Effect of crystalline phase on the dielectric and energy storage properties of poly(vinylidene fluoride)
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 7/2016
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The crystal structure shows great influence on dielectric and energy storage performance of poly(vinylidene fluoride) (PVDF) films. In this paper, a γ-phase PVDF film was fabricated by crystallization of PVDF from a DMF solution through a solution-casting method and a quenching treatment. The influences of crystalline phases on the dielectric and energy storage properties of the films were studied. It has been found that, compared with common α- and β-phase, the obtained γ-phase PVDF film presents much higher relative permittivity of about 9.8 in a 1 kHz electric field. The ferroelectric hysteresis loop investigation indicates that the γ-phase PVDF film exhibits much slimmer polarization–electric field hysteresis loops than α- and β-phase PVDF films and a high energy efficiency more than 72 % is obtained. This γ-phase PVDF film also shows low leakage current at high working voltage, which is more desirable and promising for high performance pulse discharge capacitor application.