mater., ASM, 1964, p. 127.
C. I. McMahon, Jr.: ASTM STP 407, p. 127, American Society for Testing and Materials, 1968.
E. B. Kula and A. A. Anctil:J. Mater., 1964, vol. 4, p. 817.
B. J. Schulz and C. J. McMahon, Jr.: ASTM STP 499, p. 104, American Society for Testing and Materials, 1972.
M. A. Grossmann:Trans. AIME, 1946, vol. 167, p. 39.
H. Schrader, H. J. Wiester, and H. Siepmann:Arch. Eisenhuettenw., 1950, vol. 21, p. 21.
R. L. Rickett and J. M. Hodge:Proc. ASTM, 1951, vol. 51, p. 931.
L. J. Klingler, W. J. Barnett, R. P. Frohmberg, and A. R. Troiano:Trans. ASM, 1954, vol. 46, p. 1557.
J. J. Irani, M. J. May, and D. Elliott: ASTM STP 407, p. 168, American Society for Testing and Materials, 1968.
E. J. Ripling:Trans. ASM, 1950, vol. 42, p. 439.
G. V. Luerssen and O. V. Greene:, 1935, vol. 23, p. 861.
L. S. Castleman, B. L. Averbach, and M. Cohen:, 1952, vol. 44, p. 240.
R. M. Horn: Ph.D. Thesis, University of California at Berkeley, 1976 (Lawrence Berkeley Laboratory Report No. LBL-5787, December 1976).
V. H. Lindborg and B. L. Averbach:Acta Met., 1966, vol. 14, p. 1583.
E. F. Walker and M. J. May: ISI Publ. 120, p. 135, 1970.
W. Backfisch and K. H. Schwalbe:Proc. Fourth International Conf. on Fracture, Waterloo, vol. 2, p. 73, 1977.
J. E. King, R. F. Smith, and J. F. Knott:Ibid, vol. 2, p. 279.
G. Thomas:Met. Trans. A, 1978, vol. 9A, p. 439.
A. Nakashima and J. F. Libsch:Trans. ASM, 1961, vol. 53, p. 753.
B. S. Lement, B. L. Averbach, and M. Cohen:, 1954, vol. 46, p. 851.
A. J. Baker, F. J. Lauta, and R. P. Wei: ASTM STP 370; p. 3, American Society for Testing and Materials, 1963.
R. D. Goolsby: Ph.D. Thesis, University of California in Berkeley, 1971 (Lawrence Berkeley Laboratory Report No. LBL-405, November 1971).
A. G. Allten and P. Payson:Trans. ASM, 1953, vol. 45, p. 498.
C. H. Shih, B. L. Averbach, and M. Cohen:, 1956, vol. 48, p. 86.
C. J. Altstetter, M. Cohen, and B. L. Averbach:, 1962, vol. 55, p. 287.
M. S. Bhat: Ph.D. Thesis, University of California at Berkeley, 1977 (Lawrence Berkeley Laboratory Report No. LBL-6046, February 1977)
W. S. Owen:J. Iron Steel Inst., 1957, vol. 177, p. 445.
B. R. Banerjee: ASTM STP 370, p. 94, American Society for Testing and Materials, 1963.
B. R. Banerjee:J. Iron Steel Inst., 1965, vol. 203, p. 166.
J. M. Capus and G. Mayer:Metallurgia, 1960, vol. 62, p. 133.
J. R. Rellick and C. J. McMahon, Jr.:Met. Trans., 1974, vol. 5, p. 2439.
S. K. Banerji, C. J. M Mahon, Jr., and H. C. Feng:Met. Trans. A, 1978, vol. 9A, p. 237.
R. M. Horn and R. O. Ritchie:Proc. 106th Annual AIME Meeting, Atlanta, March 1977.
F. J. Witt:Practical Application of Fracture Mechanics to Pressure-Vessel Technology, p. 163, The Institute of Mechanical Engineers, London, 1971.
J. D. Landes and J. A. Begley: Westinghouse Scientific Paper 76-1E7-JINTF-P3, May 1976, Westinghouse Research Laboratories, Pittsburgh, Pa. 15235.
R. O. Ritchie, G. G. Garrett, and J. F. Knott:Int. J. of Fract. Mech, 1971, vol. 7, p. 462.
B. D. Cullity: inElements of X-Ray Diffraction, p. 391, Addison-Wesley Publ. Co. Inc., Reading, Mass., 1959.
D. Bhandarkar, V. F. Zackay, and E. R. Parker:Met. Trans., 1972, vol. 3, p. 2619.
R. O. Ritchie, M. H. Castro-Cedeno, V. F. Zackay, and E. R. Parker:Met. Trans. A, 1978, vol. 9A, p. 35.
C. W. Marschall, R. F. Hehemann, and A. R. Troiano:Trans. ASM, 1962, vol. 55, p. 135.
J. McMahon and G. Thomas:Proc. Third Int’l Conf. on the Strength of Metals and Alloys, vol. 1, p. 180, Cambridge, Institute of Metals, London, August 1973.
G. Y. Lai, W. E. Wood, R. A. Clark, V. F. Zackay, and E. R. Parker:Met. Trans., 1974, vol. 5, p. 1663.
B. V. N. Rao, J. Y. Koo, and G. Thomas:Proc. Electron Microscopy Society of America, p. 30, Claitors Publication Division, Baton Rouge, 1975.
K. J. Kim and L. H. Schwartz:Mater. Sci. Eng., in press.
W. W. Gerberich, P. L. Hemmings, V. F. Zackay, and E. R. Parker: inFracture 1969, p. 288, Proc. Second Int’l. Conf. on Fracture, Brighton, 1969, Chapman and Hall, Ltd., London.
R. O. Ritchie:J. Eng. Mater. Technol., Trans. ASME Series H, 1977, vol. 99, p. 195.
C. L. Briant and S. K. Banerji: Unpublished research, General Electric Co., Schenectady, New York, 1977.
R. O. Ritchie: Ph.D. Thesis, University of Cambridge, 1973.
G. Y. Lai, W. E. Wood, E. R. Parker, and V. F. Zackay: Lawrence Berkeley Laboratory Report No. LBL-2236, University of California, April, 1975.
Der-Hung Huang and G. Thomas:Met. Trans. A, 1977, vol. 8A, p. 1661.
Author information
Authors and Affiliations
Additional information
Formerly with the Lawrence Berkeley Laboratory, University of California.
Rights and permissions
About this article
Cite this article
Horn, R.M., Ritchie, R.O. Mechanisms of tempered martensite embrittlement in low alloy steels. Metall Trans A 9, 1039–1053 (1978). https://doi.org/10.1007/BF02652208
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02652208