Optically transparent superhydrophobic TEOS-derived silica films by surface silylation method

Optically transparent silica films were prepared at room temperature (~27°C) by keeping the molar ratio of TEOS:MeOH:H₂O (0.001 M NH₄F) constant at 1:19.29:6.20, respectively. A surface chemical modification of the films was done with alkylchlorosilanes at different concentrations from 0 to 1 vol. % and aging times varied from half to 2 h. The DMCS and TMCS surface modified silica films showed the static water contact angle of 146° and 162°, respectively. When the DMCS and TMCS modified films were cured at temperatures higher than 240 and 275°C, respectively, the films became superhydrophilic. Further, the humidity study was carried out at a relative humidity of 90% at 30°C temperature over 60 days. We characterized the water repellent silica films by Fourier transform infrared spectroscopy, scanning electron microscopy, atomic force microscopy, % of optical transmission, humidity tests and contact angle measurements.