Abstract
Disordered alloy and bi-phase PtSn nanoparticles of nominal Pt:Sn ratio of 70:30 atomic % with controlled size and narrow size distribution were synthesized using a single-step polyol method. By adjusting the solution pH it was possible to obtain Pt7Sn3 nanoparticles of various sizes from 2.8 to 6.5 nm. We found that the presence of NaOH in the synthesis solution not only influenced the nanoparticle size, but as it was revealed by XRD, it apparently also dictated the degree of Pt and Sn alloying. Three catalysts prepared at lower NaOH concentrations (CNaOH < 0.15 M) showed disordered alloy structure of the nominal composition, while the other three catalysts synthesized at higher NaOH concentrations (CNaOH > 0.15 M) consisted of bi-phase nanoparticles comprising a crystalline phase close to that of pure Pt together with an amorphous Sn phase. These observations are plausibly due to the phase separation and formation of monometallic Pt and amorphous SnOx phases. A proposed reaction mechanism of Pt7Sn3 nanoparticle formation is presented to explain these observations along with the catalytic activities measured for the six synthesized carbon-supported Pt7Sn3 catalysts. The highest catalytic activity towards ethanol electro-oxidation was found for the carbon-supported bi-phase catalyst that formed the largest Pt (6.5 nm) nanoparticles and SnOx phase. The second best catalyst was a disordered alloy Pt7Sn3 catalyst with the second largest nanoparticle size (5 nm), while catalysts of smaller size (4.5–4.6 nm) but different structure (disordered alloy vs. bi-phase) showed similar catalytic performance inferior to that of the 5 nm disordered alloy Pt7Sn3 catalyst. This work demonstrated the importance of producing bi-metallic PtSn catalysts with large Pt surfaces in order to efficiently electro-oxidize ethanol.
Similar content being viewed by others
References
Song S, Tsiakaras P (2006) Appl Catal B: Environ 63:187
Tsiakaras P (2007) J Power Sour 171:102
Lamy C, Rousseau S, Belgsir EM, Coutanceau C, Leger J-M (2004) Electrochim Acta 49:3901
Jiang L, Sun G, Sun S, Liu J, Tang S, Li H, Zhou B, Xin Q (2005) Electrochim Acta 50:5384
Léger J-M, Rousseau S, Coutanceau C, Hahn F, Lamy C (2005) Electrochim Acta 50:5118
Zhou WJ, Song SQ, Li WZ, Zhou ZH, Sun GQ, Xin Q, Douvartzides S, Tsiakaras P (2005) J Power Sour 140:50
Jiang L, Colmenares L, Jusys Z, Sun GQ, Behm RJ (2007) Electrochim Acta 53:377
Bommersbach P, Chaker M, Mohamedi M, Guay D (2008) J Phys Chem C 112:14672
Garcia-Rodríguez S, Somodi F, Borbáth I, Margitfalvi JL, Pena MA, Fierro JLG, Rojas S (2009) Appl Catal B 91:83
Siné G, Foti G, Comninellis Ch (2006) J Electroanal Chem 595:115
Jiang L, Sun G, Zhou Z, Sun S, Wang Q, Yan S, Li H, Tian J, Guo J, Zhou B, Xin Q (2005) J Phys Chem B 109:8774
Zhu M, Sun G, Xin Q (2009) Electrochim Acta 54:1511
Zhou WJ, Song SQ, Li WZ, Sun GQ, Xin Q, Kontou S, Poulianitis K, Tsiakaras P (2004) Solid State Ion 175:797
Gupta SS, Singh S, Datta J (2009) Mater Chem Phys 116:223
Guo Y, Zheng Y, Huang M (2008) Electrochim Acta 53:3102
Alcala R, Shabaker JW, Huber GW, Sanchez-Castillo MA, Dumesic JA (2005) J Phys Chem B 109:2074
Li H, Sun G, Cao L, Jiang L, Xin Q (2007) Electrochim Acta 52:6622
Camara GC, de Lima RB, Iwasita T (2004) Electrochem Commun 6:812
Fujiwara N, Friedrich KA, Stimming U (1999) J Electroanal Chem 472:120
Ribeiro J, dos Anjos DM, Kokoh KB, Coutanceau C, Léger J-M, Olivi P, de Andrade AR, Tremiliosi-Filho G (2007) Electrochim Acta 52:6997
Debye P (1915) Ann Phys 46:809
Baranova EA, Le Page Y, Ilin D, Bock C, MacDougall B, Mercier PHJ (2009) J Alloys Compd 471:387
Harris IR, Norman M, Bryant AW (1968) J Less-Common Met 16:427
Le Page Y, Rodgers JR (2005) J Appl Crystallogr 38:697
Weissmann S (1981) Metal and alloys, data book vol 1. Center for diffraction data JCPDS, Pennsylvania
Baranova EA, Miles N, Mercier PHJ, Le Page Y, Patarachao B (2010) Electrochim Acta (in press). doi:10.1016/j.electacta.2009.12.090
Shukla AK, Arico AS, El-Khatib KM, Kim H, Antonucci PL, Antonucci V (1999) Appl Surf Sci 137:20
Hall SC, Subramanian V, Teeter G, Rambabu B (2004) Solid State Ion 175:809
Aricò AS, Antonucci V, Giordano N, Shukla AK, Ravikumar MK, Roy A, Barman SR, Sarma DD (1994) J Power Sour 50:295
Wagner CD, Riggs WM, Davis LE, Moulder JF, Muilenberg GE (1979) Handbook of X-ray photoelectron spectroscopy. Perkin-Elmer Corp, Eden Prairie
Eberhardt W, Fayet P, Cox DM, Fu Z, Kaldor A, Sherwood R, Sondericker D (1990) Phys Rev Lett 64:780
Baranova EA, Bock C, Ilin D, Wang D, MacDougall B, Wu X (2006) Surf Sci 600:3502
Bock C, Paquet C, Couillard M, Botton GA, MacDougall BR (2004) J Am Chem Soc 126:8028
Sheppard SA, Campbell SA, Smith JR, Lloyd GW, Ralph TR, Walsh FC (1998) Analyst 123:1923
Vigier F, Coutanceau C, Hahn F, Belgsir EM, Lamy C (2004) J Electroanal Chem 563:81
Park S, Wasileski SA, Weaver MJ (2001) J Phys Chem B 105:9719
Chang S-C, Weaver MJ (1991) J Phys Chem 95:5391
Nashner MS, Frenkel AI, Adler DL, Shapley JR, Nuzzo RG (1998) J Am Chem Soc 120:8093
Acknowledgments
Authors would like to thank Mr. Sander Mommers and Dr. Yun Liu from the Centre for Catalysis Research and Innovation (CCRI) for XPS and EDS/TEM measurements, respectively. This work was supported by Research Development Program at the University of Ottawa.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Baranova, E.A., Amir, T., Mercier, P.H.J. et al. Single-step polyol synthesis of alloy Pt7Sn3 versus bi-phase Pt/SnOx nano-catalysts of controlled size for ethanol electro-oxidation. J Appl Electrochem 40, 1767–1777 (2010). https://doi.org/10.1007/s10800-010-0135-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10800-010-0135-5