Nanocomposite-based lignocellulosic fibers 3: polyelectrolyte adsorption onto heterogeneous fiber surfaces

verfasst von: Zhiyuan Lin, Scott Renneckar

Erschienen in: Cellulose | Ausgabe 3/2011

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Wood and natural fibers are composed of multiple polymeric components. Lignin, one primary component, is typically removed to various degrees during paper-making, but is present on thermomechanically isolated fibers. The effect of the residual lignin on the adsorption of poly(diallyldimethylammonium) chloride (PDDA) onto lignocellulosic fibers was investigated under varying solution conditions (electrolyte concentration and pH). Using nitrogen elemental analysis it was shown for the samples containing the highest concentration of lignin, PDDA adsorption to the fibers was reduced for all solution conditions. Upon extracting the alkali-soluble lignin, the samples showed the greatest amount of PDDA adsorption, achieving ~1.6% (w/w), under neutral solution conditions without the presence of added electrolyte. Furthermore, the influence of polyelectrolyte loading and electrokinetic potential on subsequent multilayer formation of PDDA and montmorillonite clay was quantified. It was revealed that electrokinetic potential of fiber after PDDA adsorption, rather than the amount of adsorbed PDDA layer, controlled the subsequent clay adsorption. Significant mass of PDDA/clay (up to ~75% of starting dry fiber mass for only 4 bi-layers) can be adsorbed onto steam-exploded wood fibers through the multilayer assembly process. This paper provides insight into how non-covalent modification of heterogeneous fibrous substrates offers a novel route for the creation of organic/inorganic fiber materials.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Literatur
Zurück zum Zitat Allan GG, Reif WM (1971a) Fiber surface modification. 6. Jack-in-the-Box effect: new mechanism for the retention of poly(ethylenimine) and other polyelectrolytes by pulp fibers. Sv Papperstidn 74:25–31 Allan GG, Reif WM (1971a) Fiber surface modification. 6. Jack-in-the-Box effect: new mechanism for the retention of poly(ethylenimine) and other polyelectrolytes by pulp fibers. Sv Papperstidn 74:25–31
Zurück zum Zitat Allan GG, Reif WM (1971b) Fiber surface modification. Stereotopochemistry of ionic bonding in paper. Sv Papperstidn 74:563–570 Allan GG, Reif WM (1971b) Fiber surface modification. Stereotopochemistry of ionic bonding in paper. Sv Papperstidn 74:563–570
Zurück zum Zitat Ariga K, Hill JP, Ji Q (2007) Layer-by-layer assembly as a versatile bottom-up nanofabrication technique for exploratory research and realistic application. Phys Chem Chem Phys 9:2319–2340CrossRef Ariga K, Hill JP, Ji Q (2007) Layer-by-layer assembly as a versatile bottom-up nanofabrication technique for exploratory research and realistic application. Phys Chem Chem Phys 9:2319–2340CrossRef
Zurück zum Zitat Cheng L, Cox JA (2001) Preparation of multilayered nanocomposites of polyoxometalates and poly(amidoamine) dendrimers. Electrochem Commun 3:285–289CrossRef Cheng L, Cox JA (2001) Preparation of multilayered nanocomposites of polyoxometalates and poly(amidoamine) dendrimers. Electrochem Commun 3:285–289CrossRef
Zurück zum Zitat Decher G (1997) Fuzzy nanoassemblies: toward layered polymeric multicomposites. Science 277:1232–1237 (Washington, DC)CrossRef Decher G (1997) Fuzzy nanoassemblies: toward layered polymeric multicomposites. Science 277:1232–1237 (Washington, DC)CrossRef
Zurück zum Zitat Decher G, Hong JD (1991) Buildup of ultrathin multilayer films by a self-assembly process. 1. Consecutive adsorption of anionic and cationic bipolar amphiphiles on charged surfaces. Makromol Chem Macromol Symp 46:321–327CrossRef Decher G, Hong JD (1991) Buildup of ultrathin multilayer films by a self-assembly process. 1. Consecutive adsorption of anionic and cationic bipolar amphiphiles on charged surfaces. Makromol Chem Macromol Symp 46:321–327CrossRef
Zurück zum Zitat Donaldson LA, Wong KKY, Mackie KL (1988) Ultrastructure of steam-exploded wood. Wood Sci Technol 22:103–114CrossRef Donaldson LA, Wong KKY, Mackie KL (1988) Ultrastructure of steam-exploded wood. Wood Sci Technol 22:103–114CrossRef
Zurück zum Zitat Elbert DL, Herbert CB, Hubbell JA (1999) Thin polymer layers formed by polyelectrolyte multilayer techniques on biological surfaces. Langmuir 15:5355–5362CrossRef Elbert DL, Herbert CB, Hubbell JA (1999) Thin polymer layers formed by polyelectrolyte multilayer techniques on biological surfaces. Langmuir 15:5355–5362CrossRef
Zurück zum Zitat Eriksson M, Notley SM, Wagberg L (2005) The influence on paper strength properties when building multilayers of weak polyelectrolytes onto wood fibers. J Colloid Interface Sci 292:38–45CrossRef Eriksson M, Notley SM, Wagberg L (2005) The influence on paper strength properties when building multilayers of weak polyelectrolytes onto wood fibers. J Colloid Interface Sci 292:38–45CrossRef
Zurück zum Zitat Erspamer A (1940) The flocculation and dispersion of papermaking fibers. Pap Trade J 110:33–38 Erspamer A (1940) The flocculation and dispersion of papermaking fibers. Pap Trade J 110:33–38
Zurück zum Zitat Formento JC, Maximino MG, Mina LR, Srayh MI, Martinez MJ (1994) Cationic starch in the wet end: its contribution to interfiber bonding. Appita J 47:305–308 Formento JC, Maximino MG, Mina LR, Srayh MI, Martinez MJ (1994) Cationic starch in the wet end: its contribution to interfiber bonding. Appita J 47:305–308
Zurück zum Zitat Fras L, Laine J, Stenius P, Stana-Kleinschek K, Ribitsch V, Dolecek V (2004) Determination of dissociable groups in natural and regenerated cellulose fibers by different titration methods. J Appl Polym Sci 92:3186–3195CrossRef Fras L, Laine J, Stenius P, Stana-Kleinschek K, Ribitsch V, Dolecek V (2004) Determination of dissociable groups in natural and regenerated cellulose fibers by different titration methods. J Appl Polym Sci 92:3186–3195CrossRef
Zurück zum Zitat Gimaker M, Wagberg L (2009) Adsorption of polyallylamine to lignocellulosic fibres: effect of adsorption conditions on localisation of adsorbed polyelectrolyte and mechanical properties of resulting paper sheets. Cellulose 16:87–101 (Dordrecht, Neth)CrossRef Gimaker M, Wagberg L (2009) Adsorption of polyallylamine to lignocellulosic fibres: effect of adsorption conditions on localisation of adsorbed polyelectrolyte and mechanical properties of resulting paper sheets. Cellulose 16:87–101 (Dordrecht, Neth)CrossRef
Zurück zum Zitat Glasser WG, Taib R, Jain RK, Kander R (1999) Fiber-reinforced cellulosic thermoplastic composites. J Appl Polym Sci 73:1329–1340CrossRef Glasser WG, Taib R, Jain RK, Kander R (1999) Fiber-reinforced cellulosic thermoplastic composites. J Appl Polym Sci 73:1329–1340CrossRef
Zurück zum Zitat Horvath AE, Lindstrom T, Laine J (2006) On the indirect polyelectrolyte titration of cellulosic fibers. Conditions for charge stoichiometry and comparison with ESCA. Langmuir 22:824–830CrossRef Horvath AE, Lindstrom T, Laine J (2006) On the indirect polyelectrolyte titration of cellulosic fibers. Conditions for charge stoichiometry and comparison with ESCA. Langmuir 22:824–830CrossRef
Zurück zum Zitat Horvath AT, Horvath AE, Lindstrom T, Wagberg L (2008a) Adsorption of highly charged polyelectrolytes onto an oppositely charged porous substrate. Langmuir 24:7857–7866CrossRef Horvath AT, Horvath AE, Lindstrom T, Wagberg L (2008a) Adsorption of highly charged polyelectrolytes onto an oppositely charged porous substrate. Langmuir 24:7857–7866CrossRef
Zurück zum Zitat Horvath AT, Horvath AE, Lindstrom T, Wagberg L (2008b) Diffusion of cationic polyelectrolytes into cellulosic fibers. Langmuir 24:10797–10806CrossRef Horvath AT, Horvath AE, Lindstrom T, Wagberg L (2008b) Diffusion of cationic polyelectrolytes into cellulosic fibers. Langmuir 24:10797–10806CrossRef
Zurück zum Zitat Hubbe MA (2006) Sensing the electrokinetic potential of cellulosic fiber surfaces. BioResources 1:116–149 Hubbe MA (2006) Sensing the electrokinetic potential of cellulosic fiber surfaces. BioResources 1:116–149
Zurück zum Zitat Hunter RJ (ed) (1981) Colloid Science: Zeta Potential in Colloid Science: Principles and Applications Hunter RJ (ed) (1981) Colloid Science: Zeta Potential in Colloid Science: Principles and Applications
Zurück zum Zitat Hyde K, Rusa M, Hinestroza J (2005) Layer-by-layer deposition of polyelectrolyte nanolayers on natural fibers: cotton. Nanotechnology 16:422–428CrossRef Hyde K, Rusa M, Hinestroza J (2005) Layer-by-layer deposition of polyelectrolyte nanolayers on natural fibers: cotton. Nanotechnology 16:422–428CrossRef
Zurück zum Zitat Ibrahim M, Glasser WG (1999) Steam-assisted biomass fractionation. Part III: a quantitative evaluation of the “clean fractionation” concept. Bioresour Technol 70:181–192CrossRef Ibrahim M, Glasser WG (1999) Steam-assisted biomass fractionation. Part III: a quantitative evaluation of the “clean fractionation” concept. Bioresour Technol 70:181–192CrossRef
Zurück zum Zitat Katz S, Beatson RP, Scallan AM (1984) The determination of strong and weak acidic groups in sulfite pulps. Sv Papperstidn 87:R48–R53 Katz S, Beatson RP, Scallan AM (1984) The determination of strong and weak acidic groups in sulfite pulps. Sv Papperstidn 87:R48–R53
Zurück zum Zitat Kotov NA, Haraszti T, Turi L, Zavala G, Geer RE, Dekany I, Fendler JH (1997) Mechanism of and defect formation in the self-assembly of polymeric polycation-montmorillonite ultrathin films. J Am Chem Soc 119:6821–6832CrossRef Kotov NA, Haraszti T, Turi L, Zavala G, Geer RE, Dekany I, Fendler JH (1997) Mechanism of and defect formation in the self-assembly of polymeric polycation-montmorillonite ultrathin films. J Am Chem Soc 119:6821–6832CrossRef
Zurück zum Zitat Laatikainen M (1989) Adsorption of cationic compounds on groundwood and on cellulose and lignin surfaces. J Colloid Interface Sci 132:451–461CrossRef Laatikainen M (1989) Adsorption of cationic compounds on groundwood and on cellulose and lignin surfaces. J Colloid Interface Sci 132:451–461CrossRef
Zurück zum Zitat LeBaron PC, Wang Z, Pinnavaia TJ (1999) Polymer-layered silicate nanocomposites: an overview. Appl Clay Sci 15:11–29CrossRef LeBaron PC, Wang Z, Pinnavaia TJ (1999) Polymer-layered silicate nanocomposites: an overview. Appl Clay Sci 15:11–29CrossRef
Zurück zum Zitat Lin Z, Renneckar S (2010) Nanocomposite-based lignocellulosic fibers 2: layer-by-layer modification of wood fibers for reinforcement in thermoplastic composites. Composites: Part A 42:84–91 Lin Z, Renneckar S (2010) Nanocomposite-based lignocellulosic fibers 2: layer-by-layer modification of wood fibers for reinforcement in thermoplastic composites. Composites: Part A 42:84–91
Zurück zum Zitat Lin Z, Renneckar S, Hindman DP (2008) Nanocomposite-based lignocellulosic fibers 1. Thermal stability of modified fibers with clay-polyelectrolyte multilayers. Cellulose 15:333–346 (Dordrecht, Neth)CrossRef Lin Z, Renneckar S, Hindman DP (2008) Nanocomposite-based lignocellulosic fibers 1. Thermal stability of modified fibers with clay-polyelectrolyte multilayers. Cellulose 15:333–346 (Dordrecht, Neth)CrossRef
Zurück zum Zitat Lindstrom T, Wagberg L (1983) Effects of pH and electrolyte concentration on the adsorption of cationic polyacrylamides on cellulose. Tappi J 66:83–85 Lindstrom T, Wagberg L (1983) Effects of pH and electrolyte concentration on the adsorption of cationic polyacrylamides on cellulose. Tappi J 66:83–85
Zurück zum Zitat Lingstrom R, Wagberg L, Larsson Per T (2006) Formation of polyelectrolyte multilayers on fibres: influence on wettability and fibre/fibre interaction. J Colloid Interface Sci 296:396–408CrossRef Lingstrom R, Wagberg L, Larsson Per T (2006) Formation of polyelectrolyte multilayers on fibres: influence on wettability and fibre/fibre interaction. J Colloid Interface Sci 296:396–408CrossRef
Zurück zum Zitat Lu Z, Eadula S, Zheng Z, Xu K, Grozdits G, Lvov Y (2007) Layer-by-layer nanoparticle coatings on lignocellulose wood microfibers. Colloids Surf A 292:56–62CrossRef Lu Z, Eadula S, Zheng Z, Xu K, Grozdits G, Lvov Y (2007) Layer-by-layer nanoparticle coatings on lignocellulose wood microfibers. Colloids Surf A 292:56–62CrossRef
Zurück zum Zitat Lvov Y, Decher G, Sukhorukov G (1993) Assembly of thin films by means of successive deposition of alternate layers of DNA and poly(allylamine). Macromolecules 26:5396–5399CrossRef Lvov Y, Decher G, Sukhorukov G (1993) Assembly of thin films by means of successive deposition of alternate layers of DNA and poly(allylamine). Macromolecules 26:5396–5399CrossRef
Zurück zum Zitat Lvov Y, Ariga K, Ichinose I, Kunitake T (1996) Formation of ultrathin multilayer and hydrated gel from montmorillonite and linear polycations. Langmuir 12:3038–3044CrossRef Lvov Y, Ariga K, Ichinose I, Kunitake T (1996) Formation of ultrathin multilayer and hydrated gel from montmorillonite and linear polycations. Langmuir 12:3038–3044CrossRef
Zurück zum Zitat Lvov Y, Ariga K, Onda M, Ichinose I, Kunitake T (1997) Alternate assembly of ordered multilayers of SiO2 and other nanoparticles and polyions. Langmuir 13:6195–6203CrossRef Lvov Y, Ariga K, Onda M, Ichinose I, Kunitake T (1997) Alternate assembly of ordered multilayers of SiO2 and other nanoparticles and polyions. Langmuir 13:6195–6203CrossRef
Zurück zum Zitat Ma JC, Dougherty DA (1997) The Cation-pi Interaction. Chem Rev 97:1303–1324 (Washington, DC)CrossRef Ma JC, Dougherty DA (1997) The Cation-pi Interaction. Chem Rev 97:1303–1324 (Washington, DC)CrossRef
Zurück zum Zitat Marcelo G, Tarazona MP, Saiz E (2005) Solution properties of poly(diallyldimethylammonium chloride) (PDDA). Polymer 46:2584–2594CrossRef Marcelo G, Tarazona MP, Saiz E (2005) Solution properties of poly(diallyldimethylammonium chloride) (PDDA). Polymer 46:2584–2594CrossRef
Zurück zum Zitat Messersmith PB, Giannelis EP (1994) Synthesis and characterization of layered silicate-epoxy nanocomposites. Chem Mater 6:1719–1725CrossRef Messersmith PB, Giannelis EP (1994) Synthesis and characterization of layered silicate-epoxy nanocomposites. Chem Mater 6:1719–1725CrossRef
Zurück zum Zitat Michalowicz G, Toussaint B, Vignon MR (1991) Ultrastructural changes in poplar cell wall during steam explosion treatment. Holzforschung 45:175–179CrossRef Michalowicz G, Toussaint B, Vignon MR (1991) Ultrastructural changes in poplar cell wall during steam explosion treatment. Holzforschung 45:175–179CrossRef
Zurück zum Zitat Norgren M, Lindstrom B (2000) Dissociation of phenolic groups in kraft lignin at elevated temperatures. Holzforschung 54:519–527CrossRef Norgren M, Lindstrom B (2000) Dissociation of phenolic groups in kraft lignin at elevated temperatures. Holzforschung 54:519–527CrossRef
Zurück zum Zitat Notley SM, Norgren M (2008) Adsorption of a strong polyelectrolyte to model lignin surfaces. Biomacromolecules 9:2081–2086CrossRef Notley SM, Norgren M (2008) Adsorption of a strong polyelectrolyte to model lignin surfaces. Biomacromolecules 9:2081–2086CrossRef
Zurück zum Zitat Odberg L, Tanaka H, Swerin A (1993) Kinetic aspects of the adsorption of polymers on cellulosic fibers. Nord Pulp Pap Res J 8:6–9, 47 Odberg L, Tanaka H, Swerin A (1993) Kinetic aspects of the adsorption of polymers on cellulosic fibers. Nord Pulp Pap Res J 8:6–9, 47
Zurück zum Zitat Okada A, Kawasumi M, Kurauchi T, Kamigaito O (1987) Synthesis and characterization of a nylon 6-clay hybrid. Polym Prepr (Am Chem Soc, Div Polym Chem) 28:447–448 Okada A, Kawasumi M, Kurauchi T, Kamigaito O (1987) Synthesis and characterization of a nylon 6-clay hybrid. Polym Prepr (Am Chem Soc, Div Polym Chem) 28:447–448
Zurück zum Zitat Okada A, Kawasumi M, Usuki A, Kojima Y, Kurauchi T, Kamigaito O (1990) Nylon 6-clay hybrid. Mater Res Soc Symp Proc 171:45–50CrossRef Okada A, Kawasumi M, Usuki A, Kojima Y, Kurauchi T, Kamigaito O (1990) Nylon 6-clay hybrid. Mater Res Soc Symp Proc 171:45–50CrossRef
Zurück zum Zitat Onoda M, Yoshino K (1995) Fabrication of self-assembled multilayer heterostructure of poly(p-phenylene vinylene) and its use for an electroluminescent diode. J Appl Phys 78:4456–4462CrossRef Onoda M, Yoshino K (1995) Fabrication of self-assembled multilayer heterostructure of poly(p-phenylene vinylene) and its use for an electroluminescent diode. J Appl Phys 78:4456–4462CrossRef
Zurück zum Zitat Overend RP, Chornet E (1987) Fractionation of lignocellulosics by steam-aqueous pretreatments. Philos Trans R Soc London A 321:523–536CrossRef Overend RP, Chornet E (1987) Fractionation of lignocellulosics by steam-aqueous pretreatments. Philos Trans R Soc London A 321:523–536CrossRef
Zurück zum Zitat Peng CQ, Thio YS, Gerhardt RA (2008) Conductive paper fabricated by layer-by-layer assembly of polyelectrolytes and ITO nanoparticles. Nanotechnology 19: 505603/505601-505603/505610 Peng CQ, Thio YS, Gerhardt RA (2008) Conductive paper fabricated by layer-by-layer assembly of polyelectrolytes and ITO nanoparticles. Nanotechnology 19: 505603/505601-505603/505610
Zurück zum Zitat Pillai KV, Renneckar S (2009) Cation-pi Interactions as a mechanism in technical lignin adsorption to cationic surfaces. Biomacromolecules 10:798–804CrossRef Pillai KV, Renneckar S (2009) Cation-pi Interactions as a mechanism in technical lignin adsorption to cationic surfaces. Biomacromolecules 10:798–804CrossRef
Zurück zum Zitat Renneckar S, Zhou Y (2009) Nanoscale coatings on wood: polyelectrolyte adsorption and layer-by-layer assembled film formation. ACS Appl Mater Interfaces 1:559–566CrossRef Renneckar S, Zhou Y (2009) Nanoscale coatings on wood: polyelectrolyte adsorption and layer-by-layer assembled film formation. ACS Appl Mater Interfaces 1:559–566CrossRef
Zurück zum Zitat Rojas OJ, Ernstsson M, Neuman RD, Claesson PM (2002) Effect of polyelectrolyte charge density on the adsorption and desorption behavior on mica. Langmuir 18:1604–1612CrossRef Rojas OJ, Ernstsson M, Neuman RD, Claesson PM (2002) Effect of polyelectrolyte charge density on the adsorption and desorption behavior on mica. Langmuir 18:1604–1612CrossRef
Zurück zum Zitat Sarkanen KV (1962) Chemistry of delignification in pulp bleaching. Pure Appl Chem 5:219–231CrossRef Sarkanen KV (1962) Chemistry of delignification in pulp bleaching. Pure Appl Chem 5:219–231CrossRef
Zurück zum Zitat Schmitt J, Gruenewald T, Decher G, Pershan PS, Kjaer K, Loesche M (1993) Internal structure of layer-by-layer adsorbed polyelectrolyte films: a neutron and x-ray reflectivity study. Macromolecules 26:7058–7063CrossRef Schmitt J, Gruenewald T, Decher G, Pershan PS, Kjaer K, Loesche M (1993) Internal structure of layer-by-layer adsorbed polyelectrolyte films: a neutron and x-ray reflectivity study. Macromolecules 26:7058–7063CrossRef
Zurück zum Zitat Strazdins E (1995) Critical issues in applying electrokinetics to papermaking. Tappi J 78:115–119 Strazdins E (1995) Critical issues in applying electrokinetics to papermaking. Tappi J 78:115–119
Zurück zum Zitat Tammelin T, Saarinen T, Oesterberg M, Laine J (2006) Preparation of Langmuir/Blodgett-cellulose surfaces by using horizontal dipping procedure. Application for Polyelectrolyte Adsorption Studies Performed with QCM-D. Cellulose 13:519–535 (Dordrecht, Neth)CrossRef Tammelin T, Saarinen T, Oesterberg M, Laine J (2006) Preparation of Langmuir/Blodgett-cellulose surfaces by using horizontal dipping procedure. Application for Polyelectrolyte Adsorption Studies Performed with QCM-D. Cellulose 13:519–535 (Dordrecht, Neth)CrossRef
Zurück zum Zitat Tanaka H, Tachiki K, Sumimoto M (1979) Adsorption of cationic polymers onto bleached kraft pulp. Tappi 62:41–44 Tanaka H, Tachiki K, Sumimoto M (1979) Adsorption of cationic polymers onto bleached kraft pulp. Tappi 62:41–44
Zurück zum Zitat van de Steeg HGM, Cohen Stuart MA, De Keizer A, Bijsterbosch BH (1992) Polyelectrolyte adsorption: a subtle balance of forces. Langmuir 8:2538–2546CrossRef van de Steeg HGM, Cohen Stuart MA, De Keizer A, Bijsterbosch BH (1992) Polyelectrolyte adsorption: a subtle balance of forces. Langmuir 8:2538–2546CrossRef
Zurück zum Zitat van Duffel B, Verbiest T, van Elshocht S, Persoons A, de Schryver FC, Schoonheydt RA (2001) Fuzzy assembly and second harmonic generation of clay/polymer/dye monolayer films. Langmuir 17:1243–1249CrossRef van Duffel B, Verbiest T, van Elshocht S, Persoons A, de Schryver FC, Schoonheydt RA (2001) Fuzzy assembly and second harmonic generation of clay/polymer/dye monolayer films. Langmuir 17:1243–1249CrossRef
Zurück zum Zitat Wagberg L (2000) Polyelectrolyte adsorption onto cellulose fibers–a review. Nord Pulp Pap Res J 15:586–597CrossRef Wagberg L (2000) Polyelectrolyte adsorption onto cellulose fibers–a review. Nord Pulp Pap Res J 15:586–597CrossRef
Zurück zum Zitat Wagberg L, Odberg L (1989) Polymer adsorption on cellulosic fibers. Nord Pulp Pap Res J 4:135–140CrossRef Wagberg L, Odberg L (1989) Polymer adsorption on cellulosic fibers. Nord Pulp Pap Res J 4:135–140CrossRef
Zurück zum Zitat Wagberg L, Forsberg S, Johansson A, Juntti P (2002) Engineering of fibre surface properties by application of the polyelectrolyte multilayer concept. Part I. Modification of paper strength. J Pulp Pap Sci 28:222–228 Wagberg L, Forsberg S, Johansson A, Juntti P (2002) Engineering of fibre surface properties by application of the polyelectrolyte multilayer concept. Part I. Modification of paper strength. J Pulp Pap Sci 28:222–228
Zurück zum Zitat Wang L, Hu N (2001) Direct electrochemistry of hemoglobin in layer-by-layer films with poly(vinyl sulfonate) grown on pyrolytic graphite electrodes. Bioelectrochemistry 53:205–212CrossRef Wang L, Hu N (2001) Direct electrochemistry of hemoglobin in layer-by-layer films with poly(vinyl sulfonate) grown on pyrolytic graphite electrodes. Bioelectrochemistry 53:205–212CrossRef
Zurück zum Zitat Wise LE, Murphy M, D’Addieco AA (1946) Chlorite holocellulose, its fractionation and bearing on summative wood analysis and on studies on the hemicelluloses. Pap Trade J 122:35–43 Wise LE, Murphy M, D’Addieco AA (1946) Chlorite holocellulose, its fractionation and bearing on summative wood analysis and on studies on the hemicelluloses. Pap Trade J 122:35–43
Zurück zum Zitat Wong KKY, Deverell KF, Mackie KL, Clark TA, Donaldson LA (1988) The relationship between fiber porosity and cellulose digestibility in steam-exploded Pinus radiata. Biotechnol Bioeng 31:447–456CrossRef Wong KKY, Deverell KF, Mackie KL, Clark TA, Donaldson LA (1988) The relationship between fiber porosity and cellulose digestibility in steam-exploded Pinus radiata. Biotechnol Bioeng 31:447–456CrossRef
Zurück zum Zitat Yoon HC, Kim H-S (2000) Multilayered assembly of dendrimers with enzymes on gold: thickness-controlled biosensing interface. Anal Chem 72:922–926CrossRef Yoon HC, Kim H-S (2000) Multilayered assembly of dendrimers with enzymes on gold: thickness-controlled biosensing interface. Anal Chem 72:922–926CrossRef
Zurück zum Zitat Zhou Y, Renneckar S, Pillai KV, Li Q, Lin Z, Church WT (2010) Layer-by-layer nanoscale bondlines for macroscale adhesion. BioResources 5:1530–1541 Zhou Y, Renneckar S, Pillai KV, Li Q, Lin Z, Church WT (2010) Layer-by-layer nanoscale bondlines for macroscale adhesion. BioResources 5:1530–1541
Metadaten
Titel
Nanocomposite-based lignocellulosic fibers 3: polyelectrolyte adsorption onto heterogeneous fiber surfaces
verfasst von
Zhiyuan Lin
Scott Renneckar
Publikationsdatum
01.06.2011
Verlag
Springer Netherlands
Erschienen in
Cellulose / Ausgabe 3/2011
Print ISSN: 0969-0239
Elektronische ISSN: 1572-882X
DOI
https://doi.org/10.1007/s10570-011-9502-6

Weitere Artikel der Ausgabe 3/2011

Cellulose 3/2011 Zur Ausgabe