Densification of wood veneers by compression combined with heat and steam

Wood veneer 700×700 mm² specimens made with aspen (Populus tremuloides) and hybrid poplar clone 15303 (Populus maximowiczii × Populus balsamifera) were densified using heat, steam, and pressure. Temperatures of 140, 160, 180, 200, and 220°C were applied at a maximum steam pressure of 550 kPa and maximum press hydraulic pressure ranging from 4.5 to 9.0 MPa. After densification, the oven-dry density increased significantly, veneers darkened, and lathe checks that were present on veneers before densification were conglutinated and veneer surface roughness decreased. Densified veneers showed markedly reduced hygroscopicity: the higher the densification temperature, the lower the wood hygroscopicity. The Brinell hardness of densified veneer was about two to three times that of control for both aspen and hybrid poplar. Tensile and bending strength also increased significantly after densification. However, the mechanical properties of densified veneers decreased slightly with increased densification temperature. The modulus of elasticity in tension and bending increased after densification, especially at high temperatures. A very high compression set recovery was found for veneers densified at low temperatures. Recovery decreased dramatically when densification temperature exceeded 180°C. Almost no recovery was found for veneers densified at 220°C.