Rheology of SiO₂/(acrylic polymer/epoxy) suspensions. I. Linear viscoelasticity

Linear viscoelastic properties of SiO₂/(AP/EP) suspension with various SiO₂ volume fractions (ϕ) in a blend of acrylic polymer (AP) and epoxy (EP) were investigated at various temperatures (T). The AP/EP contained 70 vol.% of EP. The SiO₂ particles were treated with epoxy silane coupling agent. The effects of the SiO₂ particles are more pronounced in the terminal zone: a transition from viscoelastic liquid (ϕ ≤ 30 vol.%) to viscoelastic solid (ϕ ≥ 40 vol.%) was observed which can be interpreted as a critical gelation occurring at a critical particle content and critical gel temperature. The SiO₂/(AP/EP) systems exhibited a critical gel behavior at ϕ ≅ 35 vol.% and T ≅ 100°C characterized with a power–law relationship between the storage and loss moduli (G ^′ and G ^″) and frequency (ω); G ^′ = G ^″/tan(nπ/2) ∝ ω ⁿ . The critical gel exponent (n) was estimated to be about 0.45. The gelation occurred with increasing T.