Abstract
The lateral levitation force between melt-textured (Gd123)1−x :(Gd211) x bulk superconductors for x = 0.0, 0.1, 0.2, 0.3, 0.4, and 0.5 and a permanent magnet is measured at 30, 40, 50, 60, and 77 K under zero-field-cooling and field-cooling conditions. The variations on the observed levitation force are correlated to the varied content of Gd211 in these melt-textured samples.
Similar content being viewed by others
References
Hull, J.R., Hanany, S., Matsumura, T., Johnson, B., Jones, T.: Characterization of a high-temperature superconducting bearing for use in a cosmic microwave background polarimeter. Supercond. Sci. Technol. 18, S1 (2005)
Ma, K.B., Postrekhin, Y.V., Chu, W.K.: Superconductor and magnet levitation devices. Rev. Sci. Instrum. 74, 4989 (2003)
Gapalek, W., Habisreuthe, T., Strasser, T., Wu, M., Litzkendorf, D., Fischer, K., Gornert, P., Gladum, A., Stoye, P., Verges, P., Ilushin, K.V., Kovalev, L.K.: Remanent induction and levitation force of melt textured YBCO. Appl. Supercond. 2, 465 (1994)
Wang, S., Wang, J., Wang, X., Ren, Z., Zeng, Y., Deng, C., Jiang, H.: The man-loading high-temperature superconducting maglev test vehicle. IEEE Trans. Appl. Ind. 13, 2134 (2003)
Xu, C., Hu, A., Sakai, N., Izumi, M., Hirabayashi, I.: Enhanced Jc in air-processed GdBa2Cu3O7 −δ superconductors. Physica C 426–431, 613–617 (2005)
Yang, W.M., Zhou, L., Feng, Y., Zhang, P.X., Chen, S., Wu, M.Z., Zhang, C.P., Wang, J.R., Du, Z.H., Wang, F.Y., Yu, Z.M., Wu, X.Z., Gawalek, W., Gornert, P.: The grain-alignment and its effect on the levitation force of melt processed YBCO single-domained bulk superconductors. Physica C 307, 271–276 (1998)
Zhou, D., Hara, S., Li, B., Noudem, J., Izumi, M.: Flux pinning properties of Gd-Ba-Cu-O trapped field magnets grown by a modified top-seeded melt growth. Supercond. Sci. Technol. 27, 044015 (2014)
Kambara, M., Nadendla, H.B., Shi, Y., Cardwell, D.A.: Reduction of porosity in RE1Ba2Cu3Oy pseudo crystals. Physica C 341–348, 2473–2474 (2000)
Nadendla, H.B., Iida, K., Shi, Y., Cardwell, D.A.: Fabrication of high performance light rare earth based single-grain superconductors in air. Appl. Phys. Lett. 87, 202506 (2005)
Nariki, S., Seo, S.J., Sakai, N., Murakami, M.: Influence of the size of Gd211 starting powder on the critical current density of Gd-Ba-Cu-O bulk superconductor. Supercond. Sci. Technol. 13, 778 (2000)
Nariki, S., Sakai, N., Tomita, M., Murakami, M.: Mechanical properties of melt-textured Gd–Ba–Cu–O bulk with silver addition. Physica C 378-381, 779–782 (2000)
Celik, S., Ozturk, K.: Semiempirical equation of the levitation-force density for (Sm123)1–x(Yb211)x superconducting samples, Phys. Status Solidi (A) 206, 724–730 (2009)
Song, H., de Haas, O., Beyer, C., Krabbes, G., Verges, P., Schultz, L.: Influence of the lateral movement on the levitation and guidance force in the high-temperature superconductor maglev system. Appl. Phys. Lett. 86, 192506 (2005)
Davis, L.C., Logothetis, E.M., Soltis, R.E.: Stability of magnets levitated above superconductors. J. Appl. Phys. 64, 4212 (1988)
Hull, J.R., Cansiz, A.: Vertical and lateral forces between a permanent magnet and a high-temperature superconductor. J. Appl. Phys. 86, 6396 (1999)
Zhang, X., Zhou, Y., Zhou, J.: Three-dimensional measurements of forces between magnet and superconductor in a levitation system. Physica C 467, 125–129 (2007)
Bhadrakumari, S., Predeep, P., Sheela, A.: Magnetic levitation force measurement on HTSC ceramic/thermoplastic mer composites. Compos. Sci. Technol. 68, 3230–3233 (2008)
Zhao, Y., Wang, J.S., Wang, S.Y., Ren, Z.Y., Song, H.H., Wang, X.R., Cheng, C.H.: Applications of YBCO melt textured bulks in maglev technology. Physica C 412–414, 771–777 (2004)
Kim, C.J., Kim, H.J., Joob, J.H., Honga, G.W.: Processing variables of the multi-seeded melt growth process of YBCO superconductors: The properties of YBCO samples with various grain junctions. Physica C 354, 384–387 (2001)
Patel, A., Giunchi, G., Albisetti, A.F., Shi, Y., Hopkins, S.C., Palka, R., Cardwell, D., Glowacki, B.A.: High force magnetic levitation using magnetized superconducting bulks as a field source for bearing applications. Phys. Procedia 36, 937–942 (2012)
Erdem, O., Ozturk, K., Guner, S.B., Celik, S., Yanmaz, E.: Effects of initial cooling conditions and measurement heights on the levitation performance of bulk MgB2 superconductor at different measurement temperatures. J. Low Temp. Phys. 177, 28–39 (2014)
Savaskan, B., Koparan, E.T., Celik, S., Ozturk, K., Yanmaz, E.: Investigation on the levitation force behaviour of malic acid added bulk MgB2 superconductors. Physica C 502, 63–69 (2014)
Nariki, S., Seo, S.J., Sakai, N., Murakami, M.: Influence of the size of Gd211 starting powder on the critical current density of Gd–Ba–Cu–O bulk superconductor. Supercond. Sci. Technol. 13, 778–784 (2000)
Celik, S.: Design of magnetic levitation force measurement system at any low temperatures from 20 K to room temperature. J. All. And Comp. 662, 546–556 (2016)
Hari Babu, N., Cardwell, D.A., Lo, W., Campbell, A.M.: Flux pinning in large NdBa2Cu3 O 7 grains fabricated by seeded-melt growth. Phys. Rev. B 61, 735–740 (200)
Acknowledgments
This research was supported by the Recep Tayyip Erdogan University Scientific Research Projects Coordination Department (project number: 2012.102.01.1). All the magnetic levitation force measurements were performed in the MLFMS designed by the project of TÜBİTAK (project number: 110T622) and whose patent application number is 2013/13638 for the Turkish Patent Institute (TPE).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Guner, S.B., Celik, S., Cansız, A. et al. Lateral Force Measurements for (Gd123)1−x :(Gd211) x Superconductors at Different Temperatures. J Supercond Nov Magn 30, 1335–1343 (2017). https://doi.org/10.1007/s10948-016-3779-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-016-3779-5