Effect of CaO-doped in NiMn2O4–LaMnO3 composite ceramics on microstructure and electrical properties

verfasst von: Fang Guan, Huimin Zhang, Aimin Chang, Pengjun Zhao, Bo Zhang

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 9/2012

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The composite ceramics (NiMn2O4)0.50(La1−x Ca x MnO3)0.50 (0 ≤ x ≤ 0.3) consisting of spinel-structured NiMn2O4 and perovskite-structured CaO-doped LaMnO3 were prepared by classical solid state reaction. The X-ray diffraction (XRD) patterns have shown that the major phases presented in the sintered samples are NiMn2O4 compounds with a spinel structure, La1−x Ca x MnO3 with a perovskite structure. The Scanning Electron Microscope (SEM) pictures have exhibited that the grain size of the composite ceramics decreases from ca. 6.5 to 2.0 μm as the mole fraction of CaO increases from 0 to 0.3. The ρ 25 °C and B 25/50 constants of the composite samples are in the range of 0.234–8.61 Ω cm and 2,600–2,962 K, respectively. In particular, CaO-doped leads to a decrease in the resistance drift of the (NiMn2O4)0.50(La1−x Ca x MnO3)0.50 composite NTC (negative temperature coefficient) ceramics after aging test. This indicates that the CaO-doped (NiMn2O4)0.50(La1−x Ca x MnO3)0.50 NTC ceramics display high electrical stability in comparison with the Ca-free (NiMn2O4)0.50(LaMnO3)0.50 ceramics. The X-ray photoelectron spectroscopy (XPS) analysis verifies that the valence states of the manganese ions have a highly mixed state of Mn2+, Mn3+ and Mn4+ at B site. And the electrical conduction of the composite ceramics can be elaborated by the ions migration mechanism.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
2.
Zurück zum Zitat M.M. Vakiv, O.I. Shpotyuk, V.O. Balitska, B. Butkiewicz, L.I. Shpotyuk, J. Eur. Ceram. Soc. 24, 1243 (2004)CrossRef M.M. Vakiv, O.I. Shpotyuk, V.O. Balitska, B. Butkiewicz, L.I. Shpotyuk, J. Eur. Ceram. Soc. 24, 1243 (2004)CrossRef
3.
Zurück zum Zitat T. Yokoyama, T. Meguro, Y. Shimada, J. Tatami, K. Komeya, Y. Abe, J. Mater. Sci. 42, 5860 (2007)CrossRef T. Yokoyama, T. Meguro, Y. Shimada, J. Tatami, K. Komeya, Y. Abe, J. Mater. Sci. 42, 5860 (2007)CrossRef
4.
Zurück zum Zitat T. Yokoyama, T. Meguro, Y. Shimada, J. Tatami, K. Komeya, Y. Abe, J. Mater. Sci. 42, 5860 (2007)CrossRef T. Yokoyama, T. Meguro, Y. Shimada, J. Tatami, K. Komeya, Y. Abe, J. Mater. Sci. 42, 5860 (2007)CrossRef
6.
Zurück zum Zitat Z.B. Wang, C.H. Zhao, C.S. Chen, A.J.A. Winnubst, J. Eur. Ceram. Soc. 26, 2833 (2006)CrossRef Z.B. Wang, C.H. Zhao, C.S. Chen, A.J.A. Winnubst, J. Eur. Ceram. Soc. 26, 2833 (2006)CrossRef
7.
Zurück zum Zitat K. Park, J.K. Lee, S.J. Kim, W.S. Seo, W.S. Cho, C.W. Lee, S. Nahm, J. Alloy Compd. 467, 310 (2009)CrossRef K. Park, J.K. Lee, S.J. Kim, W.S. Seo, W.S. Cho, C.W. Lee, S. Nahm, J. Alloy Compd. 467, 310 (2009)CrossRef
8.
Zurück zum Zitat C.H. Zhao, Z.B. Wang, S.M. Wang, P.H. Yang, C.S. Chen, J. Electroceram. 20, 113 (2008)CrossRef C.H. Zhao, Z.B. Wang, S.M. Wang, P.H. Yang, C.S. Chen, J. Electroceram. 20, 113 (2008)CrossRef
9.
Zurück zum Zitat W. Luo, H.M. Yao, P.H. Yang, C.S. Chen, J. Am. Ceram. Soc. 92, 2682 (2009)CrossRef W. Luo, H.M. Yao, P.H. Yang, C.S. Chen, J. Am. Ceram. Soc. 92, 2682 (2009)CrossRef
10.
Zurück zum Zitat M.L. Singla, S. Awasthi, A. Srivastava, D.V.S. Jain, Sens. Actuators A 136, 604 (2007)CrossRef M.L. Singla, S. Awasthi, A. Srivastava, D.V.S. Jain, Sens. Actuators A 136, 604 (2007)CrossRef
11.
Zurück zum Zitat I. Maurin, P. Barboux, Y. Lassailly, J.P. Boilot, J. Solid State Chem. 160, 123 (2001)CrossRef I. Maurin, P. Barboux, Y. Lassailly, J.P. Boilot, J. Solid State Chem. 160, 123 (2001)CrossRef
12.
Zurück zum Zitat Z. Branković, K. Ðuriš, A. Radojković, S. Bernik, Z. Jaglićić, M. Jagodić, K. Vojisavljevic, J. Sol–Gel Sci. Technol. 55, 311 (2010)CrossRef Z. Branković, K. Ðuriš, A. Radojković, S. Bernik, Z. Jaglićić, M. Jagodić, K. Vojisavljevic, J. Sol–Gel Sci. Technol. 55, 311 (2010)CrossRef
13.
Zurück zum Zitat S. Guillemet-Fritsch, J.L. Baudour, C. Chanel, F. Bouree, A. Rousset, Solid State Ion. 132, 63 (2000)CrossRef S. Guillemet-Fritsch, J.L. Baudour, C. Chanel, F. Bouree, A. Rousset, Solid State Ion. 132, 63 (2000)CrossRef
16.
Zurück zum Zitat P.N. Lisboa-Filho, M. Bahout, P. Barahona, C. Moure, O. Pena, J. Phys. Chem. Solids 66, 1206 (2005)CrossRef P.N. Lisboa-Filho, M. Bahout, P. Barahona, C. Moure, O. Pena, J. Phys. Chem. Solids 66, 1206 (2005)CrossRef
17.
Zurück zum Zitat Y. Boudeville, F. Fiqueras, M. Forissier, J.L. Portefaix, J.C. Vedrine, J. Catal. 58, 52 (1979)CrossRef Y. Boudeville, F. Fiqueras, M. Forissier, J.L. Portefaix, J.C. Vedrine, J. Catal. 58, 52 (1979)CrossRef
Metadaten
Titel
Effect of CaO-doped in NiMn2O4–LaMnO3 composite ceramics on microstructure and electrical properties
verfasst von
Fang Guan
Huimin Zhang
Aimin Chang
Pengjun Zhao
Bo Zhang
Publikationsdatum
01.09.2012
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 9/2012
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-012-0654-4

Weitere Artikel der Ausgabe 9/2012

Journal of Materials Science: Materials in Electronics 9/2012 Zur Ausgabe

Neuer Inhalt