The morphology and kinetic evolution of intermetallic compounds at Sn–Ag–Cu solder/Cu and Sn–Ag–Cu-0.5Al2O3 composite solder/Cu interface during soldering reaction

verfasst von: S. Y. Chang, L. C. Tsao, M. W. Wu, C. W. Chen

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 1/2012

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In this work, Sn3.0Ag0.7Cu (SAC) composite solders were produced by mechanically intermixing 0.5 wt% Al2O3 nanoparticles into Sn3.0Ag0.7Cu solder. The formation and growth kinetics of the intermetallic compounds (IMC) formed during the liquid–solid reactions between SAC-0.5Al2O3 composite solder and Cu substrates at various temperatures ranging from 250 to 325 °C were investigated, and the results were compared to the SAC/Cu system. Scanning electron microscopy (SEM) was used to quantify the interfacial microstructure for each processing condition. The thickness of interfacial intermetallic layers was quantitatively evaluated from SEM micrographs using imaging software. Experimental results showed that IMC could be dramatically affected by a small amount of intermixing 0.5 wt% Al2O3 nanoparticles into Sn3.0Ag0.7Cu solder. A continuous elongated scallop-shaped overall IMC layer was found at SAC/Cu interfaces. However, after the addition of Al2O3 nanoparticles, a discontinuous rounded scallop-shaped overall IMC layer appeared at SAC-0.5Al2O3/Cu interfaces. Kinetics analyses showed that growth of the overall IMC layer in SAC/Cu and SAC-0.5Al2O3/Cu soldering was diffusion controlled. The activation energies calculated for the overall IMC layer were 44.2 kJ/mol of SAC/Cu and 59.3 kJ/mol for SAC-0.5Al2O3/Cu soldering, respectively. This indicates that the presence of a small amount of Al2O3 nanoparticles is effective in suppressing the growth of the overall IMC layer.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat M. Abtew, G. Selvaduray, Mater. Sci. Eng. A27, 95–141 (2000) M. Abtew, G. Selvaduray, Mater. Sci. Eng. A27, 95–141 (2000)
2.
4.
Zurück zum Zitat J. Glazer, Inter. Mater. Rev. 40, 65–93 (1995) J. Glazer, Inter. Mater. Rev. 40, 65–93 (1995)
5.
6.
8.
Zurück zum Zitat L.C. Tsao, S.Y. Chang, C.I. Lee, W.H. Sun, C.H. Huang, Mater. Des. 31, 4831–4835 (2010)CrossRef L.C. Tsao, S.Y. Chang, C.I. Lee, W.H. Sun, C.H. Huang, Mater. Des. 31, 4831–4835 (2010)CrossRef
9.
Zurück zum Zitat J.H. Lee, J.H. Park, Y.S. Kim, D.H. Shin, J. Mater. Res. 16, 1227–1230 (2001)CrossRef J.H. Lee, J.H. Park, Y.S. Kim, D.H. Shin, J. Mater. Res. 16, 1227–1230 (2001)CrossRef
10.
11.
Zurück zum Zitat A. Zribi, A. Clark, L. Zavalij, P. Borgesen, E.J. Cotts, J. Elect. Mater. 30, 1157–1164 (2001)CrossRef A. Zribi, A. Clark, L. Zavalij, P. Borgesen, E.J. Cotts, J. Elect. Mater. 30, 1157–1164 (2001)CrossRef
12.
Zurück zum Zitat K.S. Kim, S.H. Huh, K. Suganuma, Microelectr. Rel. 43, 259–267 (2003)CrossRef K.S. Kim, S.H. Huh, K. Suganuma, Microelectr. Rel. 43, 259–267 (2003)CrossRef
13.
Zurück zum Zitat W. Yang, E.Felton. Lawrence, Robert.W. Messler Jr, J. Electron. Mater. 24, 1465–1472 (1995)CrossRef W. Yang, E.Felton. Lawrence, Robert.W. Messler Jr, J. Electron. Mater. 24, 1465–1472 (1995)CrossRef
14.
Zurück zum Zitat T.L. Su, L.C. Tsao, S.Y. Chang, T.H. Chuang, JMEPEG 11, 365–368 (2002)CrossRef T.L. Su, L.C. Tsao, S.Y. Chang, T.H. Chuang, JMEPEG 11, 365–368 (2002)CrossRef
15.
Zurück zum Zitat R.W. Wu, L.C. Tsao, S.Y. Chang, C.C. Jain, R.S. Chen, J.Mater Sci. Mater. Electron. 22, 1181–1187 (2011)CrossRef R.W. Wu, L.C. Tsao, S.Y. Chang, C.C. Jain, R.S. Chen, J.Mater Sci. Mater. Electron. 22, 1181–1187 (2011)CrossRef
16.
Zurück zum Zitat R.J.K. Wassink, (Electrochemical Publications Ltd., Ayr, Scotland, 1989), p. 149 R.J.K. Wassink, (Electrochemical Publications Ltd., Ayr, Scotland, 1989), p. 149
17.
Zurück zum Zitat T.H. Chuang, M.W. Wu, S.Y. Chang, S.F. Ping, L.C. Tsao, J.Mater. Sci. Mater. Electron. 22, 1021–1027 (2011)CrossRef T.H. Chuang, M.W. Wu, S.Y. Chang, S.F. Ping, L.C. Tsao, J.Mater. Sci. Mater. Electron. 22, 1021–1027 (2011)CrossRef
18.
Zurück zum Zitat J. Shen, Y.C. Liu, Y.J. Han, Y.M. Tian, H.X. Gao, J. Electron. Mater. 35, 1672–1679 (2006)CrossRef J. Shen, Y.C. Liu, Y.J. Han, Y.M. Tian, H.X. Gao, J. Electron. Mater. 35, 1672–1679 (2006)CrossRef
19.
Zurück zum Zitat M. Harada, R. Satoh, IEEE Trans. Comp. Hybrids. Manuf. Tech. 13, 736–742 (1990)CrossRef M. Harada, R. Satoh, IEEE Trans. Comp. Hybrids. Manuf. Tech. 13, 736–742 (1990)CrossRef
21.
22.
24.
Zurück zum Zitat H.L. John, L.H. Pang, X.Q. Xu et al., J Electron Mater 33, 1219–1226 (2004)CrossRef H.L. John, L.H. Pang, X.Q. Xu et al., J Electron Mater 33, 1219–1226 (2004)CrossRef
25.
Zurück zum Zitat H. Schoeller, S. Bansal, A. Knobloch, D. Shaddock, J. Cho, J Electron Mater 38, 802–809 (2009)CrossRef H. Schoeller, S. Bansal, A. Knobloch, D. Shaddock, J. Cho, J Electron Mater 38, 802–809 (2009)CrossRef
26.
Zurück zum Zitat G. Zeng, S. Xue, L. Zhang, L. Gao, W. Dai, J. Luo, J Mater Sci. Mater Electron. 21, 421–440 (2010)CrossRef G. Zeng, S. Xue, L. Zhang, L. Gao, W. Dai, J. Luo, J Mater Sci. Mater Electron. 21, 421–440 (2010)CrossRef
28.
Zurück zum Zitat K. Suganuma, K.S. Kim, S.H. Huh, in International symposium on microelectronics (IMAPS, Washington, DC, 2001), pp. 529–534 K. Suganuma, K.S. Kim, S.H. Huh, in International symposium on microelectronics (IMAPS, Washington, DC, 2001), pp. 529–534
32.
Zurück zum Zitat X.Y. Liu, M.L. Huang, C.M.L. Wu, L. Wang, J. Mater. Sci.: Mater. Electron. 21, 1046–1054 (2010)CrossRef X.Y. Liu, M.L. Huang, C.M.L. Wu, L. Wang, J. Mater. Sci.: Mater. Electron. 21, 1046–1054 (2010)CrossRef
33.
Zurück zum Zitat S.M.L. Nai, M. Gupta, J. Wei, in 2nd IEEE international nanoelectronics conference, (2008). pp. 15–19 S.M.L. Nai, M. Gupta, J. Wei, in 2nd IEEE international nanoelectronics conference, (2008). pp. 15–19
34.
Zurück zum Zitat S.M.L. Nai, J. Wei, M. Gupta, J. Alloys. Compd. 473, 100–106 (2009)CrossRef S.M.L. Nai, J. Wei, M. Gupta, J. Alloys. Compd. 473, 100–106 (2009)CrossRef
35.
Zurück zum Zitat A.K. Gain, T. Fouzder, Y.C. Chan, K. Winco, C. Yung, J. Alloys Compd. 509, 3319–3325 (2011)CrossRef A.K. Gain, T. Fouzder, Y.C. Chan, K. Winco, C. Yung, J. Alloys Compd. 509, 3319–3325 (2011)CrossRef
Metadaten
Titel
The morphology and kinetic evolution of intermetallic compounds at Sn–Ag–Cu solder/Cu and Sn–Ag–Cu-0.5Al2O3 composite solder/Cu interface during soldering reaction
verfasst von
S. Y. Chang
L. C. Tsao
M. W. Wu
C. W. Chen
Publikationsdatum
01.01.2012
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 1/2012
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-011-0476-9

Weitere Artikel der Ausgabe 1/2012

Journal of Materials Science: Materials in Electronics 1/2012 Zur Ausgabe

Neuer Inhalt