Ni3Al Matrix Composite with Lubricious Tungstate at High Temperatures

verfasst von: Shengyu Zhu, Qinling Bi, Jun Yang, Weimin Liu

Erschienen in: Tribology Letters | Ausgabe 2/2012

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Ni3Al–Ag–BaF2/CaF2–W composites were fabricated by the powder metallurgy route, and their tribological properties over a wide temperature range, starting from room temperature up to 800 °C, were investigated. The Ni3Al matrix composite with 15 wt% BaF2/CaF2 exhibited a favorable friction coefficient (range 0.3–0.4) and wear rate (0.2–6.2 × 10−4mm3 N−1 m−1). The formation of BaWO4 and CaWO4 with lubricity on the worn surface due to a tribo-chemical reaction at high temperatures provided excellent lubricating properties. The low friction coefficient over a broad temperature range could be attributed to the synergistic effect of Ag, BaF2/CaF2, BaWO4, and CaWO4.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Dellacorte, C., Sliney, H.E.: Tribological properties of PM212-a high-temperature, self-lubricating, powder-metallurgy composite. Lubric. Eng. 47, 298–303 (1991) Dellacorte, C., Sliney, H.E.: Tribological properties of PM212-a high-temperature, self-lubricating, powder-metallurgy composite. Lubric. Eng. 47, 298–303 (1991)
2.
Zurück zum Zitat Dellacorte, C., Sliney, H.E.: Tribological and mechanical comparison of sintered and HIPped PM212: high temperature self-lubricating composites. Lubric. Eng. 48, 877–885 (1992) Dellacorte, C., Sliney, H.E.: Tribological and mechanical comparison of sintered and HIPped PM212: high temperature self-lubricating composites. Lubric. Eng. 48, 877–885 (1992)
3.
Zurück zum Zitat Dellacorte, C., Fellenstein, J.A.: The effect of compositional tailoring on the thermal expansion and tribological properties of PS300: a solid lubricant composite coating. Tribol. Trans. 40, 639–642 (1997)CrossRef Dellacorte, C., Fellenstein, J.A.: The effect of compositional tailoring on the thermal expansion and tribological properties of PS300: a solid lubricant composite coating. Tribol. Trans. 40, 639–642 (1997)CrossRef
4.
Zurück zum Zitat Blanchet, T.A., Kim, J.H., Calabrese, S.J., DellaCorte, C.: Thrust-Washer evaluation of self-lubricating PS304 composite coatings in high temperature sliding contact. Tribol. Trans. 45, 491–498 (2002)CrossRef Blanchet, T.A., Kim, J.H., Calabrese, S.J., DellaCorte, C.: Thrust-Washer evaluation of self-lubricating PS304 composite coatings in high temperature sliding contact. Tribol. Trans. 45, 491–498 (2002)CrossRef
5.
Zurück zum Zitat Wang, W.C.: Application of a high temperature self-lubricating composite coating on steam turbine components. Surf. Coat. Technol. 177–178, 12–17 (2004) Wang, W.C.: Application of a high temperature self-lubricating composite coating on steam turbine components. Surf. Coat. Technol. 177–178, 12–17 (2004)
6.
Zurück zum Zitat Ding, C.H., Li, P.L., Ran, G., Tian, Y.W., Zhou, J.N.: Tribological property of self-lubricating PM304 composite. Wear 262, 575–581 (2007)CrossRef Ding, C.H., Li, P.L., Ran, G., Tian, Y.W., Zhou, J.N.: Tribological property of self-lubricating PM304 composite. Wear 262, 575–581 (2007)CrossRef
7.
Zurück zum Zitat Ouyang, J.H., Li, Y.F., Wang, Y.M., Zhou, Y., Murakami, T., Sasakic, S.: Microstructure and tribological properties of ZrO2(Y2O3) matrix composites doped with different solid lubricants from room temperature to 800 °C. Wear 267, 1353–1360 (2009)CrossRef Ouyang, J.H., Li, Y.F., Wang, Y.M., Zhou, Y., Murakami, T., Sasakic, S.: Microstructure and tribological properties of ZrO2(Y2O3) matrix composites doped with different solid lubricants from room temperature to 800 °C. Wear 267, 1353–1360 (2009)CrossRef
8.
Zurück zum Zitat Jin, Y., Kato, K., Umehara, N.: Effects of sintering aids and solid lubricants on tribological behaviours of CMC/Al2O3 pair at 650°C. Tribol. Lett. 6, 15–21 (1999)CrossRef Jin, Y., Kato, K., Umehara, N.: Effects of sintering aids and solid lubricants on tribological behaviours of CMC/Al2O3 pair at 650°C. Tribol. Lett. 6, 15–21 (1999)CrossRef
9.
Zurück zum Zitat Skopp, A., Woydt, M., Habig, K.-H.: Tribological behavior of silicon nitride materials under unlubricated sliding between 22 and 1000°C. Wear 181–183, 571–580 (1995) Skopp, A., Woydt, M., Habig, K.-H.: Tribological behavior of silicon nitride materials under unlubricated sliding between 22 and 1000°C. Wear 181–183, 571–580 (1995)
10.
Zurück zum Zitat Deevi, S.C., Sikkat, V.K., Liu, C.T.: Processing, properties, and applications of nickel and iron aluminides. Prog. Mater. Sci. 42, 177–192 (1991)CrossRef Deevi, S.C., Sikkat, V.K., Liu, C.T.: Processing, properties, and applications of nickel and iron aluminides. Prog. Mater. Sci. 42, 177–192 (1991)CrossRef
11.
Zurück zum Zitat Yamaguchi, M., Inui, H., Ito, K.: High temperature structural intermetallics. Acta Mater. 48, 307–322 (2000)CrossRef Yamaguchi, M., Inui, H., Ito, K.: High temperature structural intermetallics. Acta Mater. 48, 307–322 (2000)CrossRef
12.
Zurück zum Zitat Sikka, V.K., Deevi, S.C., Viswanathan, S., Swindeman, R.W., Santella, M.L.: Advances in processing of Ni3Al-based intermetallics and applications. Intermetallics 8, 1329–1337 (2000)CrossRef Sikka, V.K., Deevi, S.C., Viswanathan, S., Swindeman, R.W., Santella, M.L.: Advances in processing of Ni3Al-based intermetallics and applications. Intermetallics 8, 1329–1337 (2000)CrossRef
13.
Zurück zum Zitat Czeppe, T., Wierzbinski, S.: Structure and mechanical properties of NiAl and Ni3Al-based alloys. Int. J. Mech. Sci. 42, 1499–1518 (2000)CrossRef Czeppe, T., Wierzbinski, S.: Structure and mechanical properties of NiAl and Ni3Al-based alloys. Int. J. Mech. Sci. 42, 1499–1518 (2000)CrossRef
14.
Zurück zum Zitat Zhu, S.Y., Bi, Q.L., Yang, J., Liu, W.M., Xue, Q.J.: Ni3Al matrix high temperature self-lubricating composites. Tribol. Int. 44, 445–453 (2011)CrossRef Zhu, S.Y., Bi, Q.L., Yang, J., Liu, W.M., Xue, Q.J.: Ni3Al matrix high temperature self-lubricating composites. Tribol. Int. 44, 445–453 (2011)CrossRef
15.
Zurück zum Zitat Zhu, S.Y., Bi, Q.L., Yang, J., Liu, W.M.: Influence of Cr content on tribological properties of Ni3Al matrix high temperature self-lubricating composites. Tribol. Int. 44, 1182–1187 (2011)CrossRef Zhu, S.Y., Bi, Q.L., Yang, J., Liu, W.M.: Influence of Cr content on tribological properties of Ni3Al matrix high temperature self-lubricating composites. Tribol. Int. 44, 1182–1187 (2011)CrossRef
16.
Zurück zum Zitat Zhu, S.Y., Bi, Q.L., Yang, J., Liu, W.M.: Effect of fluoride content on friction and wear performance of Ni3Al matrix high temperature self-lubricating composites. Tribol. Lett. 43, 341–349 (2011)CrossRef Zhu, S.Y., Bi, Q.L., Yang, J., Liu, W.M.: Effect of fluoride content on friction and wear performance of Ni3Al matrix high temperature self-lubricating composites. Tribol. Lett. 43, 341–349 (2011)CrossRef
17.
Zurück zum Zitat Zhu, S.Y., Bi, Q.L., Yang, J., Liu, W.M., Xue, Q.J.: Effect of particle size on tribological behavior of Ni3Al matrix high temperature self-lubricating composites. Tribol. Int. 44, 1800–1809 (2011)CrossRef Zhu, S.Y., Bi, Q.L., Yang, J., Liu, W.M., Xue, Q.J.: Effect of particle size on tribological behavior of Ni3Al matrix high temperature self-lubricating composites. Tribol. Int. 44, 1800–1809 (2011)CrossRef
18.
Zurück zum Zitat Peterson, M.B., Murray, S.F., Florek, J.J.: Consideration of lubricants for temperatures above 1000 F. Tribol. Trans. 2, 225–234 (1959)CrossRef Peterson, M.B., Murray, S.F., Florek, J.J.: Consideration of lubricants for temperatures above 1000 F. Tribol. Trans. 2, 225–234 (1959)CrossRef
19.
Zurück zum Zitat Zha, J.N., Wang, J.B., Huang, Y.Z., Zhang, G.W., Ouyang, J.L.: Study on the WC–Ni–PbO high temperature self-lubricating metal-cermet materials (in Chinese). Tribology 11, 28–34 (1991) Zha, J.N., Wang, J.B., Huang, Y.Z., Zhang, G.W., Ouyang, J.L.: Study on the WC–Ni–PbO high temperature self-lubricating metal-cermet materials (in Chinese). Tribology 11, 28–34 (1991)
20.
Zurück zum Zitat Prasad, S.V., McDevitt, N.T., Zabinski, J.S.: Tribology of tungsten disulfide-nanocrystalline zinc oxide adaptive lubricant films from ambient to 500°C. Wear 237, 186–196 (2000)CrossRef Prasad, S.V., McDevitt, N.T., Zabinski, J.S.: Tribology of tungsten disulfide-nanocrystalline zinc oxide adaptive lubricant films from ambient to 500°C. Wear 237, 186–196 (2000)CrossRef
21.
Zurück zum Zitat Jujur, I.N., Hanada, S.: Tensile properties of W/Ni3Al composites at elevated temperatures. Mater. Sci. Eng. A. 192–193, 848–855 (1995) Jujur, I.N., Hanada, S.: Tensile properties of W/Ni3Al composites at elevated temperatures. Mater. Sci. Eng. A. 192–193, 848–855 (1995)
22.
Zurück zum Zitat Stone, D., Liu, J., Singh, D.P., Muratore, C., Voevodin, A.A., Mishra, S., Rebholz, C., Ge, Q., Aouadi, S.M.: Layered atomic structures of double oxides for low shear strength at high temperatures. Scripta Mater. 62, 735–738 (2010)CrossRef Stone, D., Liu, J., Singh, D.P., Muratore, C., Voevodin, A.A., Mishra, S., Rebholz, C., Ge, Q., Aouadi, S.M.: Layered atomic structures of double oxides for low shear strength at high temperatures. Scripta Mater. 62, 735–738 (2010)CrossRef
23.
Zurück zum Zitat Walck, S.D., Zabinski, J.S., McDevitt, N.T., Bultman, J.E.: Characterization of air-annealed, pulsed laser deposited ZnO–WS2 solid film lubricants by transmission electron microscopy. Thin Solid Films 305, 130–143 (1997)CrossRef Walck, S.D., Zabinski, J.S., McDevitt, N.T., Bultman, J.E.: Characterization of air-annealed, pulsed laser deposited ZnO–WS2 solid film lubricants by transmission electron microscopy. Thin Solid Films 305, 130–143 (1997)CrossRef
Metadaten
Titel
Ni3Al Matrix Composite with Lubricious Tungstate at High Temperatures
verfasst von
Shengyu Zhu
Qinling Bi
Jun Yang
Weimin Liu
Publikationsdatum
01.02.2012
Verlag
Springer US
Erschienen in
Tribology Letters / Ausgabe 2/2012
Print ISSN: 1023-8883
Elektronische ISSN: 1573-2711
DOI
https://doi.org/10.1007/s11249-011-9885-4

Weitere Artikel der Ausgabe 2/2012

Tribology Letters 2/2012 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.