Abstract
In this study, polyvinyl alcohol (PVA) and boric acid (BA) were mixed in an aqueous medium by heating in order to prepare a PVA/BA hybrid material. The viscosity and pH values of the PVA/BA hybrid material mixed in various proportions were determined. Then the hybrid polymer was electrospun to give dimensions to fibers. The FT-IR spectra of these fibers revealed that BA chemically reacted with PVA and formed B–O–C bonds. The fibers were first calcified at 500 °C and then the calcified products were pelleted and exposed to the sintering process at 1300 °C. The XRD peaks of the sintered product were seen at 2θ = 34.7 and 37.7° verified the formation of boron carbide. The study proved that it was possible to use sub-micron fibers for the production of sub-micron boron carbide material.
Similar content being viewed by others
References
A. Alizadeh, E. Taheri-Nassaj, N. Ehsani, J. Eur. Ceram. Soc. 24, 3227 (2004)
M. Kakiage, N. Tahara, I. Yanase, H. Kobayashi, Mater. Lett. 65, 1839 (2011)
M. Kakiage, N. Tahara, S. Yanagidani, I. Yanase, H. Kobayashi, J. Ceram. Soc. Jpn. 119, 6–422 (2011)
A. Kadenkin, M. Amberger, U.E.A. Fittschen, J.A.C. Broekaert, Microchim. Acta 173, 183 (2011)
W.G. Fahrenholtz, E.W. Neuman, H.J. Brown-Shaklee, G.E. Hilmas, J. Am. Ceram. Soc. 93(11), 3580 (2010)
H.A. Castillo, E. Restrepo-Parra, J.M. Vélez, W. dela Cruz, Surf. Coat. Technol. 205, 3607 (2011)
M.U. Guruz, V.P. Dravid, Y.W. Chung, Thin Solid Films 414, 129 (2002)
C.H. Jung, M.J. Lee, C.J. Kim, Mater. Lett. 58, 609 (2004)
Y. Chen, Y.-W. Chung, S.-Y. Li, Surf. Coat. Technol. 200, 4072 (2006)
P.D. Cuong, H.-S. Ahn, E.-S. Yoon, K.-H. Shin, Surf. Coat. Technol. 201, 4230 (2006)
R.G. Abrefah, R.B.M. Sogbadji, E. Ampomah-Amoako, S.A. Birikorang, H.C. Odoi, B.J.B. Nyarko, Appl. Radiat. Isotopes 69, 85 (2011)
M.G.L. Mirabelli, A.T. Lynch, L.G. Sneddon, Solid State Ionics 32–33, 655 (1989)
D.T. Welna, J.D. Bender, X.L. Wei, L.G. Sneddon, H.R. Allcock, Adv. Mater. 17, 859 (2005)
A.K. Khanra, Bull. Mater. Sci. 30, 93 (2007)
S. Mondal, A.K. Banthia, J. Eur. Ceram. Soc. 25, 287 (2005)
L. Shi, Y. Gu, L. Chen, Y. Qian, Z. Yang, J. Ma, Solid State Commun. 128, 5 (2003)
P.M. Barros, O.V.P. Yoshida, M.A. Schiavon, J. Noncryst. Solids 352, 3444 (2006)
A. Kaminska, A. Sionkowska, Polym. Degrad. Stab. 51(1), 19 (1996)
Z. Chen, X. Mo, C. He, H. Wang, Carbohydr. Polym. 72(3), 410 (2008)
E.J. Shin, W.S. Lyoo, Y.H. Lee, J. Appl. Polym. Sci. 109(2) 1143 (2008)
J.D. Hanawalt, H.W. Rinn, L.K. Frevel, Ind. Eng. Chem. 10, 457 (1938)
J. Linke, H. Bolt, R. Doerner, H. Grubmeir, Y. Hirooka, H. Hoven, C. Mingham, H. Schulze, M. Seki, E. Wallura, T. Weber, J. Winter, J. Nucl. Mater. 176, 856 (1990)
B. Chang, B.L. Gersten, S.T. Szewczyk, J.W. Adams, Appl. Phys. A 86, 83 (2007)
O. Conde, A.J. Silvestre, J.C. Oliveira, Surf. Coat. Technol. 125, 141 (2000)
T. Endo, T. Sato, M. Shimada, J. Mater. Sci. Lett. 6, 683 (1987)
I. Yanase, R. Ogawara, H. Kobayashi, Mater. Lett. 63, 91 (2009)
Acknowledgment
We are grateful to TUBITAK for the financial support (Project no. 106T630).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Uslu, İ., Tunç, T. The Synthesis of Boron Carbide Ceramic via Electrospinning Technique. J Inorg Organomet Polym 22, 183–189 (2012). https://doi.org/10.1007/s10904-011-9600-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10904-011-9600-9