Abstract
Zeolite Y was synthesized from bentonite via the hydrothermal method. The effects of various parameters on the synthesis were investigated. The samples were characterized by XRD, XRF, IR, DTG and wet chemical analysis. The results show that crystallization temperature, aging time and concentration of sodium hydroxide play important roles in the formation of the zeolite. P zeolite was the competitive phase and present in most of the products. However, under optimized conditions, such as crystallization temperature (97 °C), aging time (20 h), concentration of NaOH (3N), pure zeolite Y with high crystallinity was synthesized. The results showed that optimization of the process results in a commercial route to synthesis zeolite Y from bentonite.
Similar content being viewed by others
Notes
Loss of ignition
References
Y. Tang, W.M. Hua, Petrochem. Technol. 29, 336 (2000)
X.S. Zhao, G.Q. Lu, J. Porous Mater. 4, 245 (1997)
A. Singer, V. BerkGaut, Environ. Sci. Technol. 29, 1748 (1995)
N. Shigemoto, H. Hayashi, K. Miyaura, J. Mater. Sci. 28, 4781 (1993)
J. LaRosa, S. Kwan, M.W. Grutzeck, J. Am. Ceram. Soc. 75, 1574 (1992)
C. Amrhein, G.H. Haghnia, T.S. Kim, Environ. Sci. Technol. 30, 735 (1996)
S. Song, J. Guo, Zeolite 18, 84 (1997)
J. Komadel, V. Madejova, F. Elsass, Clay Miner. 31, 333 (1996)
X. Liu, J. Qiu, X. Cui, Appl. Mineral. 697 (2004)
X. Liu, Z. Yan, H. Wang, Y. Luo, J. Nat. Gas Chem. 12, 63 (2003)
H.V. Bekkum, E.M. Flanigen, J.C. Ganson, Introduction to Zeolite Science and Practice (Elsevier, New York, 2001), p. 261
M. Arruebo, R. Fernando, S. Irusta, J. Arbiol, M. Ricardo, J. Santamaria, Nano technology 17, 4057 (2006)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Faghihian, H., Godazandeha, N. Synthesis of nano crystalline zeolite Y from bentonite. J Porous Mater 16, 331–335 (2009). https://doi.org/10.1007/s10934-008-9204-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10934-008-9204-0