Abstract
The influences of water/cement ratio and admixtures on carbonation resistance of sulphoaluminate cement-based high performance concrete (HPC) were investigated. The experimental results show that with the decreasing water/cement ratio, the carbonation depth of sulphoaluminate cement-based HPC is decreased remarkably, and the carbonation resistance capability is also improved with the adding admixtures. The morphologies and structure characteristics of sulphoaluminate cement hydration products before and after carbonation were analyzed using SEM and XRD. The analysis results reveal that the main hydration product of sulphoaluminate cement, that is ettringite (AFt), decomposes after carbonation.
Similar content being viewed by others
References
Wang Yanmou, Su Muzhen, Zhang Liang. Sulphoaluminate Cement[M]. Beijing: Beijing Industrial University Press, 1999(in Chinese)
Feng Naiqian. High Performance Concrete[M]. Beijing: China Architecture & Building Press, 1996 (in chinese) Odler. Cements Containing Calcium Sulfoaluminate[C]//Special Inorganic Cements, E and FN Spon, London and New York, 2000: 69–87
J Pera, J Ambroise. New Application of Calcium Sulfoaluminate Cement[J]. Cement and Concrete Research, 2004, 34(4): 671–676
L Zhang, Al Glasser. New Concretes based on Calcium Sulfoaluminate Cement[C]//Proceedings of the Internations Conference on Modern Concrete Materials: Binders, Additions and Adimixers, 1999: 261–274
Su Muzhen. Analysis of Sulphoaluminate Cement Durability [N]. China Building Material Newspaper, 2004: 9–2(in Chinese)
Wu Zhongwei. Development Prospects and Problems of High Performance Concrete[J]. Architecture Technology, 1998, (1): 8–13(in Chinese)
Diao Jiangjing. Production and Application of Sulphoaluminate Cement[M]. Beijing: China Building Materials Industry Press, 2006(in Chinese)
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by the National Natural Science Foundation of China (No.50872043)
Rights and permissions
About this article
Cite this article
Zhang, D., Xu, D., Cheng, X. et al. Carbonation resistance of sulphoaluminate cement-based high performance concrete. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 24, 663–666 (2009). https://doi.org/10.1007/s11595-009-4663-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-009-4663-y