BaTiO3 and SrBiO2.5 two phase system NTC thermistors
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 3/2008
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
BaTiO3-based materials doped with SrBiO2.5 only show negative temperature coefficient effect over a wide temperature range. X-ray diffraction analysis displays that major phases present in the sintered bodies were the Ba0.5Sr0.5TiO3 compounds with a cubic structure and the BaBiO3 compounds with a monoclinic structure. The mean grain size of samples remains unchanged with an increase from 20 to 50 in SrBiO2.5 content. The values of ρ
25
and B
25/125
constants of thermistors decreased with an increase in SrBiO2.5 content. The resistivity measured at other temperatures showed basically the same behavior as that at room temperature, irrespective of the measuring temperature.