Effect of Ag and Ti₃SiC₂ on Tribological Properties of TiAl Matrix Self-lubricating Composites at Room and Increased Temperatures

Dry sliding tribological properties of TiAl matrix self-lubricating composites (TMSC) containing Ag, Ti₃SiC₂, Ag and Ti₃SiC₂ were investigated from 25 to 800 °C under ball-on-disk test conditions against Si₃N₄ counterface under the same conditions of 10 N-0.234 m/s. The results indicated that the tribological properties were strongly dependent on the lubricant additives. TMSC with the addition of Ag and Ti₃SiC₂ (TAT) exhibited the lower friction coefficients (0.32–0.43) and less wear rates (1.23–4.13 × 10⁻⁴ mm³ N⁻¹m⁻¹) in the wide temperature range of 25–800 °C. The excellent tribological properties of TAT over the wide temperature range were attributed to the synergetic effect of Ag and Ti₃SiC₂ lubricants, silver diffusion forming a rich-silver smooth tribo-film on the frictional surface of TAT at low and moderate temperatures from 25 to 400 °C, while Ti₃SiC₂ oxidation reaction forming rich-oxide tribo-film on the worn surface of TAT at higher temperatures of 600 and 800 °C.