Abstract
The selective structuring of thin molybdenum (Mo) films is a major challenge for the monolithic interconnection of CIS thin film solar cells during their production. Here we present the structuring of ca. 0.5 μm thin molybdenum films on glass substrates with picosecond laser pulses (pulse duration 10 ps, wavelength 1064 nm) without any visible thermal effect on both, the remaining film and the substrate material. When the molybdenum film is irradiated from the transparent substrate side with a fluence level below 1 J/cm2 a “lift-off” process is initiated, which seems to be induced by a direct effect in the removed molybdenum film. At that fluence level, the energy input per ablated volume of ca. 30 J/mm3 is much less than would be needed for a thermodynamic heating, melting and vaporization of the complete film with ca. 78 J/mm3. Therefore we conclude that the molybdenum is only evaporated partially. Parts of the ablated Mo-film can be found as structurally intact debris. We assume that partial melting and vaporization with high-pressure formation play an important role during that picosecond laser ablation without thermal side effects. Due to its remarkable physical nature we called that process “directly induced laser ablation”.
Similar content being viewed by others
References
B.N. Chichkov, C. Momma, S. Nolte, F. Von Alvensleben, A. Tuennermann, Appl. Phys. A, Mater. Sci. Process. 63, 109 (1997)
S. Nolte, C. Momma, H. Jacobs, A. Tuennermann, B.N. Chichkov, B. Wellegehausen, H. Welling, J. Opt. Soc. Am. B, Opt. Phys. 14, 2716 (1997)
P.B. Corkum, F. Brunel, N.K. Sherman, T. Srinivasan-Rao, Phys. Rev. Lett. 61, 2886 (1988)
A.P. Kanavin, I.V. Smetanin, V.A. Isakov, Y.V. Afanasiev, B.N. Chichkov, B. Wellegehausen, S. Nolte, C. Momma, A. Tuennermann, Phys. Rev. B, Condens. Matter Mater. Phys. 57, 14698 (1998)
S.I. Anisimov, B.L. Kapeliovich, T.L. Perel’Man, Sov. Phys. JETP 39, 375 (1974)
G. Paltauf, P.E. Dyer, Chem. Rev. 103, 487 (2003)
S. Preuss, A. Demchuk, M. Stuke, Appl. Phys. A, Mater. Sci. Process. 61 (1995)
S. Zoppel, H. Huber, G.A. Reider, Appl. Phys. A, Mater. Sci. Process. 89, 161 (2007)
S. Hermann, N.P. Harder, R. Brendel, D. Herzog, H. Haferkamp, Appl. Phys. A, Mater. Sci. Process. 1 (2009)
H.P. Huber, M. Englmaier, C. Hellwig, G. Heise, M. Kemnitzer, T. Kuznicki, C. Menhard, R. Brenning, A. Heiss, H. Vogt, J. Palm, in Proceedings of 24rd EUPVSEC (2009)
H.P. Huber, M. Englmaier, C. Hellwig, A. Heiss, T. Kuznicki, M. Kemnitzer, H. Vogt, R. Brenning, J. Palm, in Proceedings of SPIE Commercial and Biomedical Applications of Ultrafast Lasers IX, vol. 7203 (2009)
H.P. Huber, F. Herrnberger, S. Kery, S. Zoppel, Proceedings of SPIE Vol. 6881 (2008)
F.H. Karg, Sol. Energy Mater. Solar Cells 66 (2001)
B. Dimmler, H.W. Schock, Prog. Photovolt. 4, 425 (1996)
J. Hermann, M. Benfarah, S. Bruneau, E. Axente, G. Coustillier, T. Itina, J.-F. Guillemoles, P. Alloncle, J. Phys. D, Appl. Phys. 39, 453 (2006)
L. Stolt, J. Hedström, J. Kessler, M. Ruckh, K.O. Velthaus, H.W. Schock, Appl. Phys. Lett. 62, 597 (1993)
C. Molpeceres, S. Lauzurica, J.L. Ocana, J.J. Gandia, L. Urbina, J. Carabe, J. Micromech. Microeng. 15, 1271 (2005)
A.D. Compaan, I. Matulionis, S. Nakade, Opt. Lasers Eng. 34, 15 (2000)
R. Mayerhofer, L. Muellers, A. Becker, in Conference Record of the 2006 IEEE 4th World Conference on Photovoltaic Energy Conversion, WCPEC-4 1, 1115 (2007)
A.B. Bullock, P.R. Bolton, J. Appl. Phys. 85, 460 (1999)
S. Beyer, V. Tornari, D. Gornicki, Proc. SPIE 5063, 202 (2003)
J.M. Liu, Opt. Lett. 7, 196 (1982)
D.R. Lide, Handbook of Chemistry and Physics (2004)
R. Iffländer, Solid-State Lasers for Materials Processing (Springer, Berlin, 2001)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Heise, G., Englmaier, M., Hellwig, C. et al. Laser ablation of thin molybdenum films on transparent substrates at low fluences. Appl. Phys. A 102, 173–178 (2011). https://doi.org/10.1007/s00339-010-5993-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-010-5993-5