Convenient synthesis and morphology of latex particles composed of poly (methyl methacrylate)-b-poly (n-butyl acrylate) by 1, 1-diphenylethylene (DPE) seeded emulsion polymerization

verfasst von: Wenwen Wang, Mengjiao Liu, Junwei Gu, Qiuyu Zhang, Jimmy W. Mays

Erschienen in: Journal of Polymer Research | Ausgabe 8/2014

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Methyl methacrylate-butyl acrylate structural latexes were synthesized by two-stage seeded emulsion polymerization using 1,1-diphenylethylene (DPE) as a control reagent. In the first stage, the seed latex particles with the precursor poly (methyl methacrylate-DPE) (P(MMA-DPE)) were prepared, and then the second monomer n-butyl acrylate (nBA) was swollen into the seed latex particles under stirring at room temperature. In the second stage, the polymerization of nBA was thermally initiated at 80 °C, and the latex particles composed of block copolymer were synthesized. The size and morphology of the latex particles were investigated by light scattering and TEM. The contact angles of different latex films were also measured. The block copolymer was characterized by size exclusion chromatography, nuclear magnetic resonance spectroscopy, and differential scanning calorimetry. Microphase separation of the block copolymer was examined using atomic force microscopy.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
2.
Zurück zum Zitat Ahmad H, Miah M, Pervin M, Rahman M (2003) Colloid Polym Sci 281:897–901CrossRef Ahmad H, Miah M, Pervin M, Rahman M (2003) Colloid Polym Sci 281:897–901CrossRef
3.
Zurück zum Zitat Cao J, Pan X, Huang W, Wang Y, Hua D, Zhu X, Liang H (2012) J Colloid Interface Sci 381:137–142CrossRef Cao J, Pan X, Huang W, Wang Y, Hua D, Zhu X, Liang H (2012) J Colloid Interface Sci 381:137–142CrossRef
4.
Zurück zum Zitat You B, Zhou D, Yang F, Ren X (2011) Colloids Surf A Physicochem Eng Asp 392:365–370CrossRef You B, Zhou D, Yang F, Ren X (2011) Colloids Surf A Physicochem Eng Asp 392:365–370CrossRef
5.
Zurück zum Zitat Oh JK (2008) J Polym Sci A Polym Chem 46:6983–7001 Oh JK (2008) J Polym Sci A Polym Chem 46:6983–7001
7.
8.
Zurück zum Zitat Herrera V, Pirri R, Leiza JR, Asua JM (2006) Macromolecules 39:6969–6974CrossRef Herrera V, Pirri R, Leiza JR, Asua JM (2006) Macromolecules 39:6969–6974CrossRef
9.
11.
Zurück zum Zitat Charleux B, D’Agosto F, Delaittre G (2010) In Hybrid Latex Particles; Herk, A. M., Landfester, K., Eds. Springer Berlin Heidelberg: 233:125–183 Charleux B, D’Agosto F, Delaittre G (2010) In Hybrid Latex Particles; Herk, A. M., Landfester, K., Eds. Springer Berlin Heidelberg: 233:125–183
12.
13.
Zurück zum Zitat Kitayama Y, Yorizane M, Kagawa Y, Minami H, Zetterlund PB, Okubo M (2009) Polymer 50:3182–3187CrossRef Kitayama Y, Yorizane M, Kagawa Y, Minami H, Zetterlund PB, Okubo M (2009) Polymer 50:3182–3187CrossRef
14.
Zurück zum Zitat Kitayama Y, Kagawa Y, Minami H, Okubo M (2010) Langmuir 26:7029–7034CrossRef Kitayama Y, Kagawa Y, Minami H, Okubo M (2010) Langmuir 26:7029–7034CrossRef
15.
Zurück zum Zitat Nicolas J, Ruzette A-V, Farcet C, Gérard P, Magnet S, Charleux B (2007) Polymer 48:7029–7040CrossRef Nicolas J, Ruzette A-V, Farcet C, Gérard P, Magnet S, Charleux B (2007) Polymer 48:7029–7040CrossRef
16.
Zurück zum Zitat Das P, Claverie JP (2012) J Polym Sci A Polym Chem 50:2802–2808 Das P, Claverie JP (2012) J Polym Sci A Polym Chem 50:2802–2808
18.
19.
Zurück zum Zitat Wei R, Luo Y, Zeng W, Wang F, Xu S (2012) Ind Eng Chem Res 51:15530–15535CrossRef Wei R, Luo Y, Zeng W, Wang F, Xu S (2012) Ind Eng Chem Res 51:15530–15535CrossRef
20.
Zurück zum Zitat Kitayama Y, Yorizane M, Kagawa Y, Minami H, Zetterlund PB, Okubo M (2009) Polymer 50:3182–3187CrossRef Kitayama Y, Yorizane M, Kagawa Y, Minami H, Zetterlund PB, Okubo M (2009) Polymer 50:3182–3187CrossRef
21.
Zurück zum Zitat Chern C-S, Chen T-J, Wu S-Y, Chu H-B, Huang C-F (1997) Journal of Macromolecular Science. Part A: Pure and Applied Chemistry 34:1221–1236 Chern C-S, Chen T-J, Wu S-Y, Chu H-B, Huang C-F (1997) Journal of Macromolecular Science. Part A: Pure and Applied Chemistry 34:1221–1236
22.
Zurück zum Zitat Csetneki I, Faix MK, Szilagyi A, Kovacs A, Németh Z, Zrinyi M (2004) J Polym Sci A Polym Chem 42:4802–4808 Csetneki I, Faix MK, Szilagyi A, Kovacs A, Németh Z, Zrinyi M (2004) J Polym Sci A Polym Chem 42:4802–4808
24.
Zurück zum Zitat Viala S, Antonietti M, Tauer K, Bremser W (2003) Polymer 44:1339–1351CrossRef Viala S, Antonietti M, Tauer K, Bremser W (2003) Polymer 44:1339–1351CrossRef
25.
Zurück zum Zitat Luo Y-D, Chiu W-Y (2009) J Polym Sci A Polym Chem 47:6789–6800 Luo Y-D, Chiu W-Y (2009) J Polym Sci A Polym Chem 47:6789–6800
26.
Zurück zum Zitat Wang W, Zhang H, Geng W, Gu J, Zhou Y, Zhang J, Zhang QJ (2013) Colloid Interf Sci 406:154–164CrossRef Wang W, Zhang H, Geng W, Gu J, Zhou Y, Zhang J, Zhang QJ (2013) Colloid Interf Sci 406:154–164CrossRef
27.
Zurück zum Zitat Wang W, Zhang Q, Guo F, Gu J, Yin C (2011) J Polym Res 18:1229–1235CrossRef Wang W, Zhang Q, Guo F, Gu J, Yin C (2011) J Polym Res 18:1229–1235CrossRef
28.
Zurück zum Zitat Haloi DJ, Ata S, Singha NK, Jehnichen D, Voit B (2012) ACS Appl Mater Interfaces 4:4200–4207CrossRef Haloi DJ, Ata S, Singha NK, Jehnichen D, Voit B (2012) ACS Appl Mater Interfaces 4:4200–4207CrossRef
29.
Zurück zum Zitat Ohno S, Gao H, Cusick B, Kowalewski T, Matyjaszewski K (2009) Macromol Chem Phys 210:421–430CrossRef Ohno S, Gao H, Cusick B, Kowalewski T, Matyjaszewski K (2009) Macromol Chem Phys 210:421–430CrossRef
30.
32.
Zurück zum Zitat Taenghom T, Pan Q, Rempel GL, Kiatkamjornwong S (2013) Colloid Polym Sci 291:1365–1374CrossRef Taenghom T, Pan Q, Rempel GL, Kiatkamjornwong S (2013) Colloid Polym Sci 291:1365–1374CrossRef
34.
35.
Zurück zum Zitat Anastasiadis S, Russell T, Satija S, Majkrzak C (1989) Phys Rev Lett 62:1852CrossRef Anastasiadis S, Russell T, Satija S, Majkrzak C (1989) Phys Rev Lett 62:1852CrossRef
36.
Zurück zum Zitat Sriprom W, James M, Perrier S, Neto C (2009) Macromolecules 42:3138–3146CrossRef Sriprom W, James M, Perrier S, Neto C (2009) Macromolecules 42:3138–3146CrossRef
Metadaten
Titel
Convenient synthesis and morphology of latex particles composed of poly (methyl methacrylate)-b-poly (n-butyl acrylate) by 1, 1-diphenylethylene (DPE) seeded emulsion polymerization
verfasst von
Wenwen Wang
Mengjiao Liu
Junwei Gu
Qiuyu Zhang
Jimmy W. Mays
Publikationsdatum
01.08.2014
Verlag
Springer Netherlands
Erschienen in
Journal of Polymer Research / Ausgabe 8/2014
Print ISSN: 1022-9760
Elektronische ISSN: 1572-8935
DOI
https://doi.org/10.1007/s10965-014-0502-8

Weitere Artikel der Ausgabe 8/2014

Journal of Polymer Research 8/2014 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.