The Modification of Al-Si Casting Alloys: Important Practical and Theoretical Aspects

  • Published:
International Journal of Metalcasting Aims and scope Submit manuscript

Abstract

A review is given of the modification of aluminum-silicon casting alloys. The mechanisms involved and important practical aspects are described. While a number of IA and IIA elements and several lanthanides produce a modified eutectic, only strontium and sodium have found significant commercial application. They react with and remove aluminum phosphide (AlP), an effective nucleant for silicon, and produce a fine fibrous eutectic. The resulting as-cast structure has improved ductility. In heat treated castings it is possible to reduce the solution time when a modifier is employed. The result is a significant cost saving—usually ten or more times the cost of the modifier addition. Modification may change the relative formation of porosity and shrinkage in a casting. This subject has been the subject of a great deal of controversy and confusion in the past, but recent research in Australia has clarified the mechanisms involved. This work is summarized and practical guidelines are offered for the foundryman. The modifiers strontium and sodium are poisoned by phosphorus, antimony and bismuth. Consequently, the levels of these impurities should be monitored carefully in secondary alloys.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. A. Pacz: U.S. Patent 1,387,900, 16 August, 1921.

  2. R.W. Smith: “Modification of Aluminum-Silicon Alloys,” Solidification of Metals, pp. 224–237, Iron and Steel Inst., London, © 1968.

    Google Scholar 

  3. P.B. Crosley and L.F. Mondolfo: “The Modification of Aluminum-Silicon Alloys,” Modern Castings, pp. 89–100 (March, 1966).

  4. Serge Bercovici: “Control of Solidification Structures and Properties of Al-Si Alloys,” Paper presented at the 45th. International Foundry Congress, Budapest (October, 1978).

  5. R.J. Kissing and J.F. Wallace: “Refinement of Aluminum-Silicon Alloys,” Foundry, Vol. 91(4), pp. 74–79 (April, 1963).

    Google Scholar 

  6. Shu-Zu Lu and A. Hellawell: “Modification of Al-Si Alloys: Microstructure, Thermal Analysis, and Mechanisms,” J. of Metals, pp. 38–40 (February, 1995).

  7. G.K. Sigworth: “Theoretical and Practical Aspects of the Modification of Al-Si Alloys,” AFS Transactions, Vol. 91, pp. 7–16 (1983).

    Google Scholar 

  8. M. Adachi: “Modification of Hypo-eutectic and Eutectic Al-Si System Casting Alloys,” J. Japan Inst. Light Metals, Vol. 34(6), pp 361–373 (1984).

    Article  Google Scholar 

  9. J.E. Gruzleski and B. Closset: The Treatment of Aluminum-Silicon Alloys, pp. 25–105, American Foundry Soc., Des Plaines, Illinois © 1990.

    Google Scholar 

  10. L. Backerud, G. Chai and J. Tamminen: Solidification Characteristics of Aluminum Alloys—Volume 2: Foundry Alloys, pp. 25–38, AFS/Skanaluminium © 1990.

  11. J.E. Grazieski: “The Art and Science of Modification: 25 Years of Progress,” AFS Transactions, Vol. 100, pp. 673–683 (1992).

    Google Scholar 

  12. M.M. Makhlouf and H.V. Guthy: “The Al-Si Eutectic Reaction: Mechanisms and Crystallography,” J. Light Metals, Vol. 1, pp. 199–218 (2001).

    Article  Google Scholar 

  13. M. Adachi: “Modification of Hypereutectic Al-Si System Casting Alloys,” J. Japan Inst. Light Metals, Vol. 34(7), pp 430–436 (1984).

    Article  Google Scholar 

  14. A.P. Bates: “Hypereutectic Aluminum-Silicon Alloys: A Review of Published Information,” Metallurgia, Vol. 61(364), pp. 70–79 (February, 1960).

    Google Scholar 

  15. J.L. Jorstad: “The Hypereutectic Al-Si Alloy Used to Cast the Vega Engine Block,” Modern Casting, Vol. 60, pp. 59–64 (October, 1971).

    Google Scholar 

  16. Y.P. Telang: “Process Variables in Al-21 Si Alloys Refinement,” Modern Casting, Vol. 43(5), pp. 232–240 (1963).

    Google Scholar 

  17. J.L. Jorstad and D. Apelian: “Hypereutectic Al-Si Alloys: Practical Processing Techniques,” Die Casting Engineer, Vol. 48(3), pp. 50–58, (May, 2004).

    Google Scholar 

  18. S. Nafisi and R. Ghomashchi: “Effects of Modification during Conventional and Semi-Solid Metal Processing of A356 Al-Si Alloy,” Materials Science and Engineering A, Vol. 415, pp. 273–285 (2006).

    Article  Google Scholar 

  19. M. Helmanova: “The Influence of Solidification Rate on the Spatial Distribution of Eutectic Silicon in Technical Silumins,” Praktische Metallographie, Vol. 12, pp. 59–68 (1975).

    Google Scholar 

  20. J. Gobrecht: “The Influence of Alloying Elements on the Duration of Modification of Na and Sr in Al-Si Cast Alloys,” Giesserei, Vol. 65, pp. 158–164 (1978).

    Google Scholar 

  21. B.M. Thall and B. Chalmers: “Modification in Aluminum-Silicon Alloys,” J. Inst. Metals, Vol. 77, pp. 79–97 (1950).

    Google Scholar 

  22. Z. Poniewierski: “Effect of the Type of Modification on the Microstructure of Al-Si Eutectic,” Rev. Hautes Temp. et Refract., Vol. 14, pp. 253–260 (1977).

    Google Scholar 

  23. F. Fommei: “Modification Treatments of Al-Si Alloys,” Aluminio, Vol. 46, pp. 121–135 (1977).

    Google Scholar 

  24. T.J. Hurley and R.G. Atkinson: “Effects of Modification Practice on Aluminum A356 Alloys,” AFS Transactions, Vol. 93, pp. 291–196 (1985).

    Google Scholar 

  25. M. Garat, G. Laslay, S. Jacob, P. Meyer, P.H. Gaerin and R. Adam: “State of the Art Use of Sb-, Na- and Sr-modified Al-Si Casting Alloys,” AFS Transactions, Vol. 100, pp. 821–832 (1992).

    Google Scholar 

  26. J.J. Jorstad and W.M. Rasmussen: Aluminum Casting Technology, 2nd. Edition, pp. 76–77, American Foundry Society, © 1993.

  27. S. Shivkumar, S. Ricci, B. Steenhoff, D. Apelian and G. Sigworth: “An Experimental Study to Optimize the Heat Treatment of A356 Alloy,” AFS Transactions, Vol. 97, pp. 791–810 (1989).

    Google Scholar 

  28. S.A. Levy: “Techniques for Improving Ductility of Low Pressure Die Cast Aluminum Wheels,” AFS Transactions, Vol. 86, pp. 135–138 (1978).

    Google Scholar 

  29. F. Paray and J.E. Grusleski: “Factors to Consider in Modification,” AFS Transactions, Vol. 102, pp. 833–842 (1994).

    Google Scholar 

  30. M. Drouzy, S. Jacob and M. Richard: “Interpretation of Tensile Results by Means of a Quality Index,” AFS International Cast Metals Journal, Vol. 5, pp 43–50 (1980).

    Google Scholar 

  31. P.Y. Zhu, Q.Y. Liu and T.X. Hon: “Spheroidization of Eutectic Silicon in Al-Si Alloys,” AFS Transactions, Vol. 91, pp. 609–614 (1983).

    Google Scholar 

  32. D.L. McLellan and M.M. Tuttle: “Aluminum Castings — A Technical Approach,” AFS Transactions, Vol. 91, pp. 243–252 (1983).

    Google Scholar 

  33. Q.C. Wang, C.H. Caceres, and J.R. Griffiths: “Damage by Eutectic Particle Cracking in Aluminum Casting Alloys A356/A357,” Met. Mater. Trans. A, Vol. 34A, pp. 2901–2912 (2003).

    Article  Google Scholar 

  34. Q.T. Fang and D.A. Granger: “Porosity Formation in Modified and Unmodified A356 Alloy Castings,” AFS Transactions, Vol. 97, pp. 989–1000 (1989).

    Google Scholar 

  35. D. Emadi and J.E. Gruzleski: “Effects of Casting and Melt Variables on Porosity in Directionally Solidified Al-Si Alloys,” AFS Transactions, Vol. 102, pp. 307–312 (1994).

    Google Scholar 

  36. J. Charbonnier: “Microprocessor Assisted Thermal Analysis Testing of Aluminum Alloy Structures,” AFS Transactions, Vol. 92, pp. 907–922 (1984).

    Google Scholar 

  37. D. Apelian, G. K. Sigworth, and K. Whaler: “Assessment of Grain Refinement and Modification of Al-Si Foundry Alloys by Thermal Analysis,” AFS Transactions, Vol. 92, pp. 297–305 (1984).

    Google Scholar 

  38. N. Tenekedjiev and J.E. Gruzleski: “Thermal Analysis of Strontium Treated Hypoeutectic and Eutectic Al-Si Casting Alloys,” AFS Transactions, Vol. 99, pp. 1–6 (1991).

    Google Scholar 

  39. G. Chai and L. Bäckerad: “Factors Affecting Modification of Al-Si Alloys by Adding Sr-Containing Master Alloys,” AFS Transactions, Vol. 100, pp. 847–854 (1992).

    Google Scholar 

  40. K. Nogita and A.K. Dahle: “Eutectic Growth Mode in Sr, Sb and P Modified Hypoeutectic Al-Si Foundry Alloys,” Materials Trans., Vol. 42(3), pp. 393–396 (2001).

    Article  Google Scholar 

  41. A. Knuutinen, K. Nogita, S.D. McDonald and A.K. Dahle: “Modification of Al-Si Alloys Modified with Ba, Ca, Y and Yb,” J. Light Metals, Vol. 1, pp. 229–240 (2001).

    Article  Google Scholar 

  42. A.K. Dahle, S.D. McDonald and K. Nogita: “Eutectic Solidification in Hypoeutectic Al-Si Alloys and Its Effect on Porosity,” Advances in Aluminum Casting Technology, pp. 1–10, M. Tiryakioglu and J. Campbell, editors, ASM International, Metals Park, Ohio, © 2002.

    Google Scholar 

  43. K. Nogita, S.D. McDonald, K. Tsujimoto, K. Yasuda and A.K. Dahle: “Aluminum Phosphide as a Eutectic Grain Nucleus in Hypoeutectic Al-Si Alloys,” J. Electron Microscopy, Vol. 53(4), pp. 361–369 (2004).

    Article  Google Scholar 

  44. A. Knuutinen, K. Nogita, S.D. McDonald and A.K. Dahle: “Modification of Al-Si Alloys with Ba, Ca, Y and Yb,” J. Light Metals, Vol. 1, pp. 229–240 (2001).

    Article  Google Scholar 

  45. C. B. Kim and R.W. Heine: “Fundamentals of Modification in the Aluminum-Silicon System,” J. Inst. Metals, Vol. 92, pp. 367–376 (1963–1964).

    Google Scholar 

  46. Y. Tsumura, A. Sakakibara, K. Toyoda and M. Ishikawa: „The Mechanism of Incubation Period of Modification Effect of Al-Si Alloy,” J. Japan Inst Light Metals, Vol. 30, pp. 239–245 (1980).

    Article  Google Scholar 

  47. N. Tenekedjiev, D. Argo and J.E. Gruzleski: “Sodium, Strontium and Phosphorus Effects in Hypereutectic Al-Si Alloys,” AFS Transactions, Vol. 97, pp. 127–136 (1989).

    Google Scholar 

  48. G. K. Sigworth: “Observations on the Refinement of Hypereutectic Al-Si Alloys,” AFS Transactions, vol. 95, pp. 303–314 (1987).

    Google Scholar 

  49. S.C. Flood and J.D. Hunt: “Modification of Al-Si Eutectic Alloys with Na,” Metal Science, Vol. 15, pp. 287–294 (1981).

    Article  Google Scholar 

  50. D.C. Jenkinson and L.M. Hogan: “The Modification of Al-Si Alloys with Strontium,” J. Crystal Growth, Vol. 28, pp. 171–187 (1975).

    Article  Google Scholar 

  51. A.K. Dahle, K. Nogita, S.D. McDonald, C. Dinnis and L. Lu: “Eutectic Modification and Microstructural Development in Al-Si Alloys,” Materials Sci. Eng. A, Vol. 413–414, pp. 243–248 (2005).

    Article  Google Scholar 

  52. K. Nogita, S.D. McDonald and A.K. Dahle: “New Approaches to Understand Modification and Nucleation Mechanisms of Hypoeutectic Al-Si Alloys,” Shape Casting: 2nd. Internat. Symposium, pp. 51–58, The Metals Society, Warrandale, Pennsylvania © 2007.

    Google Scholar 

  53. A.K. Dahle, J.A. Taylor and D.A. Graham: “The Role of Eutectic Growth Mode in Porosity Formation in Al-Si Alloys,” Aluminum Trans., Vol. 3(1), pp 17–30 (2000).

    Google Scholar 

  54. S.D. McDonald, A.K. Dahle, J.A. Taylor and D.H. StJohn: “Eutectic Grains in Unmodified and Strontium-Modified Hypoeutectic Al-Si Alloys,” Metall.Mater. Trans. A, Vol. 35A, pp. 1829–1837 (2004).

    Article  Google Scholar 

  55. S.D. McDonald, A.K. Dahle, J.A. Taylor and D.H. StJohn: “Modification-Related Porosity Formation in Hypoeutectic Al-Si Alloys,” Metall.Mater. Trans. B, Vol. 35B, pp. 1097–1106 (2004).

    Article  Google Scholar 

  56. S.D. McDonald: “Eutectic Solidification and Porosity Formation in Unmodified and Modified Hypoeutectic Al-Si Alloys,” Ph.D. Thesis, Division of Materials Engineering, University of Queensland, Brisbane, Australia, July, 2002.

    Google Scholar 

  57. J.P. Anson, M. Stucky and J.E. Gruzleski: “Effect of Sr Modification on Nucleation and Growth of Microporosity During Solidification of Al-7% Si Foundry Alloy,” AFS Transactions, Vol. 108, pp. 419–426 (2000).

    Google Scholar 

  58. J.P. Anson, M. Stucky and J.E. Gruzleski: “Effect of Sr Concentration on Microporosity Formation in A356 Aluminum Alloy,” AFS Transactions, Vol. 109, pp. 1–16 (2001).

    Google Scholar 

  59. R. Fuoco, H. Goldenstein and J.E. Gruzleski: “Evaluation of Effect of Modification Induced Undercooling on Microporosity Formation in A356 Aluminum Alloy”, AFS Transactions, Vol. 102, pp. 297–312 (1994).

    Google Scholar 

  60. R. Fuoco, E.R. Correa and A. V.O. Correa: “Effect of Modification on Microporosity Formation in 356 Aluminum Alloy,” AFS Transactions, Vol. 103, pp. 379–386 (1995).

    Google Scholar 

  61. K.J. Brondyke and P.D. Hess: “Interpretation of Vacuum Gas Test Results for Aluminum Alloys,” Trans. TMS-AIME, Vol. 230, pp. 1542–46 (1964).

    Google Scholar 

  62. E.L. Rooy and E.F. Fischer: “Control of Aluminum Casting Quality by Vacuum Solidification Tests,” AFS Transactions, Vol. 76, pp. 237–240 (1963).

    Google Scholar 

  63. K.E. Höner and Z. Youling: “Influence of Ca ans Sr on the Hydrogen Pickup in Aluminum Alloy Melts by Example of G-AlSi12,” Giesserei-Forschung, Vol. 39(11), pp. 34–48 (1987).

    Google Scholar 

  64. L. Liu, A.M. Samuel, F.H. Samuel, H.W. Doty and S. Valtierra: “Influence of Oxides on Porosity Formation of Sr-Treated Al-Si Casting Alloys,” J. Materials Sci., Vol. 38, pp 1255–67 (2003).

    Article  Google Scholar 

  65. D. Emadi, J.E. Gruzleski and M. Pekguleryuz: “Melt Oxidation Behavior and Inclusion Content in Unmodified and Sr-Modified A356 Alloy—Their Role in Pore Nucleation,” AFS Transactions, Vol. 104, pp. 763–768 (1996).

    Google Scholar 

  66. S. McDonald, M. Dargusch, G. Song and D. StJohn: “Unintentional Effects of Sr Additions in Al-Si Foundry Alloys,” Shape Casting: 2nd. Internat. Symposium, pp. 59–66, The Metals Society, Warrandale, Pennsylvania © 2007.

    Google Scholar 

  67. H. Iwahori, K. Yonekura, Y. Sugiyama, Y. Yamamoto and M. Nakamura: “Behavior of Shrinkage Porosity Defects and Limiting Solid Fraction of Feeding on Al-Si Alloys,” AFS Transactions, Vol. 93, pp. 443–451 (1985).

    Google Scholar 

  68. H. Iwahori, K. Yonekura, Y. Yamamoto and M. Nakamura: “Occurring Behavior of Porosity and Feeding Capabilities of Sodium- and Strontium-Modified Al-Si Alloys,” AFS Transactions, Vol. 98, pp. 167–173 (1990).

    Google Scholar 

  69. R. Fuoco, E.R. Correa and H. Goldenstein: “Effect of Modification on Microporosity in 356 Aluminum Alloy,” AFS Transactions, Vol. 104, pp. 1151–1157 (1996).

    Google Scholar 

  70. Ø. Nielsen and S.O. Olsen: “Experiment for Quantification of Feedability and Permeability in Industrial Aluminum Alloys,” Internat. J. Cast Metals Research, Vol. 19(1), pp. 32–37 (2006).

    Article  Google Scholar 

  71. J.M. Kim, H.W. Kwon and C.R. Loper, Jr.: “Feeding Behavior of Modified and Unmodified Al-Si Alloys,” AFS Transactions, Vol. 104, pp. 743–749 (1996).

    Google Scholar 

  72. P.D. Hess and E.V. Blackmun: “Strontium as Modifying Agent for Hypoeutectic Aluminum-Silicon Alloys,” AFS Transactions, Vol. 92, pp. 87–90 (1975).

    Google Scholar 

  73. S.D. McDonald, K. Nogita, A.K. Dahle, J.A. Taylor and D.H. StJohn: “Eutectic Solidification and Porosity Formation in Al-Si Alloys: Role of Strontium,” AFS Transactions, Vol. 108, pp. 463–470 (2000).

    Google Scholar 

  74. C.M. Dinnis, A.K. Dahle and J.A. Taylor: “Eutectic Morphology and Porosity in Unmodified and Sr-Modified Al-Si Alloys,” AFS Transactions, Vol. 113, pp. 99–106 (2005).

    Google Scholar 

  75. D. Argo and J.E. Gruzleski: “Porosity in Modified Aluminum Alloy Castings,” AFS Transactions, Vol. 96, pp. 65–74 (1988).

    Google Scholar 

  76. Z. Li, A.M. Samuel, F.H. Samuel, C. Ravrindran and S. Valtierra: “Effect of Alloying Elements on the Segregation and Dissolution of CuAl2 Phase in Al-Si-Cu 319 Alloys,” J. Materials Sci., Vol. 38, pp. 1203–1218 (2003).

    Article  Google Scholar 

  77. F.H. Samuel, A.M. Samuel and H.W. Doty: “Factors Controlling the Type and Morphology of Cu-Containing Phases in 319 Aluminum Alloy,” AFS Transactions, Vol. 104, pp. 893–901 (1996).

    Google Scholar 

  78. M. Djurdjevic, T. Stockwell and J. Sokolowski: “Effect of Strontium on Microstructure of Al-Si and Al-Cu Eutectics in 319 Aluminum Alloy,” Internat. J. Cast Metals Res., Vol. 12, pp. 67–73 (1999).

    Google Scholar 

  79. B. Closset and S. Kitaoka: “Evaluation of Sr Modifiers for Al-Si Casting Alloys,” AFS Transactions, Vol. 85, pp. 233–240 (1987).

    Google Scholar 

  80. M.O. Pekguleryuz and J.E. Gruzleski: “Conditions for Strontium Master Alloy Additions to A356 Melts,” AFS Transactions, Vol. 96, pp. 55–64 (1988).

    Google Scholar 

  81. G. Chai and L. Bäckerud: “Factors Affecting Modification of Al-Si Alloys by Adding Sr-Containing Master Alloys”, AFS Transactions, Vol. 100, pp. 847–854 (1992).

    Google Scholar 

  82. B. Closset and J.E. Gruzleski: “Mechanical Properties of A356 Alloy Modified with Pure Strontium,” AFS Transactions, Vol. 90, pp. 453–464 (1982).

    Google Scholar 

  83. R. DasGupta, C.G. Brown and S. Marek: “Analysis of Overmodified 356 Aluminum Alloy,” AFS Transactions, Vol. 96, pp. 297–310 (1988).

    Google Scholar 

  84. J. Gruzleski, N. Handiak, H. Campbell and B. Closset: “Hydrogen Measurement by Telegas in Sr-Treated A356 Melts,” AFS Transactions, Vol. 94, pp. 147–154 (1986).

    Google Scholar 

  85. F.C. Dinayuga, N. Handiak and J.E. Gruzleski: “The Degassing and Regassing Behavior of Sr-Modified A356 Melts,” AFS Transactions, Vol. 96, pp. 83–88 (1988).

    Google Scholar 

  86. X.-G. Chen, F.J. Klinkenberg, R. Ellerbrok and S. Engler: “Efficiency of Impeller Degassing and Regassing Phenomena in Aluminum Melts,” AFS Transactions, Vol. 102, pp. 191–197 (1994).

    Google Scholar 

  87. G.K. Sigworth, C. Wang, H. Huang and J. T. Berry: “Porosity Formation in Modified and Unmodified Al-Si Alloy Castings,” AFS Transactions, Vol. 102, pp. 245–261 (1994).

    Google Scholar 

  88. B. Gallois and G. K. Sigworth: “An Analysis of Silicon Eutectic Modification,” Thermal Analysis of Molten Aluminum, pp. 101–119, Amer. Foundry Society, Des Plaines, IL, © 1985.

    Google Scholar 

  89. H. Fredriksson, M. Hillert and N. Lange: “Modification of Aluminum Silicon Alloys by Sodium,” J. Inst. Metals, Vol. 101, pp 285–299 (1973).

    Google Scholar 

  90. M.G. Day and A. Hellawell: “The Microstructure and Crystallography of Aluminium-Silicon Eutectic Alloys,” Proc. Roy. Soc., Vol. 305A, pp. 473–491 (1968).

    Article  Google Scholar 

  91. Shu-Zu Lu and A. Hellawell: “Mechanisms of Silicon Modification in Aluminum-Silicon Alloys: Impurity Induced Twinning,” Metall. Trans. A, Vol. 18A, pp. 1721–1731 (1987).

    Article  Google Scholar 

  92. A. Hellawell: “How Does a Modifier Work?,” pp. 9-1 to 9-17, Proc. 2nd. Internat. Conference on Molten Aluminum Processing, American Foundry Soc., © 1989.

  93. R. Elliott: Eutectic Solidification Processing, Butterworth, London, 1983.

    Google Scholar 

  94. R. Elliott: “Growth Kinetics in Aluminum Silicon Eutectic Alloys,” pp. 10-1 to 10-24, Proc. 2nd. Internat. Conference on Molten Aluminum Processing, American Foundry Soc., © 1989.

  95. L. Clapham and R.W. Smith: “Partial Modification in Unidirectionally Solidified Al-Si Eutectic Alloys,” Acta Metall., Vol. 37(1), pp. 303–311 (1989).

    Article  Google Scholar 

  96. J.F. Major and J.W. Rutter: “Effect of Strontium and Phosphorus on Solid/Liquid Interface of Al-Si Eutectic,” Mater. Sci. Technol., Vol. 5(7), pp. 645–656 (1989).

    Article  Google Scholar 

  97. G. K. Sigworth: “Determining Grain Size and Eutectic Modification in Aluminum Alloy Castings,” Modern Casting, Vol. 77, pp. 23–25, July, 1987.

    Google Scholar 

  98. S.D. McDonald, K. Nogita and A.K. Dahle: “Eutectic Nucleation in Al-Si Alloys,” Acta Mater., Vol. 52, pp. 4273–4280 (2004).

    Article  Google Scholar 

  99. CR. Loper, Jr., H.-G. Seong and J.-I. Cho: “Interaction of Phosphorus and Bismuth (with Sr) in A356.2 Alloy,” AFS Transactions, Vol. 109, pp. 1–13 (2001).

    Google Scholar 

  100. C.R. Loper, Jr. and J.-I. Cho: “Influence of Trace Amounts of Phosphorus in Aluminum Castings,” AFS Transactions, Vol. 108, pp. 667–672 (2000).

    Google Scholar 

  101. B. Günther and H. Jürgens: “Influence of Minor Impurities on Mechanical Properties, Structure and Solidification Form of Eutectic on Near-Eutectic Al-Si Casting Alloys,” Giesserei, Vol. 67, pp. 8–13 (1980).

    Google Scholar 

  102. S. Bercovici, M. Garat and R. Scalliet: “A Review of Recent French Casting Alloy Developments,” Report 13691, April, 1978, Pechiney Ugine Kuhlmann, 125 Third Ave., N.Y., New York, 10022.

  103. N. Handiak, J.E. Gruzleski and D. Argo: “Sodium, Strontium and Antimony Interactions During Modification of AS7G03 (A356) Alloys,” AFS Transactions, Vol. 95, pp. 31–38 (1987).

    Google Scholar 

  104. E.N. Pan, Y.C. Cherng, C.A. Lin and H.S. Chiou: “Roles of Sr and Sb on Silicon Modification of A356 Aluminum Alloys”, AFS Transactions, Vol. 102, pp. 609–629 (1994).

    Google Scholar 

  105. B.L. Tuttle, D Twarog and E. Daniels: “The Effect of Trace Amounts of Antimony on the Structure and Properties of Aluminum Alloy A356.2,” AFS Transactions, Vol. 99, pp. 7–16 (1991).

    Google Scholar 

  106. W. Wang and J.E. Gruzleski: “Interactive Effects During Sodium or Strontium Treatment of Antimony-Containing A356 Alloy,” AFS Transactions, Vol. 98, pp. 227–234 (1990).

    Google Scholar 

  107. Anon.: “Incompatibility of Sodium and Antimony in the Modification of Al-Si Alloys,” Fondeur D’aujord’hui, Vol. 272, pp. 12–13 (1976).

  108. S. El-Hadad, A.M. Samuel, F.H. Samuel, H. W. Doty and S. Valtierra: “Effect of Bi and Ca Additions on the Characteristics of Eutectic Silicon Particles in Sr-Modified 319 Alloys,” Internat. J. Cast Metals Res., Vol. 15, pp. 551–564 (2003).

    Google Scholar 

  109. C.J. Machovec, G.E. Byczynski, J.W. Zinel and L.A. Godlewski: “Effect of Bi-Sr Interactions on Si Morphology in a 319 Type Aluminum Alloy,” AFS Transactions, Vol. 108, pp. 439–444 (2000).

    Google Scholar 

  110. G. Heiberg et al.: “Effect of Mg, Fe and Cu on Eutectic Solidification of Hypoeutectic Al-Si Alloys,” AFS Transactions, Vol. 110, pp. 347–358 (2002).

    Google Scholar 

  111. B. Golhahar, A.M. Samuel, F.H. Samuel, H.W. Doty and S. Valtierra: “Effect of Grain Refiner-Modifier Interactions on the Microstructure and Mechanical Properties of A356 Alloys,” AFS Transactions, Vol. 115, paper 07–012 (2007).

    Google Scholar 

  112. A. Abdollahi and J.E. Gruzleski: “Evaluation of Calcium as a Eutectic Modifier in A357 Alloy,” Internat. J. Cast Metals Res., Vol. 11, pp 145–155 (1998).

    Google Scholar 

  113. C.R. Loper, Jr. and J.-I. Cho: “Influence of Trace Amounts of Calcium in Aluminum Castings,” AFS Transactions, Vol. 108, pp. 585–592 (2000).

    Google Scholar 

  114. L. Lu and A.K. Dahle: “Iron-Rich Intermetallic Phases and their Role in Casting Defect Formation in Hypoeutectic Al-Si Alloys,” Met. Mater. Trans. A, Vol. 36A, pp. 819–835 (2005).

    Google Scholar 

  115. W. Kalifa, A.M. Samuel, F.H. Samuel, H.W. Doty and S. Valtierra: “Metallographic Observations of β-AlFeSi Phase and its Role in Porosity Formation in Al-7%Si Alloys,” Internat. J. Cast Metals Res., Vol. 19, pp. 156–166 (2006).

    Article  Google Scholar 

  116. B. Kulunk, S.G. Shabestari and J.E. Gruzleski: “Beneficial Effects of Strontium in A380 Alloy,” AFS Transactions, Vol. 104, pp. 1189–1193 (1996).

    Google Scholar 

  117. S.G. Shabestari and J.E. Gruzleski: “Modification of Iron Intermetallics by Strontium in 413 Aluminum Alloy,” AFS Transactions, Vol. 103, pp. 285–293 (1995).

    Google Scholar 

  118. X. Jian, C. Xu, T. Meek and Q. Han: “Effect of Ultrasound Vibration on the Solidification Structure of A356 Alloy,” AFS Transactions, Vol. 113, pp. 131–138 (2005).

    Google Scholar 

  119. P.D. Lee and T.C. Lindley: “The Influence of Sr and TiB2 Additions on the Formation of Porosity in Aluminum Castings and Their Effect on Fatigue Properties,” Shape Casting: The J. Campbell Symposium, pp. 225–234, The Metals Soc. © 2005.

  120. E. Sato, T. Saga and S. Nagai: “Effects of Additional Elements on the Machinability of Al-Si Casting Alloys,” J. Japan. Inst. Light Metals, Vol. 33(11), pp 649–654 (1983).

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Alcoa Primary Metals, Rockdale, Texas, USA

    G. K. Sigworth

Authors
  1. G. K. Sigworth
    View author publications

    You can also search for this author in PubMed Google Scholar

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Sigworth, G.K. The Modification of Al-Si Casting Alloys: Important Practical and Theoretical Aspects. Inter Metalcast 2, 19–40 (2008). https://doi.org/10.1007/BF03355425

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/BF03355425

Keywords

Search

Navigation