In situ polymerization of modified graphene/polyimide composite with improved mechanical and thermal properties

verfasst von: Guanglei Wu, Yonghong Cheng, Zhengdong Wang, Kuikui Wang, Ailing Feng

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 1/2017

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The graphene oxide was modified by coupling agent (KH-550). The polyimide/graphene treated by KH-550 (PI/KG) composite were prepared by in situ polymerization from 4,4′-diaminodiphenyl ether (ODA), 2,2-bis(4- (3,4-dicarboxyphenoxy) phenyl) propane dianhydride (BPADA), and modified graphene. The structure and morphology of the composite membranes were analyzed by Fourier transform infrared spectroscopy (FT-IR) and X ray diffraction. Compared to pure PI system, the tensile strength and elongation at break of PI/KG-4 composite, increasing by 26.4 and 24.1 %, was 134 MPa and 9.8 %, respectively. The 5 % mass loss temperature of polyimide system was about 486.1 °C, and the PI/KG-6 composite was 493.8 °C. PI/KG composites have a better thermal stability and a higher thermal conductivity compared to PI system with the increasing of KG content.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
2.
Zurück zum Zitat G. Wu, Y. Cheng, Q. Xie, Z. Jia, F. Xiang, H. Wu, Mater. Lett. 144, 157 (2015)CrossRef G. Wu, Y. Cheng, Q. Xie, Z. Jia, F. Xiang, H. Wu, Mater. Lett. 144, 157 (2015)CrossRef
3.
Zurück zum Zitat F. Ren, G. Zhu, P. Ren, K. Wang, X. Cui, X. Yan, Appl. Surf. Sci. 351, 40 (2015)CrossRef F. Ren, G. Zhu, P. Ren, K. Wang, X. Cui, X. Yan, Appl. Surf. Sci. 351, 40 (2015)CrossRef
4.
Zurück zum Zitat X. Wang, B. Pang, Q. Zhu, J. Yu, H. Dong, L. Dong, J. Appl. Polym. Sci. 132(32), 42387 (2015) X. Wang, B. Pang, Q. Zhu, J. Yu, H. Dong, L. Dong, J. Appl. Polym. Sci. 132(32), 42387 (2015)
5.
Zurück zum Zitat X. Wang, L. Dong, B. Zhang, M. Yu, J. Liu, Nanotechnology 27, 125602 (2016)CrossRef X. Wang, L. Dong, B. Zhang, M. Yu, J. Liu, Nanotechnology 27, 125602 (2016)CrossRef
6.
Zurück zum Zitat H.J. Wu, G.L. Wu, Y.Y. Ren, L. Yang, J. Mater. Chem. C. 3, 7677 (2015)CrossRef H.J. Wu, G.L. Wu, Y.Y. Ren, L. Yang, J. Mater. Chem. C. 3, 7677 (2015)CrossRef
8.
Zurück zum Zitat H. Wu, G. Wu, Y. Ren, X. Li, L. Wang, Chem.-A Eur. J. 22, 8864 (2016)CrossRef H. Wu, G. Wu, Y. Ren, X. Li, L. Wang, Chem.-A Eur. J. 22, 8864 (2016)CrossRef
9.
Zurück zum Zitat X. Wang, M. Yu, W. Zhang, B. Zhang, L. Dong, Appl. Phys. A 118(3), 1053 (2014)CrossRef X. Wang, M. Yu, W. Zhang, B. Zhang, L. Dong, Appl. Phys. A 118(3), 1053 (2014)CrossRef
10.
12.
13.
Zurück zum Zitat G. Wang, X. Huang, P. Jiang, A.C.S. Appl, Mater. Interf. 7, 18017 (2015)CrossRef G. Wang, X. Huang, P. Jiang, A.C.S. Appl, Mater. Interf. 7, 18017 (2015)CrossRef
15.
Zurück zum Zitat F. Ren, G. Zhu, P. Ren, Y. Wang, X. Cui, Appl. Surf. Sci. 316, 549 (2014)CrossRef F. Ren, G. Zhu, P. Ren, Y. Wang, X. Cui, Appl. Surf. Sci. 316, 549 (2014)CrossRef
16.
17.
18.
19.
Zurück zum Zitat G.L. Wu, Y.H. Cheng, F. Xiang, Z.R. Jia, Mater. Sci. Semicon. Proc. 41, 6 (2016)CrossRef G.L. Wu, Y.H. Cheng, F. Xiang, Z.R. Jia, Mater. Sci. Semicon. Proc. 41, 6 (2016)CrossRef
20.
Zurück zum Zitat X. Huang, X. Wang, K. Yang, M. Zhu, P. Jiang, Y. Bando, Nanotechnology 26, 015705 (2015)CrossRef X. Huang, X. Wang, K. Yang, M. Zhu, P. Jiang, Y. Bando, Nanotechnology 26, 015705 (2015)CrossRef
22.
Zurück zum Zitat G. Wu, K.C. Kou, L.H. Zhuo, Y.Q. Wang, J.Q. Zhang, Thermochim. Acta 559, 86 (2013)CrossRef G. Wu, K.C. Kou, L.H. Zhuo, Y.Q. Wang, J.Q. Zhang, Thermochim. Acta 559, 86 (2013)CrossRef
24.
26.
Zurück zum Zitat G. Wu, Y. Cheng, Q. Xie, C. Liu, K. Kou, L. Zhuo, Y. Wang, J. Polym. Res. 21, 615 (2014)CrossRef G. Wu, Y. Cheng, Q. Xie, C. Liu, K. Kou, L. Zhuo, Y. Wang, J. Polym. Res. 21, 615 (2014)CrossRef
28.
Zurück zum Zitat C. Pan, K. Kou, G. Wu, Y. Zhang, J. Mater. Sci Mater. El. 27, 286 (2016)CrossRef C. Pan, K. Kou, G. Wu, Y. Zhang, J. Mater. Sci Mater. El. 27, 286 (2016)CrossRef
29.
Zurück zum Zitat G. Wu, Y. Cheng, K. Wang, Y. Wang, A. Feng, J. Mater. Sci Mater. El. 27, 5592 (2016)CrossRef G. Wu, Y. Cheng, K. Wang, Y. Wang, A. Feng, J. Mater. Sci Mater. El. 27, 5592 (2016)CrossRef
30.
Zurück zum Zitat Y. Wang, G. Wu, K. Kou, J. Mater. Sci. Mater. Electron. 8279, 27 (2016) Y. Wang, G. Wu, K. Kou, J. Mater. Sci. Mater. Electron. 8279, 27 (2016)
31.
Zurück zum Zitat T. Kuilla, S. Bhadra, D. Yao, N.H. Kim, S. Bose, J.H. Lee, Prog. Polym. Sci. 35, 1350 (2010)CrossRef T. Kuilla, S. Bhadra, D. Yao, N.H. Kim, S. Bose, J.H. Lee, Prog. Polym. Sci. 35, 1350 (2010)CrossRef
32.
Zurück zum Zitat J. Liang, Y. Huang, L. Zhang, Y. Wang, Y. Ma, T. Guo, Y. Chen, Adv. Funct. Mater. 19, 2297 (2009)CrossRef J. Liang, Y. Huang, L. Zhang, Y. Wang, Y. Ma, T. Guo, Y. Chen, Adv. Funct. Mater. 19, 2297 (2009)CrossRef
33.
Zurück zum Zitat M. Fang, K. Wang, H. Lu, Y. Yang, S. Nutt, J. Mater. Chem. 19, 7098 (2009)CrossRef M. Fang, K. Wang, H. Lu, Y. Yang, S. Nutt, J. Mater. Chem. 19, 7098 (2009)CrossRef
34.
Zurück zum Zitat H.J. Salavagione, M.A. Gomez, G. Martinez, Macromolecules 42, 6331 (2009)CrossRef H.J. Salavagione, M.A. Gomez, G. Martinez, Macromolecules 42, 6331 (2009)CrossRef
35.
36.
39.
40.
Zurück zum Zitat D.J. Liaw, K.L. Wang, Y.C. Huang, Prog. Polym. Sci. 37(7), 907 (2012)CrossRef D.J. Liaw, K.L. Wang, Y.C. Huang, Prog. Polym. Sci. 37(7), 907 (2012)CrossRef
42.
Zurück zum Zitat K. Yamanaka, M. Jikei, M. Kakimoto, Macromolecules 33(4), 1111 (2000)CrossRef K. Yamanaka, M. Jikei, M. Kakimoto, Macromolecules 33(4), 1111 (2000)CrossRef
43.
Zurück zum Zitat K. Yamanaka, M. Jikei, M. Kakimoto, Macromolecules 34(12), 3910 (2001)CrossRef K. Yamanaka, M. Jikei, M. Kakimoto, Macromolecules 34(12), 3910 (2001)CrossRef
44.
Zurück zum Zitat K.C. Chang, K.Y. Huang, C.H. Hsu, W.F. Ji, M.C. Lai, W.I. Hung, T.L. Chuang, J.M. Yeh, Eur. Polym. J. 56, 26 (2014)CrossRef K.C. Chang, K.Y. Huang, C.H. Hsu, W.F. Ji, M.C. Lai, W.I. Hung, T.L. Chuang, J.M. Yeh, Eur. Polym. J. 56, 26 (2014)CrossRef
45.
Zurück zum Zitat L.B. Zhang, J.Q. Wang, H.G. Wang, Y. Xu, Z.F. Wang, Z.P. Li, Y.J. Mi, S.R. Yang, Compos. A 43, 1537 (2012)CrossRef L.B. Zhang, J.Q. Wang, H.G. Wang, Y. Xu, Z.F. Wang, Z.P. Li, Y.J. Mi, S.R. Yang, Compos. A 43, 1537 (2012)CrossRef
46.
47.
Zurück zum Zitat M.H. Tsai, H.Y. Wang, H.T. Lu, I.H. Tseng, H.H. Lu, S.L. Huang, J.M. Yeh, Thin Sol. Films 519, 4969 (2011)CrossRef M.H. Tsai, H.Y. Wang, H.T. Lu, I.H. Tseng, H.H. Lu, S.L. Huang, J.M. Yeh, Thin Sol. Films 519, 4969 (2011)CrossRef
48.
Zurück zum Zitat I.H. Tseng, Y.F. Liao, J.C. Chiang, M.H. Chiang, Mater. Chem. Phys. 136, 247 (2012)CrossRef I.H. Tseng, Y.F. Liao, J.C. Chiang, M.H. Chiang, Mater. Chem. Phys. 136, 247 (2012)CrossRef
49.
50.
Zurück zum Zitat Y. Jung, S. Byun, S. Park, H. Lee, A.C.S. Appl, Mater. Interf. 6, 6054 (2014)CrossRef Y. Jung, S. Byun, S. Park, H. Lee, A.C.S. Appl, Mater. Interf. 6, 6054 (2014)CrossRef
51.
53.
54.
Zurück zum Zitat Q.Y. Tang, Y.C. Chan, N.B. Wong, R. Cheung, Polym. Int. 59, 1240 (2010)CrossRef Q.Y. Tang, Y.C. Chan, N.B. Wong, R. Cheung, Polym. Int. 59, 1240 (2010)CrossRef
55.
Zurück zum Zitat O.K. Park, J.Y.H. Wang, M. Goh, J.H. Lee, B.C. Ku, N.H. You, Macromolecules 46, 3505 (2013)CrossRef O.K. Park, J.Y.H. Wang, M. Goh, J.H. Lee, B.C. Ku, N.H. You, Macromolecules 46, 3505 (2013)CrossRef
56.
Zurück zum Zitat V.E. Yudin, J.U. Otaigbe, S.I. Nazarenko, W.D. Kim, E.N. Korytkova, Mech. Compos. Mater. 47, 335 (2011)CrossRef V.E. Yudin, J.U. Otaigbe, S.I. Nazarenko, W.D. Kim, E.N. Korytkova, Mech. Compos. Mater. 47, 335 (2011)CrossRef
57.
58.
59.
Zurück zum Zitat R. Fleming, T. Pawlowski, A. Ammala, IEEE Trans. Dielect. El. In. 12(4), 745 (2005)CrossRef R. Fleming, T. Pawlowski, A. Ammala, IEEE Trans. Dielect. El. In. 12(4), 745 (2005)CrossRef
Metadaten
Titel
In situ polymerization of modified graphene/polyimide composite with improved mechanical and thermal properties
verfasst von
Guanglei Wu
Yonghong Cheng
Zhengdong Wang
Kuikui Wang
Ailing Feng
Publikationsdatum
20.08.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 1/2017
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-016-5560-8

Weitere Artikel der Ausgabe 1/2017

Journal of Materials Science: Materials in Electronics 1/2017 Zur Ausgabe

Neuer Inhalt