Abstract
The temperature scaling of the ferroelectric hysteresis was investigated in hard lead zirconate titanate (PZT) bulk ceramic. The power-law temperature scaling relations were obtained for hystersis area 〈A〉, remnant polarization Pr, and coercivity EC in the forms of 〈A〉∝T-0.9650, Pr∝T-0.0261, and EC∝T-0.8823, respectively, which are mostly comparable to those of its soft counterpart. The observation that Pr decayed more slowly with temperature than in soft PZT was attributed to the presence of the complex defects in hard PZT. However, the product of Pr and EC still provided the similar scaling law on the T dependence in comparison with 〈A〉.
Similar content being viewed by others
References
K. Uchino, Piezoelectric Actuators and Ultrasonic Motors (Kluwer, Boston, 1997), p. 129
B. Jaffe, W.R. Cook, H. Jaffe, Piezoelectric Ceramics (Academic, New York, 1971), p. 271
M.E. Lines, A.M. Glass, Principles and Applications of Ferroelectrics and Related Materials (Clarendon, Oxford, 1977), p. 102
K. Uchino, Ferroelectric Devices (Dekker, New York, 2000), p. 145
K. Carl, K.H. Hardtl, Ferroelectrics 17, 473 (1978)
Q.M. Zhang, H. Wang, N. Kim, L.E. Cross, J. Appl. Phys. 75, 454 (1994)
T. Tsurumi, T. Sasaki, H. Kakemoto, T. Harigai, S. Wada, Japan. J. Appl. Phys. Part 1 43, 7618 (2004)
M.H. Lente, A. Picinin, J.P. Rino, J.A. Eiras, J. Appl. Phys. 95, 2646 (2004)
Q. Tan, J. Li, D. Viehland, Appl. Phys. Lett. 75, 418 (1999)
M. Morozov, D. Damjanovic, N. Setter, J. Eur. Ceram. Soc. 25, 2483 (2005)
W. Chang, A.H. King, K. Bowman, Appl. Phys. Lett. 88, 242901 (2006)
S.K. Pandey, O. P Thakur, A. Kumar, C. Prakash, R. Chatterjee, T.C. Goel, J. Appl. Phys. 100, 014104 (2006)
Q. Tan, D. Viehland, J. Am. Ceram. Soc. 81, 328 (1998)
B.S. Li, G.R. Li, Q.R. Yin, Z.G. Zhu, A.L. Ding, W.W. Cao, J. Phys. D Appl. Phys. 38, 1107 (2005)
O. Lohse, D. Bolten, S. Tiedke, T. Schneller, R. Waser, Proc. IEEE-ISAF 98 1, 27 (1998)
G.L. Yuan, J.-M. Liu, S.T. Zhang, D. Wu, Y.P. Wang, Z.G. Liu, H.L.W. Chan, C.L. Choy, Appl. Phys. Lett. 84, 954 (2004)
R. Yimnirun, R. Wongmaneerung, S. Wongsaenmai, A. Ngamjarurojana, S. Ananta, Y. Laosiritaworn, Appl. Phys. Lett. 90, 112906 (2007)
R. Yimnirun, Y. Laosiritaworn, S. Wongsaenmai, S. Ananta, Appl. Phys. Lett. 89, 162901 (2006)
R. Yimnirun, R. Wongmaneerung, S. Wongsaenmai, A. Ngamjarurojana, S. Ananta, Y. Laosiritaworn, Appl. Phys. Lett. 90, 112908 (2007)
J.-M. Liu, H.P. Li, C.K. Ong, L.C. Lim, J. Appl. Phys. 86, 5198 (1999)
Author information
Authors and Affiliations
Corresponding author
Additional information
PACS
77.80.-e; 77.80.Fm; 77.84.-s; 77.84.Dy
Rights and permissions
About this article
Cite this article
Yimnirun, R., Ngamjarurojana, A., Wongmaneerung, R. et al. Temperature scaling of ferroelectric hysteresis in hard lead zirconate titanate bulk ceramic. Appl. Phys. A 89, 737–741 (2007). https://doi.org/10.1007/s00339-007-4156-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-007-4156-9