Abstract
Sapphire-reinforced NiAl matrix composites with chromium or tungsten as alloying additions were synthesized using casting and zone directional solidification (DS) techniques and characterized by a fiber pushout test as well as by microhardness measurements. The sapphire-NiAl(Cr) specimens exhibited an interlayer of Cr rich eutectic at the fiber-matrix interface and a higher interfacial shear strength compared to unalloyed sapphire-NiAl specimens processed under identical conditions. In contrast, the sapphire-NiAl(W) specimens did not show interfacial excess of tungsten rich phases, although the interfacial shear strength was high and comparable to that of sapphire-NiAl(Cr). The postdebond sliding stress was higher in sapphire-NiAl(Cr) than in sapphire-NiAl(W) due to interface enrichment with chromium particles. The matrix microhardness progressively decreased with increasing distance from the interface in both DS NiAl and NiAl(Cr) specimens. The study highlights the potential of casting and DS techniques to improve the toughness and strength of NiAl by designing dual-phase microstructures in NiAl alloys reinforced with sapphire fibers.
Similar content being viewed by others
References
Darolia:J. Met., 1991, vol. 43 (3), p. 44.
R.D. Noebe, A. Misra, and R. Gibala:J. Iron Steel Inst. Jpn., 1991, 31, 1172–1186.
R.D. Noebe, R.R. Bowman, and J.I. Eldridge: Intermetallic Matrix Composites, Materials Research Society Symposia Proceedings, D.L. Anton, R. McMeeking, D. Miracle, and P. Martin, eds., p. Materials Research Society, Pittsburgh, PA, vol. 194, p. 323–331.
J.W. Pickens, R.D. Noebe, G.K. Watson, P.K. Brindley, and SX. Draper:NASA TM 102060, 1989.
S.N. Tewari, R. Asthana, and R.D. Noebe:Metall. Trans. A, 1993, vol. 24A, pp. 2119–25.
R. Asthana, S.N. Tewari, and R.R. Bowman:Metall. Mater. Trans. A, 1995, vol. 26A, p. 209–223.
D. Xu, D. Wang, and T.L. Lin:Scripta Metall., 1993, vol. 26, p. 599.
S.L. Draper, D.J. Gaydosh, and M.V. Nathal:J. Mater. Res., 1990, vol. 5, p. 1976.
S. Nourbakhsh, O. Sahin, W.H. Rhee, and H. Margolin:Metall. Trans. A, 1991, vol. 22A, pp. 3059–64.
R.M. Crispin and M. Nicholas:J. Mater. Sci., 1976, vol. 11, p. 17.
M. Nicholas:J. Mater. Sci., 1968, vol. 3, p. 571.
S.N. Tewari: NASA TN D 8355, 1977.
R. Johnson, S.M. Joslin, B.F. Oliver, R.D. Noebe, and J.D. Whittenberger:Intermetallic Matrix Composites II, Materials Research Society Symposia Proceedings, D.B. Miracle, J. Graves, and D. Anton, eds, Materials Research Society, Pittsburgh, PA, 1992, vol. 273, p. 87–92.
J.I. Eldridge: NASA TM 105341, 1991.
A.K. Misra: NASA CR 191167, 1993.
D.A. Koss, M.N. Kallas, and J.R. Hellman:Intermetallic Matrix Composites II, Materials Research Society Symposia Proceedings, D.B. Miracle, J. Graves, and D. Anton, eds, Material Research Society, Pittsburgh, PA, 1992, vol. 273, p. 303.
M.N. Kallas, D.A. Koss, H.T. Hahn, and J.R. Hellman:J. Mater. Sci., 1992, vol. 27 (4), p. 3821.
Metals Handbook, 8th ed., ASM, Metals Park, OH, 1961, vol. 1, p. 48.
S. Ochiai and K. Osamura:Metall. Trans. A, 1988, vol. 19A, pp. 1499 1506.
S.L. Draper and I.E. Locci:J. Mater. Res., 1994, vol. 9 (6), p. 1397–1411.
“Sapphire and Advanced Single Crystal Technologies” (Data Sheet), Saphikon Inc., Milford, NH.
R.R. Bowman, I.E. Locci, S.L. Draper, and A.K. Misra:Materials Research Society Symposia Proceedings, Materials Research Society, Pittsburgh, PA, 1994, vol. 350, p. 105–110.
R.R. Bowman, A.K. Misra, and I.E. Locci:NASA HITEMP Proc, NASA CP 19117, 1993, vol. II, p. 57–1.
A.B. Gokhale, L. Lu, and R. Abbaschian: inSolidification of Metal Matrix Composites, P. Rohatgi, ed., TMS, Warrendale, PA, 1990.
R.R. Bowman:Intermetallic Matrix Composites II, Materials Research Society Symposia Proceedings, D.B. Miracle, J. Graves, and D. Anton, eds., Materials Research Society, Pittsburgh, PA, 1992, vol. 273, p. 145.
Author information
Authors and Affiliations
Additional information
R. TIWARI, formerly Research Associate, Department of Chemical Engineering, Cleveland State University
Rights and permissions
About this article
Cite this article
Asthana, R., Tiwari, R. & Tewari, S.N. Influence of Cr and W alloying on the fiber-matrix interfacial shear strength in cast and directionally solidified sapphire nial composites. Metall Mater Trans A 26, 2175–2184 (1995). https://doi.org/10.1007/BF02670688
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02670688