Abstract
Modification of the eutectic Si in Al-Si foundry alloys by adding strontium or sodium is, unfortunately, accompanied by an increase of porosity in the casting. In an attempt to understand the nature of this problem, this study used a sessile-drop method to investigate the effect of Sr and Na on surface tension and volumetric shrinkage, two probable causes of porosity occur-rence. The addition of 0.01 wt pct Sr and 0.005 wt pct Na to A356 alloy decreases the surface tension of the liquid by about 19 and 10 pct, respectively, and may increase the volume shrink-age by about 12 pct. These changes to surface tension and volumetric shrinkage promote the early formation of the pores during solidification and give the availability of a longer period of growth prior to complete solidification, resulting in a larger pore size. The effect of surface tension on the pores is more significant than volumetric shrinkage. Although the predicted pore diameter increases with lower surface tension or higher volumetric shrinkage, these two effects alone do not seem able to completely account for the observed increase in porosity that is associated with modification.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
S. Shivkumar, L. Wang, and D. Apelian:J. Met., 1991, Jan., pp. 26–32.
Q.T. Fang and D.A. Granger:AFS Trans., 1989, vol. 97, pp. 989–1000.
H. Iwahori, K. Yonekura, Y. Yamamoto, and M. Nakamura:AFS Trans., 1990, vol. 98, pp. 167–73.
D. Argo and J.E. Gruzleski:AFS Trans., 1988, vol. 96, pp. 65–74.
J.E. Gruzleski and B.M. Closset:The Treatment of Liquid Aluminum-Silicon Alloys, American Foundrymen's Society, Des Plaines, IL, 1990, pp. 57–157.
J.R. Denton and J.A. Spittle:Mater. Sci. Technol., 1985, vol. 1, pp. 305–11.
F.C. Dimayuga, N. Handiak, and J.E. Gruzleski:AFS Trans., 1988, vol. 96, pp. 83–88.
H. Shahani :Scand. J. Metall., 1985, no. 14, pp. 306-12.
G. Lang:Aluminum, 1973, vol. 49 (3), pp. 231–38.
G. Lang:Aluminum, 1974, vol. 50 (11), pp. 731–34.
D.W.G. White:Metall. Rev., 1968, vol. 13, pp. 73–96.
D.W.G. White:ASM Trans., 1962, vol. 55, pp. 757–89.
J.F. Padday:Surface and Colloid Science, E. Matijevic, ed., Wiley Interscience, New York, NY, 1969, pp. 39–157.
T. Iida and R.I.L. Guthrie:The Physical Properties of Liquid Metals, Oxford University Press, New York, NY, 1988, pp. 109–20.
D.W.G. White:A Supplement to the Tables of Bashforth and Adams, Queen's Printer, Ottawa, Canada, 1967, pp. 1–11.
Y. Rotenberg: Ph.D. Thesis, University of Toronto, Toronto, 1983.
L. Liggieri and A. Passerone:High Temp. Technol., 1989, May, pp. 82-86.
G. Gustafsson, T. Thorvaldsson, and G.L. Dunlop:The Metallurgy of Light Alloys, Institute of Metallurgists, London, 1983, March, pp. 288–94.
Aluminum: Properties and Physical Metallurgy, J.E. Hatch, ed., ASM, Metals Park, OH, 1984, pp. 200–10.
J. Golcoechea, C. Garcia-Cordovilla, E. Louis, and A. Pamies:J. Mater. Sci., 1992, no. 27, pp. 5247-52.
V.L. Davies and J.M. West:J. Inst. Met., 1963-1964, vol. 92, pp. 208–10.
A. Yavari:Z. Metallkd., 1988, vol. 79(9), pp. 591–94.
J. Campbell:The Solidification of Metals, ISI Publication No. 110, The Iron and Steel Institute, London, 1967, pp. 18–26.
H. Shahani and H. Fredriksson:Scand. J. Metall., 1985, no. 14, pp. 316-20.
T.S. Piwonka and M.C. Flemings:Trans. TMS-AIME, 1966, vol. 236, pp. 1157–65.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Emadi, D., Gruzleski, J.E. & Toguri, J.M. The effect of na and Sr modification on surface tension and volumetric shrinkage of A356 alloy and their influence on porosity formation. Metall Trans B 24, 1055–1063 (1993). https://doi.org/10.1007/BF02660997
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02660997