Abstract
In order to better understand the formation of Precipitate Free Zones (PFZ), microanalysis was conducted on heat treated Al-2.2 at. pct Zn-4.7 at. pct Mg and Cu-30 at. pct Ni-0.9 at. pct Nb alloys. In both the alloys, no appreciable solute depletion at the grain boundaries was observed in the as-quenched condition. After aging, marked solute depletion was observed in the PFZ of both the alloys. In the Al-Zn-Mg alloy, the PFZ were supersaturated with respect toη andT phases up to 4 h of aging at 473 K. In the Cu-Ni-Nb alloy, the PFZ were supersaturated only with respect to theβ phase but not the metastable γ″ phase. Based on the results, the factors affecting the formation and growth of PFZ are discussed.
Similar content being viewed by others
References
H. S. Rosenbaum and D. Turnbull:Acta Met., 1958, vol. 6, p. 653.
H. S. Rosenbaum, D. Turnbull, and E. I. Alessandrini:Acta Met., 1959, vol. 7, p. 678.
J. B. Clark:Acta Met., 1964, vol. 12, p. 1197.
J. C. Taylor:J. Inst. Met., 1963–64, vol. 93, p. 301.
G. Thomas and J. Nutting:J. Inst. Met., 1959–60, vol. 88, p. 81.
P. N. T. Unwin, G. W. Lorimer, and R. B. Nicholson:Acta Met., 1969, vol. 17, p. 1363.
P. N. T. Unwin and R. B. Nicholson:Acta Met., 1969, vol. 17, p. 1379.
J. D. Embury and R. B. Nicholson:Acta Met., 1965, vol. 13, p. 403.
J. D. Embury and R. B. Nicholson:J. Aust. Inst. Met., 1963, vol. 8, p. 76.
G. W. Lorimer and R. B. Nicholson:Acta Met., 1966, vol. 14, p. 1009.
M. Raghavan:Met. Trans. A, 1977, vol. 8A,p. 1071.
G. Thomas:J. Inst. Met., 1960–61, vol. 89, p. 287.
C. S. Pande, M. Suenega, B. Vyas, H. S. Isaacs, and D. F. Harling:Scripta Met., 1977, vol. 11, p. 681.
D. E. Ward and G. M. Lorimer:Proc. of 3rd International Conf. on Strength of Metals and Alloys, Institute of Metals, 1973, vol. 1, p. 488.
P. R. Sperry:Met. Trans., 1970, vol. 1, p. 2650.
P. Doig, J. W. Edington, and G. Hibberf.Phil. Mag., 1973, vol. 38, p. 971.
P. Doig and J. W. Edington:Met. Trans. A, 1975, vol. 6A, p. 943.
P. Doig and J. W. Edington:Corrosion, 1975, vol. 31, p. 347.
C. R. Shastry and G. Judd:Met. Trans., 1972, vol. 3, p. 779.
S. L. Cundy, A. J. F. Metherell, and M. J. Whelan:Proc. Roy. Soc., 1968, vol. 307, A, p. 267.
D. B. Williams and J. W. Edington:J. Microscopy, 1976, vol. 108, p. 113.
E. A. Starke, Jr.:J. Metals, January 1970, vol. 22, p. 54.
C. Chen and G. Judd:Met. Trans. A, 1978, vol. 9A, p. 553.
J. I. Goldstein, J. L. Costley, G. W. Lorimer, and S. J. B. Reed:Scanning Electron Microscopy, O. Johari, ed., vol. 1, p. 315, HT Research Institute, Chicago, IL, 1977.
J. I. Goldstein:Introduction to Analytical Electron Microscopy, J. J. Hren, J. I. Goldstein, and D. C. Joy, eds., p. 83, Plenum Press, New York, 1979.
G. Cliff and G. W. Lorimer:J. Microscopy, 1975, vol. 103, p. 203.
J. Russ:Quantitative Electron Probe Microanalysis of Particles, Proc. 8th National Conference on Electron Probe Analysis, p. 30, National Bureau of Standards, Washington, 1973.
V. A. Phillips:Acta Met., 1966, vol. 14, p. 1533.
V. A. Phillips:Trans. TMS-AIME, 1966, vol. 236, p. 1302.
V. A. Phillips:Phil. Mag., 1967, vol. 16, p. 139.
M. Raghavan: Exxon Research and Engineering Company, Linden, NJ, unpublished work, 1979.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Raghavan, M. Microanalysis of precipitate free zones (PFZ) in Al-Zn-Mg and Cu-Ni-Nb alloys. Metall Trans A 11, 993–999 (1980). https://doi.org/10.1007/BF02654713
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02654713