Influence of weave of carbon fabric on abrasive wear performance of polyetherimide composites

Three composites of Polyetherimide (PEI) reinforced with carbon fabric (CF) of three weaves viz. plain, twill and satin-4 H were developed keeping the amount of fabric constant (55% by vol.). Studies on mechanical properties confirmed that the twill weave composite (T) showed the highest strength, modulus (both tensile and flexural) and interlaminar shear strength (ILSS) followed by satin (S) and plain weave (P) composites. The performance order, however, was reverse in the case of toughness and elongation to break. Specific wear rate in a single-pass, unidirectional and un-lubricated abrasive wear mode against SiC paper showed strong influence of weave in mild wear condition (load 10 N). Composite S showed the highest wear resistance (W _R) followed by composites T and P. With increase in load, the difference in performance diminished to the extent that at 40 N, it was almost similar for all the three composites. This was correlated with the difference in the length of the fibers between crossover points which, in turn, allowed the microdisplacement of fibers in the composites during abrasion. This was supported by the SEM.