Hydrophobic silica aerogels for oil spills clean-up, synthesis, characterization and preliminary performance evaluation

  • Published:
Journal of Porous Materials Aims and scope Submit manuscript

Abstract

The most important requirements for surface water management include the availability of rapid and efficient specific adsorbents. This work presents synthesis, characterization and performance analysis of a novel silica aerogel for oil decontamination from surface water. Hydrophobic silica aerogel powders were synthesized by a rapid co-precursor method applying ambient pressure. An inexpensive aqueous sodium silicate solution was used as starting material, with hexamethyldisilazane (HMDS), tetraethyl orthosilicate and trimethylchlorosilane as organic co-precursors. The prepared silica aerogels were characterized by nitrogen adsorption/desorption technique (BET), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR) and contact angle measurements. Silica aerogel samples prepared using HMDS exhibited the highest BET surface area of about 936 m2/g, pore volume (1.715 cm3/g) and contact angle approaching 106°. The aerogels were then tested for oil adsorbing capacity in oil salt–water mixtures for oil spill clean-up applications. Preliminary oil adsorption experiments have shown that a maximum oil removal of 96 and 90 % using silica aerogel prepared from HMDS from saline and non-saline oily waste waters, respectively. Moreover, the minimization of the costly precursors permits a low-cost large scale production and economic oil spill clean-up applications.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. A. Bayat, S.F. Aghamiri, A. Moheb, G.R. Vakili-Nezhaad, Oil spill cleanup from sea water by sorbent materials. Chem. Eng. Technol. 28, 1525–1528 (2005). doi:10.1002/ceat.200407083

    Article  CAS  Google Scholar 

  2. M. Fingas, Oil spills and their cleanup. Chem. Ind. 24, 1005–1008 (1995)

    Google Scholar 

  3. R.D. Delaune, C.W. Lindau, A. Jugsujinda, Effectiveness of nochar solidifier polymer in removing oil from open water in coastal wetlands. Spill Sci. Technol. Bull. 5, 357–359 (1999). doi:10.1016/S1353-2561(99)00081-X

    Article  Google Scholar 

  4. C.H. Teas, S. Kalligeros, F. Zanikos, S. Stoumas, E. Lois, G. Anastopoulos, Investigation of the effectiveness of absorbent materials in oil spills clean up. Desalination 140(3), 259–264 (2001). doi:10.1016/S0011-9164(01)00375-7

    Article  CAS  Google Scholar 

  5. R.R. Lessard, G. Demarco, The significance of oil dispersants. Spill Sci. Technol. Bull. 6(1), 59–68 (2000). doi:10.1016/S1353-2561(99)00061-4

    Article  CAS  Google Scholar 

  6. V.G. Parale, D.B. Mahadik, M.S. Kavale, A.V. Rao, P.B. Wagh, S.C. Gupta, Potential application of silica aerogel granules for cleanup of accidental spillage of various organic liquids. Soft Nanosci. Lett. 1, 97–104 (2011)

    Article  CAS  Google Scholar 

  7. J.G. Reynolds, P.R. Coronado, L.W. Hrubesh, Hydrophobic aerogels for oil-spill clean up—intrinsic absorbing properties. Energy Sour. 23, 831–843 (2001)

    Article  CAS  Google Scholar 

  8. J.L. Gurav, I.-K. Jung, H.-H. Park, E.S. Kang, D.Y. Nadargi, Review article silica aerogel: synthesis and applications. J. Nanomater. 2010, Article ID 409310

  9. J.G. Reynolds, P.R. Coronado, Hydrophobic aerogels for oil-spill cleanup—synthesis and characterization. J. Non-Cryst. Solids 292, 127–137 (2001)

    Article  CAS  Google Scholar 

  10. J.A. Quevedo, G. Patel, R. Pfeffer, Removal of oil from water by inverse fluidization of aerogels. Ind. Eng. Chem. Res. 48, 191–201 (2009)

    Article  CAS  Google Scholar 

  11. D. Wang, T. Silbaugh, R. Pfeffer, Y.S. Lin, Removal of emulsified oil from water by inverse fluidization of hydrophobic aerogels. Powder Technol. 203, 298–309 (2010)

    Article  CAS  Google Scholar 

  12. A.V. Rao, S.D. Bhagat, H. Hirashima, G.M. Pajonk, Synthesis of flexible silica aerogels using methyltrime–thoxysilane (MTMS) precursor. J. Colloids Interface Sci. 300(1), 279–285 (2006)

    Article  CAS  Google Scholar 

  13. D. Wang, E. McLaughlin, R. Pfeffer, Y.S. Lin, Adsorption of oils from pure liquid and oil–water emulsion on hydrophobic silica aerogels. Sep. Purif. Technol. 99, 28–35 (2012)

    Article  CAS  Google Scholar 

  14. A.V. Rao, M.M. Kulkarni, Hydrophobic properties of TMOS/TMES-based silica aerogels. Mater. Res. Bull. 37, 1667–1677 (2002)

    Article  CAS  Google Scholar 

  15. A.V. Rao, R.R. Kalesh, Comparative studies of the physical and hydrophobic properties of TEOS based silica aerogel using different co-precursors. Sci. Technol. Adv. Mater. 4, 509–515 (2003)

    Article  CAS  Google Scholar 

  16. S.D. Bhagat, Y.-H. Kim, Y.-S. Ahn, J.-G. Yeo, Textural properties of ambient pressure dried water-glass based silica aerogel beads: one day synthesis. Microporous Mesoporous Mater. 96, 237–244 (2006)

    Article  CAS  Google Scholar 

  17. N.D. Hedge, H. Hirashima, A.V. Rao, Two step sol–gel processing of TEOS based hydrophobic silica aerogels using trimethylethoxysilane as a co-precursor. J. Porous Mater. 14, 165–171 (2007)

    Article  Google Scholar 

  18. M. Nogami, S. Hotta, K. Kugimiya, H. Matsubara, Synthesis and characterization of transparent silica-based aerogels using methyltrimethoxysilane precursor. J. Sol–Gel. Sci. Technol. 56, 107–113 (2010)

    Article  CAS  Google Scholar 

  19. G. Pajonk, E. Elaloui, R. Begag, M. Durant, B. Chevalier, J.L. Chevalier, P. Achard, Hydrolysis of an organosilicon compound, U.S. Patent 5,795,557, 18 Aug 1998

  20. S.D. Bhagat, Y.-H. Kim, M.-J. Moon, Y.-S. Ahn, J.-G. Yeo, A cost-effective and fast synthesis of nanoporous SiO2 aerogel powders using water-glass via ambient pressure drying route. Solid State Sci. 9, 628 (2007)

    Article  CAS  Google Scholar 

  21. S.D. Bhagat, Y.-H. Kim, K.-H. Suh, Y.-S. Ahn, J.-G. Yeo, J.-H. Han, Superhydrophobic silica aerogel powders with simultaneous surface modification, solvent exchange and sodium ion removal from hydrogels. Microporous Mesoporous Mater. 112, 504–509 (2008)

    Article  CAS  Google Scholar 

  22. A.P. Rao, A.V. Rao, G.M. Pajonk, Hydrophobic and physical properties of the ambient pressure dried silica aerogels with sodium silicate precursor using various surface modification agents. J. Appl. Surf. Sci. 253, 6032–6040 (2007)

    Article  CAS  Google Scholar 

  23. S. Hwang, T. Kim, S. Hyun, Effect of surface modification conditions on the synthesis of mesoporous crack-free silica aerogel monoliths from water glass via ambient-drying. Microporous Mesoporous Mater. 130, 295–302 (2010)

    Article  CAS  Google Scholar 

  24. U.K.H. Bangi, I. Jung, C. Park, S. Baek, H. Park, Optically transparent silica aerogels based on sodium silicate by a two step sol–gel process and ambient pressure drying. Solid State Sci. 18, 50–57 (2013)

    Article  CAS  Google Scholar 

  25. M.F. Júlio, L.M. Ilharco, Super hydrophobic hybrid aerogel powders from water glass with distinctive applications. Microporous Mesoporous Mater. 199, 29–39 (2014)

    Article  Google Scholar 

  26. S.D. Bhagat, K.-T. Park, Y.-H. Kim, J.-S. Kim, J.-H. Han, A continuous production process for silica aerogel powders based on sodium silicate by fluidized bed drying of wet–gel slurry. Solid State Sci. 10, 1113–1116 (2008)

    Article  CAS  Google Scholar 

  27. S.W. Hwang, T.-Y. Kim, S.-H. Hyun, Optimization of instantaneous solvent exchange/surface modification process for ambient synthesis of monolithic silica aerogels. J. Colloid Interface Sci. 322, 224–230 (2008)

    Article  CAS  Google Scholar 

  28. S.S. Kistler, Coherent expanded aerogels and jellies. Nature 127, 741 (1931)

    Article  CAS  Google Scholar 

  29. APHA, Standard Methods for Water and Wastewater Examination, 22nd edn. (American Public Health Association, Washington, 2012)

    Google Scholar 

  30. S. Ki Hong, M.Y. Yoon, H.J. Hwang, Fabrication of spherical silica aerogel granules from water glass by ambient pressure drying. J. Am. Ceram. Soc. 94(10), 3198–3201 (2011)

    Article  Google Scholar 

  31. F. Tadayon, S. Motahar, M. Hosseini, Application of Taguchi method for optimizing the adsorption of lead ions on nanocomposite silica aerogel activated carbon. Acad. Res. Int. 2(2), 42–48 (2012)

    Google Scholar 

  32. A.C. Pierre, E. Elaloui, G.M. Pajonk, Comparison of the structure and porous texture of alumina gels synthesized by different methods. Langmiur 14, 66–73 (1998)

    Article  CAS  Google Scholar 

  33. W.C. Li, A.H. Lu, S.C. Guo, Control of mesoporous structure of aerogels derived from cresol–formaldehyde. J. Colloid interface Sci. 254, 153 (2002)

    Article  CAS  Google Scholar 

  34. J.L. Mohanan, S.L. Brock, Influence of synthetic and processing parameters on the surface area, speciation, and particle formation in copper oxide/silica aerogel composites. Chem. Mater. 15, 2567–2576 (2003)

    Article  CAS  Google Scholar 

  35. K.S.W. Sing, D.H. Everett, R.A.W. Haul, L. Moscou, R.A. Pierotti, J. Rouqerol, T. Siemieniewska, Lewis base mediated efficient synthesis and solvation. Pure Appl. Chem. 57(4), 803 (1985)

    Article  Google Scholar 

  36. Z. Shao, F. Luo, X. Cheng, Y. Zhang, Superhydrophobic sodium silicate based silica aerogel prepared by ambient pressure drying. Mater. Chem. Phys. 141, 570–575 (2013)

    Article  CAS  Google Scholar 

  37. H.X. Shi, J. Cui, H. Shen, H. Wu, Preparation of silica aerogel and its adsorption performance to organic molecule. Adv. Mater. Sci. Eng. 2014, Article ID 850420

Download references

Acknowledgments

This work was financially supported by the National Research Centre (NRC) of Egypt, Tenth plan, under Grant Number 10070406.

Author information

Authors and Affiliations

  1. Chemical Engineering and Pilot Plant Department, National Research Center, P.O. Box 12622, 33 EL Bohouth St. (Former EL Tahrir St.), Dokki, Giza, Egypt

    Mohamed H. Sorour, Heba A. Hani & Ghada A. Al-Bazedi

  2. Refractories, Ceramics and Building Materials Department, National Research Center, P.O. Box 12622, 33 EL Bohouth St. (Former EL Tahrir St.), Dokki, Giza, Egypt

    A. M. EL-Rafei

Authors
  1. Mohamed H. Sorour
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Heba A. Hani
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Ghada A. Al-Bazedi
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. A. M. EL-Rafei
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Heba A. Hani.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Sorour, M.H., Hani, H.A., Al-Bazedi, G.A. et al. Hydrophobic silica aerogels for oil spills clean-up, synthesis, characterization and preliminary performance evaluation. J Porous Mater 23, 1401–1409 (2016). https://doi.org/10.1007/s10934-016-0200-5

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10934-016-0200-5

Keywords

Search

Navigation