Thermal characterization of nitrile butadiene rubber (NBR)/PVC blends

Summary

Nitrile butadiene rubber (NBR) and NBR/PVC blends were produced using 2,2,4-trimethyl-1,2-dihydroquinoline (TMQ) or not as antioxidant. Controlled ozone degradation was performed in several samples. Thermal, compositional and morphological analysis was performed by means of differential scanning calorimetry, thermogravimetry, chemical analysis and scanning electron microscopy. Thermogravimetry analysis shows four mass loss processes related to plastizicer, complex rubber degradation and metallic oxides and other additives. In NBR (NBR/PVC blends) the onset temperature of the first degradation process varies between 227-231°C (259-262°C) and the apparent activation energy between 26 and 36 kJ mol^-1 (36-57 kJ mol^-1), the NBR/PVC samples non degraded presents the higher thermal stability.