Microstructure and electrical properties of (Na1.015−xKx)NbO3 lead-free piezoceramics

verfasst von: Guo-Zhong Zang, Xiu-Jie Yi, Juan Du, Zhi-Jun Xu, Rui-Qing Chu, Peng Fu, Wei Li

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 9/2011

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In order to obtain the morphotropic phase boundary (MPB) and good piezoelectric properties, lead-free (Na1.015−xKx)NbO3 (x = 0.32–0.35) piezoceramics were synthesized by conventional solid state sintering. The x-ray diffraction results show that the lattice parameters of the monoclinic primitive cell peak at x = 0.34. The scanning electron microscopy and energy dispersive spectroscopy reveal that the excess sodium may be an important reason for the abnormal growth of the grains larger than 20 μm. All the samples exhibit double-like hysteresis loops and it may also be attributed to the excess Na+. Although the salient microstructure was found in the studied range, the piezoelectric and ferroelectric properties changed slightly with increasing x from 0.32 to 0.35. The values of piezoelectric coefficient d 33 obtained in this study are as high as about 75 pC/N which is close to that of normally prepared (Na0.5K0.5)NbO3 ceramics with MPB structure.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
5.
Zurück zum Zitat Y. Saito, H. Takao, T. Tani, T. Nonoyama, K. Takatori, T. Homma, T. Nagaya, M. Nakamura, Nature 432, 84 (2004)CrossRef Y. Saito, H. Takao, T. Tani, T. Nonoyama, K. Takatori, T. Homma, T. Nagaya, M. Nakamura, Nature 432, 84 (2004)CrossRef
6.
7.
Zurück zum Zitat D. Lin, K.W. Kwok, K.H. Lam, H.L.W. Chan, J. Phys. D: Appl. Phys. 40, 3500 (2007)CrossRef D. Lin, K.W. Kwok, K.H. Lam, H.L.W. Chan, J. Phys. D: Appl. Phys. 40, 3500 (2007)CrossRef
8.
9.
Zurück zum Zitat G.Z. Zang, J.F. Wang, H.C. Chen, W.B. Su, C.M. Wang, P. Qi, B.Q. Ming, J. Du, L.M. Zheng, S. Zhang, T.R. Shrout, Appl. Phys. Lett. 88, 212908 (2006)CrossRef G.Z. Zang, J.F. Wang, H.C. Chen, W.B. Su, C.M. Wang, P. Qi, B.Q. Ming, J. Du, L.M. Zheng, S. Zhang, T.R. Shrout, Appl. Phys. Lett. 88, 212908 (2006)CrossRef
10.
11.
12.
Zurück zum Zitat H. Du, W. Zhou, F. Luo, D. Zhu, S. Qu, Y. Li, Z. Pei, J. Appl. Phys. 104, 034104 (2008)CrossRef H. Du, W. Zhou, F. Luo, D. Zhu, S. Qu, Y. Li, Z. Pei, J. Appl. Phys. 104, 034104 (2008)CrossRef
13.
Zurück zum Zitat J.L. Zhang, X.J. Zong, L. Wu, Y. Gao, P. Zheng, S.F. Shao, Appl. Phys. Lett. 95, 022909 (2009)CrossRef J.L. Zhang, X.J. Zong, L. Wu, Y. Gao, P. Zheng, S.F. Shao, Appl. Phys. Lett. 95, 022909 (2009)CrossRef
14.
15.
16.
17.
Zurück zum Zitat H.E. Mgbemere, R.P. Herber, G.A. Schneider, J. Eur. Ceram. Soc. 29, 3273 (2009)CrossRef H.E. Mgbemere, R.P. Herber, G.A. Schneider, J. Eur. Ceram. Soc. 29, 3273 (2009)CrossRef
18.
19.
Zurück zum Zitat P. Bomlai, P. Wichianrat, S. Muensit, S.J. Milne, J. Am. Ceram. Soc. 90, 1650 (2007)CrossRef P. Bomlai, P. Wichianrat, S. Muensit, S.J. Milne, J. Am. Ceram. Soc. 90, 1650 (2007)CrossRef
20.
21.
Zurück zum Zitat F. Rubio-Marcos, P. Ochoa, J.F. Fernandez, J. Eur. Ceram. Soc. 27, 4125 (2007)CrossRef F. Rubio-Marcos, P. Ochoa, J.F. Fernandez, J. Eur. Ceram. Soc. 27, 4125 (2007)CrossRef
22.
Zurück zum Zitat G.Z. Zang, X.J. Yi, Z.J. Xu, P. Fu, L.M. Zhao, X.P. Pu, Chin. Phys. Lett. 27, 017701 (2010)CrossRef G.Z. Zang, X.J. Yi, Z.J. Xu, P. Fu, L.M. Zhao, X.P. Pu, Chin. Phys. Lett. 27, 017701 (2010)CrossRef
23.
24.
Metadaten
Titel
Microstructure and electrical properties of (Na1.015−xKx)NbO3 lead-free piezoceramics
verfasst von
Guo-Zhong Zang
Xiu-Jie Yi
Juan Du
Zhi-Jun Xu
Rui-Qing Chu
Peng Fu
Wei Li
Publikationsdatum
01.09.2011
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 9/2011
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-011-0300-6

Weitere Artikel der Ausgabe 9/2011

Journal of Materials Science: Materials in Electronics 9/2011 Zur Ausgabe

Neuer Inhalt