The hydroxyl concentration and the dielectric properties of barium titanate nano-powder synthesized by water-based ambient condition sol process

verfasst von: Hiroki Maie, Burtrand I. Lee

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 7/2009

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Nanocrystalline barium titanate, BaTiO₃, powders have been successfully synthesized via water-based ambient condition sol (WACS) process, using barium hydroxide and titanium isopropoxide. The properties of the powder were investigated as a function of various processing parameters such as the concentration of Ba²⁺ ions ([Ba²⁺]), the concentration of base, and reaction time. The concentration of hydroxyl (OH⁻) groups in the BaTiO₃ powder was greatly affected by changing the values of each processing parameter. The dielectric constant and tetragonality of the powders which contain lattice OH⁻ more than 0.35 wt% were little affected with further increase in the lattice OH⁻ concentration. The dielectric loss was highly varied with the concentration of the OH⁻ groups, and it was increased with increasing OH⁻ concentration. Calcination treatment significantly improved the dielectric properties of the powder. With higher calcination temperature, the dielectric constant increased and the dielectric loss decreased.

Vorheriger Artikel Effects of oxygen to argon ratio on Ba(Zr0.2Ti0.8)O3 thin films prepared by RF magnetron sputtering

Nächster Artikel Ferromagnetism in Cu-doped ZnO nanoparticles at room temperature

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 340 Zeitschriften

aus folgenden Fachgebieten:

Bauwesen + Immobilien
Business IT + Informatik
Finance + Banking
Management + Führung
Marketing + Vertrieb
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

C. Pithan, D. Hennings, R. Waser, Int. J. Appl. Ceram. Technol. 2, 1–1 (2005)

Y. Rao, C.P. Wong, J. Appl. Polym. Sci. 92, 2228 (2004). doi:10.1002/app.13690 CrossRef

Y. Bai, Z.Y. Cheng, V. Bharti, H.S. Xu, Q.M. Zhang, Appl. Phys. Lett. 76, 3804 (2000). doi:10.1063/1.126787 CrossRefADS

S. Bhattacharya, R.R. Tummala, J. Electron Packag. 124, 1 (2002). doi:10.1115/1.1400751 CrossRef

N.G. Devaraju, E.S. Kim, B.I. Lee, Microelectro. Eng. 82, 71 (2005). doi:10.1016/j.mee.2005.06.003 CrossRef

L. Qi, B.I. Lee, W.D. Samuels, G.J. Exarhos, S.G. Parler Jr., J. Appl. Polym. Sci. 102, 967 (2006). doi:10.1002/app. 23739 CrossRef

P.K. Dutta, J.R. Gregg, Chem. Mater. 4, 843 (1992). doi:10.1021/cm00022a019 CrossRef

S. Wada, H. Chikamori, T. Noma, T. Suzuki, J. Mater. Sci. Lett. 19, 245 (2000). doi:10.1023/A:1006723111444 CrossRef

J. Moon, E. Suvaci, T. Li, S.A. Sostantino, J.H. Adair, J. Eur. Ceram. Soc. 22, 809 (2002). doi:10.1016/S0955-2219(01)00391-0 CrossRef

10.

R. Vivekanandan, T.R.N. Kutty, Power Technol. 57, 181 (1989). doi:10.1016/0032-5910(89)80074-9 CrossRef

11.

S. Lu, B.I. Lee, Z.L. Wang, W.D. Samuels, J. Cryst. Growth 219, 269 (2000). doi:10.1016/S0022-0248(00)00619-9 CrossRef

12.

H. Xu, L. Gao, J. Guo, J. Eur. Ceram. Soc. 22, 1163 (2002). doi:10.1016/S0955-2219(01)00425-3 CrossRef

13.

H. Xu, L. Gao, J. Am. Ceram. Soc. 86(1), 203 (2002)

14.

D.F.K. Hennings, C. Metzmacher, B.S. Schreinemacher, J. Am. Ceram. Soc. 84, 1–179 (2001)CrossRef

15.

T. Noma, S. Wada, M. Yano, T. Suzuki, J. Appl. Phys. 80, 5223 (1996). doi:10.1063/1.363508 CrossRefADS

16.

D. Hennings, S. Schreinemacher, J. Eur. Ceram. Soc. 9, 41 (1992). doi:10.1016/0955-2219(92)90075-O CrossRef

17.

I.J. Clark, T. Takeuchi, N. Ohtori, D. Sinclair, J. Mater. Chem. 9, 83 (1999). doi:10.1039/a805756g CrossRef

18.

X. Wang, B.I. Lee, M.Z. Hu, E.A. Payzant, D.A. Blom, J. Mater. Sci. Lett. 22, 557 (2003). doi:10.1023/A:1022907024179 CrossRef

19.

X. Wang, B.I. Lee, M.Z. Hu, E.A. Payzant, D.A. Blom, J. Mater. Sci. Mater. Electron. 14, 495 (2003). doi:10.1023/A:1023920902217 CrossRef

20.

X. Wang, B.I. Lee, M. Hu, E.A. Payzant, D.A. Blom, J. Eur. Ceram. Soc. 26, 2319 (2006). doi:10.1016/j.jeurceramsoc.2005.04.002 CrossRef

21.

N.G. Devaraju, B.I. Lee, M. Viviani, P. Nanni, E.S. Kim, J. Mater. Sci. 41, 3335 (2006). doi:10.1007/s10853-005-5390-1 CrossRefADS

22.

B.I. Lee, X. Wang, S.J. Kwon, H. Maie, R. Kota, J.H. Hwang et al., Microelectron. Eng. 83, 463 (2006). doi:10.1016/j.mee.2005.10.058 CrossRef

23.

A. Testino, M.T. Buscaglia, M. Viviani, V. Buscaglia, P. Nanni, J. Am. Ceram. Soc. 87, 1–79 (2004)

24.

A. Testino, V. Buscaglia, M.T. Buscaglia, M. Viviani, P. Nanni, Chem. Mater. 17, 5346 (2005). doi:10.1021/cm051119f CrossRef

25.

M. Viviani, M.T. Buscaglia, A. Testino, V. Buscaglia, P. Bowen, P. Nanni, J. Eur. Ceram. Soc. 23, 1383 (2003). doi:10.1016/S0955-2219(02)00357-6 CrossRef

26.

D.R. Brezinski, An Infrared Spectroscopy Atlas for the Coatings Industry, 4th ed., vol. 1 (Blue Bell, 1991)

27.

S.W. Lu, B.I. Lee, Z.L. Wang, W.D. Samuels, J. Cryst. Growth 219, 269 (2000). doi:10.1016/S0022-0248(00)00619-9 CrossRef

28.

S.W. Lu, B.I. Lee, L.A. Mann, Mater. Lett. 43, 102 (2000). doi:10.1016/S0167-577X(99)00253-0 CrossRef

29.

B.I. Lee, J. Electroceram. 3(1), 53 (1999). doi:10.1023/A:1009966900092 CrossRef

30.

S.K. Patil, N. Shah, F.D. Blum, M.N. Rahaman, J. Mater. Res. 20, 3312 (2005). doi:10.1557/jmr.2005.0406 CrossRefADS

31.

T. Noma, S. Wada, M. Yano, T. Suzuki, J. Appl. Phys. 80(9), 5223 (1996)

32.

S. Wada, T. Suzuki, T. Noma, J. Ceram. Soc. Jpn. 103, 1220 (1995)

33.

S. Wada, H. Yasuno, T. Hoshina, H. Song-Min Nam, H. Kakemoto, T. Tsurumi, Jpn. J. Appl. Phys. 42, 6188 (2003). doi:10.1143/JJAP.42.6188

34.

S. Wada, M. Narahara, T. Hoshina, H. Kakemoto, T. Tsurumi, J. Mater. Sci. 38, 2655 (2003)CrossRef

35.

G. Busca, V. Buscaglia, M. Leoni, P. Nanni, Chem. Mater. 6, 955 (1994). doi:10.1021/cm00043a016 CrossRef

36.

S.G. Kwon, B.H. Park, K. Choi, E.S. Choi, S. Nam, J.W. Kim et al., J. Eur. Ceram. Soc. 26, 1401 (2006). doi:10.1016/j.jeurceramsoc.2005.02.003 CrossRef

37.

S. Yoon, S. Baik, M.G. Kim, N. Shin, J. Am. Ceram. Soc. 89(6), 1816 (2006). doi:10.1111/j.1551-2916.2006.01056.x CrossRef

38.

E. Ciftci, M.N. Rahaman, M. Shumsky, J. Mater. Sci. 36, 4875 (2001)CrossRef

Titel: The hydroxyl concentration and the dielectric properties of barium titanate nano-powder synthesized by water-based ambient condition sol process
verfasst von: Hiroki Maie
Burtrand I. Lee
Publikationsdatum: 01.07.2009
Verlag: Springer US
Erschienen in: Journal of Materials Science: Materials in Electronics / Ausgabe 7/2009
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI: https://doi.org/10.1007/s10854-008-9775-1

Neuer Inhalt

Bildnachweise

VDI-Icon, Profil Icon, inhalt2, Springer Professional Modul/© Springer Fachmedien Wiesbaden GmbH, Nachhaltigkeitsaward Key Visual/© Cometis AG/Global ESG Monitor | Daniel Rupp | Generiert mit KI, Search Icon, Banner Hanser, Frank Urbansky/© Peter Eichler / Leipzig, CO2-Fußabdruck/© Jenny Sturm / stock.adobe.com, Interview Entropie Bild 1/© Bernhard Weßling, Zeitschrift Wissensmanagement Cover, PatentFit-Logo/© Springer Fachmedien Wiesbaden GmbH, Sustainibility Finance/© Robert Kneschke / stock.adobe.com / Springer Fachmedien Wiesbaden GmbH, Zukunftswerkstatt Sales Excellence 2024/© AndreyPopov / Getty Images / iStock, 2023_Antrieb/© supervisuell

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Springer Professional "Wirtschaft"

Weitere Artikel der Ausgabe 7/2009

Ferromagnetism in Cu-doped ZnO nanoparticles at room temperature

Synthesis, thermal, photoluminescent, and electroluminescent properties of a novel quaternary Eu(III) complex containing a carbazole hole-transporting functional group

Rapid synthesis of stoichiometric lithium niobate powders with Li2SO4–Na2SO4 flux

Magnetic and dielectric properties of Ni0.8Zn0.2Fe2O4/HDPE composites for high-frequency application

The structural and optical properties of ZnO nanowire arrays prepared by hydrothermal synthesis method

Effects of oxygen to argon ratio on Ba(Zr0.2Ti0.8)O3 thin films prepared by RF magnetron sputtering

Neuer Inhalt

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.