Abstract
The effects of Ar ambient pressure (vacuum and 0, 10, and 20 B) and annealing times (0.5 and 1 h) on microstructural, superconducting, and mechanical properties of bulk superconducting MgB2 are investigated. The samples are produced using the solid-state reaction method. X-ray diffraction (XRD) and scanning electron microscopy (SEM) measurements are performed for determination of the crystal structure and surface morphology of MgB2 samples, respectively. The superconducting properties are studied by AC magnetic susceptibility measurements. Microhardness analyses are made using the Vickers microhardness test for determination of mechanical properties of all samples. Increasing the Ar pressure decreases the lattice parameters and hence the average grain size. Increasing the annealing time results in larger lattice parameters and larger grain formation. The susceptibility measurements revealed a two-step transition which is reminiscent of granular superconductors. The intra-grain transition temperature is determined to be 38.4 K for all samples. The inter-grain transition temperature of 37.2 K is obtained for samples produced under Ar ambient pressure. The samples produced under Ar ambient pressure have better superconducting properties than the ones produced in vacuum. Increasing the annealing time under vacuum further decreases the superconducting properties probably due to Mg loss.
Similar content being viewed by others
References
Akimitsu, J., et Al.: Nature 410, 63 (2001)
Buzea, C., Yamashita, T.: Supercond. Sci. Technol. 14, 11 (2001)
Angst, M., Puzniak, R.: Condensed matter arXiv:0305048v2 (2003)
Larbalestier, D.C., Rike, M.O.L., Cooley, L.D., Polyanskii, A.A., Jiang, Y.J., Patnaik, S., Cai, X.Y., Feldmann, D.M., Gurevich, A., Squitieri, A.A., Naus, M.T., Eom, C.B., Hellstrom, E.E., Cava, R.J., Regan, K.A., Rogado, N., Hayward, M.A., He, T., Slusky, J.S., Khalifah, P., Inumaru, K., Haas, M.: Nature 410, 186–189 (2001)
Aksan, M.A., Yakıncı, M.E.: Güldeste, A.: J. Alloy. Comp. 424, 33–40 (2006)
Eyidi, D., Eibl, O., Wenzel, T., Nickel, K.G., Giovannini, M., Saccone, A.: Micron 34, 85–86 (2003)
Schmidt, J., Schnelle, W., Grin Y., Kniep, R.: Solid State Sci. 5, 535–539 (2003)
Kölemen, U.: J. Alloy. Comp. 425, 429–435 (2006)
Prikhna, T., Gawalek, W., Savchuk, Y., Sergienko, N., Moshchil, V., Dub, S., Sverdun, V., Kovalev, L., Penkin, V., Zeisberger, M., Wendt, M., Fuchs, G., Habisreuther, T., Litzkendorf, D., Nagorny, P., Melnikov, V.: Phys. C, 460–462 (2007)
Dancera, C.E.J., Mikheenkob, P., Bevanb, A., Abellb, J.S., Todda, R.I., Grovenor, C.R.M.: J. Eur. Ceram. Soc. 29, 1817–1824 (2009)
Gorur, O., Nursoy, M., Terzioglu, C., Varilci, A., Belenli, I.: J. Phys: Conf. Ser. 153, 012012 (2009)
Güçlü, N.: Mater. Chem. Phys. 101, 470–474 (2007)
Kitaguchi, H., Kumakura, H., Togano, K.: Phys. C: Supercond. 363, 198–201 (2001)
Goldacker, W., Schlachter, S.I., Reiner, J., Zimmer, S., Nyilas, A., Kiesel, H.: Appl. Supercond. 13, 3261–3264 (2003)
Ozturk, O.: PhD Thesis, The effect of Au diffusion-doped on structural, superconducting and mechanical properties of Bi1.8Pb0.35Sr1.9Ca2.1Cu3Oy (2007)
Aksu, E., Gencer, A., Calınlı, N., Koralay, H., Çavdar, S.: Phys. B: Condens. Matter 363, 158–165 (2005)
Goldfarb, R.B., Lelental, M., Thompson, C.A., Hein, R.A., Francavilla, T.L., Liebenberg, D.H. Plenum, New York (1992)
Supple, F., Campbell, A.M., Cooper, J.R.: Phys. C 242, 233 (1995)
Flippen, R.B., Askew, T.R., Fendrich, J.A., Vlcek, B.M.: Phys. C 228, 85 (1994)
Caplin, A.D., Cohen, L.F., Perkins, G.K., Zhukov, A.A.: Supercond. Sci. Technol. 7, 412 (1994)
Chen, D.-X., Mei, Yu, Luo, H.L.: Phys. C 167, 317–323 (1990)
Celebi, S., Kolemen, U., Malik, A.I., Ozturk, A.: Phys. Status. Solidi A194, 260–270 (2002)
Gencer, A., Mutlu, R.H., Belenli, I., Ozogul, O., Aydınuraz, A.: Supercond. Sci. Tech. 9, 284 (1996)
Jorgensen, J.D., Hinks, D.G., Short, S.: Phys. Rev. B 63, 224522 (2001)
Vogt, T., Schneider, G., Hriljac, J.A., Yang, G., Abell, J.S.: Phys. Rev. B 63, 220505 (2001)
Zhang, C., Zhang, X.: Comput. Mater. Sci. 50, 1097–1101 (2011)
Ozturk, O., Asikuzun, E., Erdem, M., Yildirim, G., Yildiz, O., Terzioglu, C.: J. Mater. Sci. Mater Electron 23, 511–519 (2012)
Schneider, T., Di Castro, D.: Phys. Rev. B 72, 054501 (2005)
Dogruer, M., Gorur, O., Zalaoglu, Y., Ozturk, O., Yildirim, G., Varilci, A., Terzioglu, C.: J. Mater. Sci. Mater Electron 24, 352–361 (2013)
Koralay, H., Hicyilmaz, O., Cavdar, S., Asikuzun, E., Tasci, A.T., Ozturk, O.: J. Mater. Sci. Mater Electron 25, 3116–3126 (2014)
Arda, L., Ozturk, O., Asikuzun, E., Ataoglu, S.: Powder Technol. 235, 479–484 (2013)
Tosun, M., Ataoglu, S., Arda, L., Ozturk, O., Asikuzun, E., Akcan, D., Cakiroglu, O.: Mater. Sci. Eng. A 590, 416–422 (2014)
Asikuzun, E., Ozturk, O., Cetinkara, H.A., Yildirim, G., Varilci, A., Yılmazlar, M., Terzioglu, C.: J. Mater. Sci. Mater Electron 23, 1001–1010 (2012)
Koralay, H., Arslan, A., Cavdar, S., Ozturk, O., Asikuzun, E., Gunen, A., Tasci, A.T.: J. Mater. Sci. Mater Electron 24, 4270–4278 (2013)
Acknowledgments
This research has been supported by the Kastamonu University Scientific Research Projects Coordination Department under the Grant No. KUBAP-03/2012-03.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ozturk, O., Asikuzun, E., Kaya, S. et al. Ac Susceptibility Measurements and Mechanical Performance of Bulk MgB2 . J Supercond Nov Magn 28, 1943–1952 (2015). https://doi.org/10.1007/s10948-015-3003-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-015-3003-z