Environmental scanning electron microscopy (ESEM) and nanoindentation investigation of the crack tip process zone in marble

  • Research Paper
  • Published:
Acta Geotechnica Aims and scope Submit manuscript

Abstract

This study explores the interaction between crack initiation and nanomechanical properties in the crack-tip fracture process zone of Carrara marble. Specimens with preexisting cracks were loaded in a uniaxial testing machine until the process zone appeared at the tips of the preexisting cracks. ESEM analysis reveals an increase in microcrack density in the process zone with increased loading of the specimen. Nanoindentation testing comprised of lines and grids of single nanoindentations located both near and far from the process zone shows a decrease in both indentation modulus and indentation hardness near grain boundaries in intact material, and with closeness to the process zone. Ultimately, the study confirms that the crack-tip process zone manifests itself as an area of reduced indentation hardness and indentation modulus in marble.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16
Fig. 17
Fig. 18
Fig. 19
Fig. 20
Fig. 21
Fig. 22
Fig. 23
Fig. 24

Similar content being viewed by others

References

  1. Alber M, Brardt A (2003) Factors influencing fracture toughness kic from simple screening tests. Int J Rock Mech Min 40(5):779–784

    Article  Google Scholar 

  2. Alber M, Hauptfleisch U (1999) Generation and visualization of microfractures in carrara marble for estimating fracture toughness, fracture shear and fracture normal stiffness. Int J Rock Mech Min 36(8):1065–1071

    Article  Google Scholar 

  3. Anders MH, Wiltschko DV (1994) Microfracturing, paleostress and the growth of faults. J Struct Geol 16(6):795–815

    Article  Google Scholar 

  4. Atkinson BK (1979) Fracture toughness of tennessee sandstone and carrara marble using the double torsion testing method. Int J Rock Mech Min 16(1):49–53

    Article  Google Scholar 

  5. Austin NJ (2008) Grain size evolution and strain localization in deformed marbles. Dissertation, Massachusetts Institute of Technology

  6. Backers T, Stanchits S, Dresen G (2005) Tensile fracture propagation and acoustic emission activity in sandstone: the effect of loading rate. Int J Rock Mech Min 42(7–8):1094–1101

    Article  Google Scholar 

  7. Bulychev SI, Alekhin VP, Shorshorov MK, Ternovskii AP (1976) Mechanical properties of materials studied from kinetic diagrams of load versus depth of impression during microimpression. Probl Prochn 9:79–83

    Google Scholar 

  8. Bulychev SI, Alekhin VP, Shorshorov MK, Ternovskii AP, Shnyrev GD (1976) Determining young’s modulus from the indentor penetration diagram. Ind Lab 41(9):1409–1412

    Google Scholar 

  9. Butenuth C, Freitas MHD, Al-Samahiji D, Park HD, Cosgrove JW, Schetelig K (1993) Observations on the measurement of tensile strength using the hoop test. Int J Rock Mech Min 30(2):157–162

    Article  Google Scholar 

  10. Chengyong W, Peide L, Rongsheng H, Xiutang S (1990) Study of the fracture process zone in rock by laser speckle interferometry. Int J Rock Mech Min 27(1):65

    Article  Google Scholar 

  11. Denarie E, Saouma VE, Iocco A, Varelas D (2001) Concrete fracture process zone characterization with fiber optics. J Eng Mech 127(5):494–502

    Google Scholar 

  12. Du JJ, Kobayashi AS, Hawkins NM (1990) An experimental–numerical analysis of fracture process zone in concrete fracture specimens. Eng Fract Mech 35(1–3):15–27

    Article  Google Scholar 

  13. Ganneau FP, Constantinides G, Ulm FJ (2006) Dual-indentation technique for the assessment of strength properties of cohesive-frictional materials. Int J Solids Struct 43(6):1727–1745

    Article  MATH  Google Scholar 

  14. Guo ZK, Kobayashi AS, Hawkins NM (1993) Further studies on fracture process zone for mode I concrete fracture. Eng Fract Mech 46(6):1041–1049

    Article  Google Scholar 

  15. Hertzberg RW (1996) Deformation and fracture mechanics of engineering materials, 4th edn. Wiley, London

    Google Scholar 

  16. Irwin GR (1957) Analysis of stresses and strains near the end of a crack traversing a plate. J Appl Mech (24):361–364

  17. Jaeger JC (1967) Failure of rocks under tensile conditions. Int J Rock Mech Min 4(2):219–227

    Article  MathSciNet  Google Scholar 

  18. Janssen C, Wagner F, Zang A, Dresen G (2001) Fracture process zone in granite: a microstructural analysis. Int J Earth Sci 90(1):46–59

    Article  Google Scholar 

  19. Labuz JF, Shah SP, Dowding CH (1983) Post peak tensile load-displacement response and the fracture process zone in rock. In: 24th U.S. symposium on rock mechanics, pp 421–428

  20. Labuz JF, Shah SP, Dowding CH (1987) The fracture process zone in granite: evidence and effect. Int J Rock Mech Min 24(4):235–246

    Article  Google Scholar 

  21. Lin Q, Fakhimi A, Haggerty M, Labuz JF (2009) Initiation of tensile and mixed-mode fracture in sandstone. Int J Rock Mech Min 46(3):489–497

    Article  Google Scholar 

  22. Marini P, Bellopede R (2009) Bowing of marble slabs: evolution and correlation with mechanical decay. Constr Build Mater 23(7):2599–2605

    Article  Google Scholar 

  23. Miller M, Bobko C, Vandamme M, Ulm FJ (2008) Surface roughness criteria for cement paste nanoindentation. Cem Concr Res 38:467–476

    Article  Google Scholar 

  24. Molli G, Conti P, Giorgetti G, Meccheri M, Oesterling N (2000) Microfabric study on the deformational and thermal history of the alpi apuane marbles (carrara marbles), Italy. J Struct Geol 22:1809–1825

    Article  Google Scholar 

  25. Nasseri MHB, Mohanty B, Young RP (2006) Fracture toughness measurements and acoustic emission activity in brittle rocks. Rock Damage and Fluid Transport, Part I. Birkhuser Basel, pp 917–945

  26. Oliver W, Pharr G (1992) An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J Mater Res 7(6):1564–1583

    Article  Google Scholar 

  27. Otsuka K, Date H (2000) Fracture process zone in concrete tension specimen. Eng Fract Mech 65(2-3):111–131

    Article  Google Scholar 

  28. Picart P, Diouf B, Lolive E, Berthelot JM (2004) Investigation of fracture mechanisms in resin concrete using spatially multiplexed digital fresnel holograms. Opt Eng 43:1169–1176

    Article  Google Scholar 

  29. Pique EJ, Dortmans L, de With G (2003) A model material approach to the study of fracture process zone of quasi-brittle materials. J Mater Sci 38(19):4003–4011

    Article  Google Scholar 

  30. Swanson PL, Spetzler H (1984) Ultrasonic probing of the fracture process zone in rock using surface waves. 25th U.S. national symposium on rock mechanics, Northwestern University, Evanston, IL, 25–27 June 1984, paper. Sponsorship: U.S. Geological Survey, 10 pp

  31. Tabor D (1948) A simple theory of static and dynamic hardness. Proc R Soc A Math Phys 192(1029):247–274

    Article  Google Scholar 

  32. Uguz A, Martin JW (1996) Plastic zone size measurement techniques for metallic materials. Mater Charact 37:105–118

    Article  Google Scholar 

  33. Vandamme M (2008) The nanogranular origin of concrete creep: a nanoindentation investigation of microstructure and fundamental properties of calcium-silicate-hydrates. Dissertation, Massachusetts Institute of Technology

  34. Wong LNY, Einstein HH (2009) Using high speed video imaging in the study of cracking processes of rock. Geotech Test J 32(2):1–17

    Google Scholar 

  35. Wong NY (2008) Crack coalescence in molded gypsum and carrara marble. Dissertation, Massachusetts Institute of Technology

  36. Wong NY (2009) Crack coalescence in molded gypsum and carrara marble: part 1. Macroscopic observations and interpretation. Rock Mech Rock Eng (42):475–511

  37. Wong NY (2009) Crack coalescence in molded gypsum and carrara marble: part 2—microscopic observations and interpretation. Rock Mech Rock Eng (42):513–545

  38. Zang A, Wagner FC, Stanchits S, Janssen C, Dresen G (2000) Fracture process zone in granite. J Geophys Res 105:23651–23662

    Article  Google Scholar 

  39. Zhang ZX (2002) An empirical relation between mode i fracture toughness and the tensile strength of rock. Int J Rock Mech Min 39(3):401–406

    Article  Google Scholar 

  40. Zietlow WK, Labuz JF (1998) Measurement of the intrinsic process zone in rock using acoustic emission. Int J Rock Mech Min 35(3):291–299

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to H. H. Einstein.

Appendices

Appendix 1: Surface preparation for nanoindentation

Surface preparation is vital for nanoindentation. An ideal surface is smooth and flat and models the infinite half-space assumed in Eqs. 1 and 2. A non-ideal surface is “rough” or contains raised and depressed regions on the surface. The properties derived from nanoindentation on a non-ideal surface exhibit greater spread with surface roughness [23]. Polishing, or rubbing the sample surface with abrasives in stages of decreasing abrasive size, reduces roughness and thereby produces more accurate nanoindentation results. Each nanoindentation specimen in the current investigation underwent a five-stage polishing procedure before nanoindentation testing [5, 23] (Table 6).

Table 6 Specimen surfaces are prepared for nanoindentation with a five-stage polishing procedure

The Asylum Research MFP-3D Atomic Force Microscope© was used to verify the adequacy of this polishing procedure. Following statistical corrections for surface sloping and large-scale surface waviness, the final roughness, R q, was determined from (via Mountains SPM Image Analysis Software; Fig. 25):

$$ R_{\rm q}=\sqrt{\frac{1}{n^{2}} \sum_{i=1}^{n} \sum_{j=1}^{n} z_{ij}^{2}}, $$
(7)

where n is the number of pixels along the edge of the AFM scan (Fig. 25; each micrometer contains a number of pixels set by the scan resolution) and z ij is the height at a position (ij) above or below a mean reference plane [23]. The scans in this investigation had a resolution of 40 pixels by 40 pixels and a size of 50 μm by 50 μm. Essentially, the roughness value represents the average distance from a reference level near the sample surface to the highest peaks or the deepest valleys on the surface. Figure 25c depicts the topographical information from a single scan; the dark line through the middle represents the reference level. Roughness is formulated with respect to distances from this datum. This yielded a final roughness of R q = 9.32 nm.

Fig. 25
figure 25

An AFM scan yields a a color-gradient contour plot of the surface, which may also be displayed as b a 3D isometric diagram. c Depicts height information from a single scan with respect to a reference level, or datum (color figure online)

Surface roughness should be less than five times the depth of nanoindentation [23]. In this investigation, the surface roughness of 9.32 nm is far less than five times the depth of nanoindentation −250 nm. Thus, the surface preparation employed in this investigation is sufficient.

Appendix 2: Nanoindentation parameter selection

The selection of two nanoindentation parameters—load applied by the nanoindenter and spacing between indentations—affects the accuracy of nanoindentation results. If the load is too high or spacing too small, indentation-induced fractures may extend from one indentation to the next and influence the derived mechanical properties.

The appropriateness of the nanoindentation parameters was verified with ESEM. An investigation was conducted to see whether indentation-induced fracture occurred for the indentation parameters used in the study. Two types of indentations were conducted—typical indentations with parameters used through the current study and “exaggerated” indentations with a much higher (by a factor of 80) indentation load (see Fig. 26 and Table 7). It was found that no indentation-induced fracture was apparent for typical indentations. It was also found that the “exaggerated” indentations induced fracture extending only 17.2 μm, or nearly twice the typical indentation spacing. It is thus assumed that the typical indentation load of 2.85 mN avoids indentation-induced fracture and a spacing of 8 μm prevents indentations from running into any potential fracture.

Table 7 A comparison of typical indentations and a large-load “exaggerated” indentation
Fig. 26
figure 26

An “exaggerated” indentation shows little indentation-induced cracking. The greatest observable distance of cracking from the center of the indentation is 17.2 μm (between center of indentation and tip of diagonal crack)

Appendix 3: Nanoindentation box plots

A box plot (Fig. 27) provides a first-order means of data analysis for this investigation because it presents a concise summary of the spread and typical values of each nanoindentation test (where a single test consists of over 300 individual nanoindentations). Although box plots may assume various forms and present various statistical parameters, for the data in this investigation, the bottom and top of the whiskers correspond to the mean nanoindentation value (either modulus or hardness), respectively, minus and plus one standard deviation. The central value corresponds to the median value, and the bottom and top of the box correspond to the 25th and 75th percentile of the data. Median is used since it expresses the typical value from many nanoindentations without being susceptible to outlier values, in the way that mean is susceptible. Note that for normally distributed data sets, approximately 25 % of the data can be found between the mean and the 25th or 75th percentile. The closeness of the ends of the box (25th/75th percentile) to the ends of the whiskers (average ±1SD) indicates the spread of the data. Data sets with little spread will have larger boxes, and smaller distances from box to whiskers; data sets with more spread will have larger boxes, and greater distances from box to whiskers. The box plot thus presents a concise summary of the spread and typical values of the data from each nanoindentation test series.

Fig. 27
figure 27

A box plot succintly captures the spread and typical value of a test comprised of many individual nanoindentations

Rights and permissions

Reprints and permissions

About this article

Cite this article

Brooks, Z., Ulm, F.J. & Einstein, H.H. Environmental scanning electron microscopy (ESEM) and nanoindentation investigation of the crack tip process zone in marble. Acta Geotech. 8, 223–245 (2013). https://doi.org/10.1007/s11440-013-0213-z

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11440-013-0213-z

Keywords

Navigation