In situ preparation of self-bonded zeolite MCM-22 bodies by vapor-phase transport method
Erschienen in: Journal of Materials Science | Ausgabe 12/2009
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Self-bonded bodies of zeolite MCM-22 were prepared by vapor-phase transport method. The resultant materials were characterized by means of X-ray diffraction, scanning electron microscope, mercury porosimetry, and nitrogen porosimetry. Self-bonded MCM-22 bodies were in situ prepared at pH 10.0 with the molar composition of 0.05Na2O:SiO2:0.033Al2O3. It was found that the bodies, prepared by aluminosilicate gel, had been transformed into zeolite MCM-22. The MCM-22 bodies of which the mechanical resistance was 126 N/cm avoided binder accession. By adding auxiliary chemical–PEG20000 to the aluminosilicate gel, the pore size distributions of MCM-22 bodies could be adjusted. The average pore radius of MCM-22 bodies reached in the 149.41–653.64 nm range when AC/SiO2 ratio was 1.5 × 10−4–9.0 × 10−4.