Thermoelectric properties of Bi3+ substituted Co-based misfit-layered oxides
Erschienen in: Journal of Electroceramics | Ausgabe 1-4/2008
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Highly densified (Ca1−x
Bi
x
)3Co4O9 thermoelectric ceramics with a layered structure were prepared by a sol–gel method followed by spark plasma sintering (SPS). Thermoelectric (TE) properties of the complex oxide ceramics were measured from room temperature to 700 °C. The results show that Bi3+ substitution leads to an increase in both electrical conductivity and Seebeck coefficient simultaneously. Bi3+ doped samples also show a lower thermal conductivity than undoped samples. The dimensional figure of merit ZT value of (Ca0.95 Bi0.05)3Co4O9 samples is 0.25 at 700 °C.