Broadband organic color photodetectors with high gain based on C60-doped tri-phase bulk heterojunction

verfasst von: Tao An, Xinying Liu

Erschienen in: Journal of Materials Science: Materials in Electronics

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

We experimentally investigate the spectrum broadening of P3HT:PC61BM:PBDT-TT-F tri-phase bulk heterojunction active layer, and the influence of material mixing degree on the optoelectronic performance of detectors is also discussed. In addition, the mechanism of gain for C60-doped P3HT:PC61BM:PBDT-TT-F detectors is studied. On the basis, we obtain a broadband with responsive spectra from 350 ~ 750 nm and photomultiplication (PM) detector. The resulting detector exhibits responsivity of 2.1, 3.95, 5.05 A/W and the external quantum efficiency of 415%, 924%, and 1361%, respectively, under the illumination of three primary light at − 4 V bias. Moreover, the specific detectivity approaches or exceeds 1012 Jones. The results indicates that the absorption spectrum of active layer can be used to broaden by adding small amount of spectrum broadening material while keeping the original morphology of binary bulk heterojunction. A small weight of C60 dispersed in tri-phase bulk heterojunction active layer can be regarded as electron trap. Combining the advantage of high exciton dissociation efficiency of bulk heterojunction, PM-type organic photodetectors working at low bias can be achieved by triggering hole tunneling injection from cathode.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Anhänge
Nur mit Berechtigung zugänglich
Literatur
1.
Zurück zum Zitat R.J. Vuuren, A. Armin, A.K. Pandey, P.L. Burn, P. Meredith, Adv. Mater. 28, 4766 (2016)CrossRef R.J. Vuuren, A. Armin, A.K. Pandey, P.L. Burn, P. Meredith, Adv. Mater. 28, 4766 (2016)CrossRef
2.
3.
Zurück zum Zitat R. Eckstein, N. Strobel, T. Rodlmeier, K. Glaser, U. Lemmer, G.H. Sosa, Adv. Opt. Mater. 6, 1701108 (2018)CrossRef R. Eckstein, N. Strobel, T. Rodlmeier, K. Glaser, U. Lemmer, G.H. Sosa, Adv. Opt. Mater. 6, 1701108 (2018)CrossRef
4.
Zurück zum Zitat D. Baierl, L. Pancheri, M. Schmidt, D. Stoppa, G.D. Betta, G. Scarpa, P. Lugli, Nat. Commun. 3, 1175 (2012)CrossRef D. Baierl, L. Pancheri, M. Schmidt, D. Stoppa, G.D. Betta, G. Scarpa, P. Lugli, Nat. Commun. 3, 1175 (2012)CrossRef
5.
Zurück zum Zitat D.M. Lyons, A. Armin, M. Stolterfoht, R. Nagiri, R.D. Vuuren, B.N. Pal, P.L. Burn, S.C. Lo, P. Meredith, Org. Electron. 15, 2903 (2014)CrossRef D.M. Lyons, A. Armin, M. Stolterfoht, R. Nagiri, R.D. Vuuren, B.N. Pal, P.L. Burn, S.C. Lo, P. Meredith, Org. Electron. 15, 2903 (2014)CrossRef
6.
Zurück zum Zitat Y. Yang, W. Chen, L.T. Dou, W.H. Chang, H.S. Duan, B. Bob, G. Li, Y. Yang, Nat. Photon. 9, 190 (2015)CrossRef Y. Yang, W. Chen, L.T. Dou, W.H. Chang, H.S. Duan, B. Bob, G. Li, Y. Yang, Nat. Photon. 9, 190 (2015)CrossRef
7.
Zurück zum Zitat R.O. Ocaya, A.G. Al-Sehemi, A. Al-Ghamdi, F. El-Tantawy, F. Yakuphanoglu, J. Alloys Compd. 702, 520 (2017)CrossRef R.O. Ocaya, A.G. Al-Sehemi, A. Al-Ghamdi, F. El-Tantawy, F. Yakuphanoglu, J. Alloys Compd. 702, 520 (2017)CrossRef
8.
Zurück zum Zitat J.S. Huang, T.H. Goh, X.K. Li, M.Y. Sfeir, E.A. Bielinski, S. Tomasulo, M.L. Lee, N. Hazari, A.D. Taylor, Nat. Photon. 7, 479 (2013)CrossRef J.S. Huang, T.H. Goh, X.K. Li, M.Y. Sfeir, E.A. Bielinski, S. Tomasulo, M.L. Lee, N. Hazari, A.D. Taylor, Nat. Photon. 7, 479 (2013)CrossRef
9.
Zurück zum Zitat Z.W. Wu, Y. Liu, S.J. Wei, X. Huang, D.Y. Zhang, M. Zhou, L.W. Chen, C.Q. Ma, H. Wang, Acta Phys. Chim. Sin. 29, 1735 (2013) Z.W. Wu, Y. Liu, S.J. Wei, X. Huang, D.Y. Zhang, M. Zhou, L.W. Chen, C.Q. Ma, H. Wang, Acta Phys. Chim. Sin. 29, 1735 (2013)
10.
11.
Zurück zum Zitat Y. Wang, L.J. Zhu, Y.F. Hu, Z.B. Deng, Z.D. Lou, Y.B. Hou, F. Teng, Opt. Express. 25, 7719 (2017)CrossRef Y. Wang, L.J. Zhu, Y.F. Hu, Z.B. Deng, Z.D. Lou, Y.B. Hou, F. Teng, Opt. Express. 25, 7719 (2017)CrossRef
12.
13.
Zurück zum Zitat L.L. Li, F.J. Zhang, W.B. Wang, Q.S. An, J. Wang, Q.Q. Sun, M. Zhang, A.C.S. Appl, Mater. Interfaces 7, 5890 (2015)CrossRef L.L. Li, F.J. Zhang, W.B. Wang, Q.S. An, J. Wang, Q.Q. Sun, M. Zhang, A.C.S. Appl, Mater. Interfaces 7, 5890 (2015)CrossRef
14.
Zurück zum Zitat W.B. Wang, F.J. Zhang, M.D. Du, L.L. Li, M. Zhang, K. Wang, Y.S. Wang, B. Hu, Y. Fang, J.S. Huang, Nano Lett. 17, 1995 (2017)CrossRef W.B. Wang, F.J. Zhang, M.D. Du, L.L. Li, M. Zhang, K. Wang, Y.S. Wang, B. Hu, Y. Fang, J.S. Huang, Nano Lett. 17, 1995 (2017)CrossRef
15.
Zurück zum Zitat R.M. Nie, X.Y. Deng, F. Lei, G.G. Hu, Y.Y. Wang, G. Yu, J.B. Xu, Small 13, 1603260 (2017)CrossRef R.M. Nie, X.Y. Deng, F. Lei, G.G. Hu, Y.Y. Wang, G. Yu, J.B. Xu, Small 13, 1603260 (2017)CrossRef
16.
Zurück zum Zitat S.T. Chuang, S.C. Chien, F.C. Chen, Appl. Phys. Lett. 100, 013309 (2012)CrossRef S.T. Chuang, S.C. Chien, F.C. Chen, Appl. Phys. Lett. 100, 013309 (2012)CrossRef
18.
Zurück zum Zitat L. Shen, Y.J. Fang, H.T. Wei, Y.B. Yuan, J.S. Huang, Adv. Mater. 28, 2043 (2016)CrossRef L. Shen, Y.J. Fang, H.T. Wei, Y.B. Yuan, J.S. Huang, Adv. Mater. 28, 2043 (2016)CrossRef
19.
Zurück zum Zitat L. Shen, Y. Zhang, Y. Bai, X.P. Zheng, Q. Wang, J.S. Huang, Nanoscale 8, 12990 (2016)CrossRef L. Shen, Y. Zhang, Y. Bai, X.P. Zheng, Q. Wang, J.S. Huang, Nanoscale 8, 12990 (2016)CrossRef
20.
Zurück zum Zitat V. Gupta, V. Bharti, M. Kumar, S. Chand, A.J. Heeger, Adv. Mater. 27, 4398 (2015)CrossRef V. Gupta, V. Bharti, M. Kumar, S. Chand, A.J. Heeger, Adv. Mater. 27, 4398 (2015)CrossRef
21.
22.
Zurück zum Zitat X. Luo, W.L. Lv, L.L. Du, F.Y. Zhao, Y.Q. Peng, Y. Wang, Y. Tang, Phys. Status Solidi RRL 10, 485 (2016)CrossRef X. Luo, W.L. Lv, L.L. Du, F.Y. Zhao, Y.Q. Peng, Y. Wang, Y. Tang, Phys. Status Solidi RRL 10, 485 (2016)CrossRef
23.
Zurück zum Zitat J.L. Miao, F.J. Zhang, M.D. Du, W.B. Wang, Y. Fang, Adv. Opt. Mater. 6, 1800001 (2018)CrossRef J.L. Miao, F.J. Zhang, M.D. Du, W.B. Wang, Y. Fang, Adv. Opt. Mater. 6, 1800001 (2018)CrossRef
24.
Zurück zum Zitat W.B. Wang, M.D. Du, M. Zhang, J.L. Miao, Y. Fang, F.J. Zhang, Adv. Opt. Mater. 6, 1800249 (2018)CrossRef W.B. Wang, M.D. Du, M. Zhang, J.L. Miao, Y. Fang, F.J. Zhang, Adv. Opt. Mater. 6, 1800249 (2018)CrossRef
25.
Zurück zum Zitat R. Dong, C. Bi, Q.F. Dong, F.W. Guo, Y.B. Yuan, Y.J. Fang, Z.G. Xiao, J.S. Huang, Adv. Opt. Mater. 2, 549 (2014)CrossRef R. Dong, C. Bi, Q.F. Dong, F.W. Guo, Y.B. Yuan, Y.J. Fang, Z.G. Xiao, J.S. Huang, Adv. Opt. Mater. 2, 549 (2014)CrossRef
26.
Zurück zum Zitat W.B. Wang, F.J. Zhang, L.L. Liang, M.L. Gao, B. Hu, A.C.S. Appl, Mater. Interfaces. 7, 22660 (2015)CrossRef W.B. Wang, F.J. Zhang, L.L. Liang, M.L. Gao, B. Hu, A.C.S. Appl, Mater. Interfaces. 7, 22660 (2015)CrossRef
Metadaten
Titel
Broadband organic color photodetectors with high gain based on C60-doped tri-phase bulk heterojunction
verfasst von
Tao An
Xinying Liu
Publikationsdatum
06.01.2020
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-019-02815-7

Neuer Inhalt