Abstract
Surface and grain boundary wetting and penetration of pure Fe and a martensitic steel by Pb and Pb-Bi eutectic alloys were studied by the sessile drop and dispensed drop techniques at different temperatures (400–900∘C) and times (up to 30 h). By using two different atmospheres—high vacuum and a He-H2 gas—and different heat treatments, wetting was studied for both oxidized and deoxidized solid substrates.
Similar content being viewed by others
References
N. EUSTATHOPOULOS, M. NICHOLAS and B. DREVET, “Wettability at High Temperatures” (Pergamon, Oxford, 1999).
B. McGURRAN and M. NICHOLAS, Braz. Solder. 8 (1985) 43.
P. PROTSENKO, A. TERLAIN, M. JEYMOND and N. EUSTATHOPOULOS, J. Nucl. Mater. 307–311P2 (2003) 1396.
S. I. POPEL, T. V. ZAKHAROVA and V. V. PAVLOV, “Adgesiya Rasplavov” (Naukova Dumka, Kiev, 1974) p. 53.
O. GOMEZ-MORENO, L. COUDURIER and N. EUSTATHOPOULOS, Acta Metall 30 (1982) 831.
A. HASOUNA, K. NOGI and K. OGINO, Mater. Trans., JIM 31 (1990) 302.
J. WEEKS and A. ROMANO, Corrosion–NACE 25 (1969) 131.
W. W. MULLINS, Trans. Metallurg. Soc. AIME 218 (1960) 354.
P. PROTSENKO, Y. KUCHERINENKO, F. ROBAUT, V. TRASKINE and N. EUSTATHOPOULOS, Defects and Diffusion Forum 216/217 (2003) 225.
E. RABKIN, D. CHATAIN, J. BERNARDINI and J. MONCHOUX, Trans. JWRI 30 (2001) 1.
W. ROBERTSON, Trans. Metallurg. Soc. AIME 242 (1968) 2139.
D. STEVENSON and J. WULFF, Trans. Metallurg. Soc. AIME 221 (1961) 271.
F. BALBAUD-CELERIER and F. BARBIER, J. Nucl. Mater. 289 (2001) 227.
J. P. MONCHOUX and E. RABKIN, Acta Materialia 50 (2002) 3159.
P. PROTSENKO, Surface and Grain Boundary Wetting of Solid Metals by Fusible Metallic Melts, Ph.D. Thesis, Moscow State University, 2002.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Protsenko, P., Eustathopoulos, N. Surface and grain boundary wetting of Fe based solids by molten Pb and Pb-Bi eutectic. J Mater Sci 40, 2383–2387 (2005). https://doi.org/10.1007/s10853-005-1963-2
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-1963-2