Erratum to: J Nanopart Res 17:462 (2015).
DOI:10.1007/s11051-015-3276-y
A calibration error on our radiometer led us to misreport irradiance values for the UVC lamps used in our original manuscript.
The original statement:
“The precursor gas mixture (H2 and CO) was injected in the reactor with a molar ratio of 0.1/1 (H2/CO) and was irradiated by two UVC lamps (main emission peak at 253.7 nm, irradiance of 5.5 × 10−4 W/cm2 at 4.5 cm).”
The corrected statement:
“The precursor gas mixture (H2 and CO) was injected in the reactor with a molar ratio of 0.1/1 (H2/CO) and was irradiated by two UVC lamps (main emission peak at 253.7 nm, irradiance of 0.01 W/cm 2 at 3.5 cm).”
Author information
Authors and Affiliations
Corresponding author
Additional information
The online version of the original article can be found at http://dx.doi.org/10.1007/s11051-015-3276-y
Rights and permissions
About this article
Cite this article
Javanbakht, T., Laurent, S., Stanicki, D. et al. Erratum to: Charge effect of superparamagnetic iron oxide nanoparticles on their surface functionalization by photo-initiated chemical vapour deposition. J Nanopart Res 18, 315 (2016). https://doi.org/10.1007/s11051-016-3628-2
Published:
DOI: https://doi.org/10.1007/s11051-016-3628-2