Erschienen in: Metallurgical and Materials Transactions A 11/2007

01.11.2007 | SYMPOSIUM: Dynamic Behavior of Materials

Dynamic Recrystallization: The Dynamic Deformation Regime

verfasst von: L.E. Murr, C. Pizaña

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 11/2007

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Severe plastic deformation (PD), especially involving high strain rates (>10s–1), occurs through solid-state flow, which is accommodated by dynamic recrystallization (DRX), either in a continuous or discontinuous mode. This flow can be localized in shear instability zones (or adiabatic shear bands (ASBs)) with dimensions smaller than 5 μ, or can include large volumes with flow zone dimensions exceeding centimeters. This article illustrates these microstructural features using optical and electron metallography to examine a host of dynamic deformation examples: shaped charge jet formation, high-velocity and hypervelocity impact crater formation, rod penetration into thick targets (which includes rod and target DRX flow and mixing), large projectile-induced target plug formation and failure, explosive welding, and friction-stir welding and processing. The DRX is shown to be a universal mechanism that accommodates solid-state flow in extreme (or severe) PD regimes.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Fußnoten
1
INCONEL is a trademark of INCO Alloys International Inc., Huntington, WV.
 
Literatur
1.
Zurück zum Zitat H.A. Grebe, H.R. Pak, M.A. Meyers: Metall. Trans. A, 1985, vol. 16A, pp. 711-21. H.A. Grebe, H.R. Pak, M.A. Meyers: Metall. Trans. A, 1985, vol. 16A, pp. 711-21.
2.
3.
Zurück zum Zitat A.H. Chokshi, M.A. Meyers: Scripta Metall. Mater., 1990, vol. 24, pp. 605–08. CrossRef A.H. Chokshi, M.A. Meyers: Scripta Metall. Mater., 1990, vol. 24, pp. 605–08. CrossRef
4.
Zurück zum Zitat U. Andrade, M.A. Meyers, K.S. Vecchio, A.H. Chokshi: Acta Metall. Mater., 1994, vol. 42 (9), pp. 3183–95. CrossRef U. Andrade, M.A. Meyers, K.S. Vecchio, A.H. Chokshi: Acta Metall. Mater., 1994, vol. 42 (9), pp. 3183–95. CrossRef
5.
Zurück zum Zitat M.A. Meyers, Y.J. Chen, F.D.S. Marquis, D.S. Kim: Metall. Mater. Trans. A, 1995, vol. 26, pp. 2493–2502. CrossRef M.A. Meyers, Y.J. Chen, F.D.S. Marquis, D.S. Kim: Metall. Mater. Trans. A, 1995, vol. 26, pp. 2493–2502. CrossRef
6.
Zurück zum Zitat L.E. Murr, H.K. Shih, C.-S. Niou, L. Zernow: Scripta Metall. Mater., 1993, vol. 29, pp. 567–71. CrossRef L.E. Murr, H.K. Shih, C.-S. Niou, L. Zernow: Scripta Metall. Mater., 1993, vol. 29, pp. 567–71. CrossRef
7.
Zurück zum Zitat L.E. Murr, H.K. Shih, C.-S. Niou, L. Zernow: Scripta Metall. Mater., 1993, vol. 29, pp. 1291–97. CrossRef L.E. Murr, H.K. Shih, C.-S. Niou, L. Zernow: Scripta Metall. Mater., 1993, vol. 29, pp. 1291–97. CrossRef
8.
Zurück zum Zitat L.E. Murr, C.-S. Niou, E.P. Garcia, E. Ferreyra, T., J.M. Rivas, and J.C. Sanchez: Mater. Sci. Eng. A, 1997, vol. 222, pp. 118–32 L.E. Murr, C.-S. Niou, E.P. Garcia, E. Ferreyra, T., J.M. Rivas, and J.C. Sanchez: Mater. Sci. Eng. A, 1997, vol. 222, pp. 118–32
9.
Zurück zum Zitat C. Kennedy, L.E. Murr: Mater. Sci. Eng. A, 2002, vol. 325, pp. 131–43. CrossRef C. Kennedy, L.E. Murr: Mater. Sci. Eng. A, 2002, vol. 325, pp. 131–43. CrossRef
10.
Zurück zum Zitat E.A. Trillo, E.V. Esquivel, L.E. Murr, L.S. Magness: Mater. Character., 2002, vol. 48, pp. 407–21. CrossRef E.A. Trillo, E.V. Esquivel, L.E. Murr, L.S. Magness: Mater. Character., 2002, vol. 48, pp. 407–21. CrossRef
11.
Zurück zum Zitat C. Pizaña, L.E. Murr, M.T. Baquera, I.A. Anchondo, A. Putrevu, C.Y. Piña, T.C. Tamoria, H.C. Chen, S.J. Cytron: Mater. Sci. Eng. A, 2006, vol. 428, pp. 301–13. CrossRef C. Pizaña, L.E. Murr, M.T. Baquera, I.A. Anchondo, A. Putrevu, C.Y. Piña, T.C. Tamoria, H.C. Chen, S.J. Cytron: Mater. Sci. Eng. A, 2006, vol. 428, pp. 301–13. CrossRef
12.
Zurück zum Zitat G. Liu, L.E. Murr, C-S. Niou, J.C. McClure, F.R. Vega: Scripta Mater., 1997, vol. 37 (3), pp. 355–61. CrossRef G. Liu, L.E. Murr, C-S. Niou, J.C. McClure, F.R. Vega: Scripta Mater., 1997, vol. 37 (3), pp. 355–61. CrossRef
13.
Zurück zum Zitat G. Liu, L.E. Murr, J.C. McClure: J. Mater. Sci. Lett., 1997, vol. 16, pp. 1801–03. CrossRef G. Liu, L.E. Murr, J.C. McClure: J. Mater. Sci. Lett., 1997, vol. 16, pp. 1801–03. CrossRef
14.
Zurück zum Zitat L.E. Murr, R.D. Flores, O.V. Flores, J.C. McClure, G. Liu, D. Brown: Mater. Res. Innov., 1998, vol. 1, pp. 211–23. CrossRef L.E. Murr, R.D. Flores, O.V. Flores, J.C. McClure, G. Liu, D. Brown: Mater. Res. Innov., 1998, vol. 1, pp. 211–23. CrossRef
15.
Zurück zum Zitat Y. Li, L.E. Murr, J.C. McClure: Mater. Sci. Eng. A, vol. 271, pp. 213–23. Y. Li, L.E. Murr, J.C. McClure: Mater. Sci. Eng. A, vol. 271, pp. 213–23.
16.
Zurück zum Zitat L.E. Murr, E.A. Trillo, S. Pappu, C. Kennedy: J. Mater. Sci., 2002, vol. 37, pp. 3337–60. CrossRef L.E. Murr, E.A. Trillo, S. Pappu, C. Kennedy: J. Mater. Sci., 2002, vol. 37, pp. 3337–60. CrossRef
17.
Zurück zum Zitat A. Karimi, M. Maamouri, J.L. Martin: Mater. Sci. Eng. A, 1989, vol. 113, pp. 287–96CrossRef A. Karimi, M. Maamouri, J.L. Martin: Mater. Sci. Eng. A, 1989, vol. 113, pp. 287–96CrossRef
18.
Zurück zum Zitat High Performance Structures and Materials II, C.A. Brebbia and W.P. DeWilde, eds., WIT Press, London, 2004 High Performance Structures and Materials II, C.A. Brebbia and W.P. DeWilde, eds., WIT Press, London, 2004
19.
Zurück zum Zitat Ultrafine Grained Materials, R.S. Mishra, S.L. Semiatin, C. Suryanarayana, N.N. Thadhani, and T.C. Lowe, eds., TMS, Warrendale, PA, 2000 Ultrafine Grained Materials, R.S. Mishra, S.L. Semiatin, C. Suryanarayana, N.N. Thadhani, and T.C. Lowe, eds., TMS, Warrendale, PA, 2000
20.
Zurück zum Zitat M.A. Meyers, A. Mishra, D.J. Benson: Progr. Mater. Sci., 2006, vol. 51, pp. 427–556. CrossRef M.A. Meyers, A. Mishra, D.J. Benson: Progr. Mater. Sci., 2006, vol. 51, pp. 427–556. CrossRef
21.
Zurück zum Zitat S.A. Quiñones, L.E. Murr: Phys. Status Solidi A, 1998, vol. 166, pp. 763–89CrossRef S.A. Quiñones, L.E. Murr: Phys. Status Solidi A, 1998, vol. 166, pp. 763–89CrossRef
22.
Zurück zum Zitat E.A. Trillo, L.E. Murr, A.H. Bujanda, N.E. Martinez: Acta Metall., 2002, vol. 50 (1), pp. 121–31 E.A. Trillo, L.E. Murr, A.H. Bujanda, N.E. Martinez: Acta Metall., 2002, vol. 50 (1), pp. 121–31
23.
Zurück zum Zitat L.E. Murr, A.A. Bujanda, E.A. Trillo, N.E. Martinez: J. Mater. Sci. Lett., 2002, vol. 21, pp. 559–63CrossRef L.E. Murr, A.A. Bujanda, E.A. Trillo, N.E. Martinez: J. Mater. Sci. Lett., 2002, vol. 21, pp. 559–63CrossRef
24.
Zurück zum Zitat B. Gonzales, L.E. Murr, O.L. Valerio, E.V. Esquivel, H. Lopez: Mater. Character., 2003, vol. 49 (4), pp. 359–66. CrossRef B. Gonzales, L.E. Murr, O.L. Valerio, E.V. Esquivel, H. Lopez: Mater. Character., 2003, vol. 49 (4), pp. 359–66. CrossRef
25.
Zurück zum Zitat E.V. Esquivel, L.E. Murr, E.A. Trillo, M. Baquera: J. Mater. Sci., 2003, vol. 38, pp. 2223–31. CrossRef E.V. Esquivel, L.E. Murr, E.A. Trillo, M. Baquera: J. Mater. Sci., 2003, vol. 38, pp. 2223–31. CrossRef
26.
Zurück zum Zitat O.L. Valerio-Flores, L.E. Murr, V.S. Hernandez, S.A. Quinones: J. Mater. Sci., 2004, vol. 39, pp. 6271–80. CrossRef O.L. Valerio-Flores, L.E. Murr, V.S. Hernandez, S.A. Quinones: J. Mater. Sci., 2004, vol. 39, pp. 6271–80. CrossRef
27.
Zurück zum Zitat E. Ferreyra, T., L.E. Murr, E.P. Garcia, and F. Hörz: J. Mater. Sci., 1997, vol. 32, pp. 2573–85 E. Ferreyra, T., L.E. Murr, E.P. Garcia, and F. Hörz: J. Mater. Sci., 1997, vol. 32, pp. 2573–85
28.
Zurück zum Zitat L.E. Murr, C.-S. Niou, E. Ferreyra, T., E.P. Garcia G. Liu F. Hörz, and R.P. Bernhard: J. Mater. Sci., vol. 32, pp. 3143–56 L.E. Murr, C.-S. Niou, E. Ferreyra, T., E.P. Garcia G. Liu F. Hörz, and R.P. Bernhard: J. Mater. Sci., vol. 32, pp. 3143–56
29.
Zurück zum Zitat F. Martinez, L.E. Murr, A. Ramirez, M.I. Lopez, S.M. Gaytan, B.F. Schuster: Mater. Sci. Eng., 2007, vol. A454–455, pp. 581–89 F. Martinez, L.E. Murr, A. Ramirez, M.I. Lopez, S.M. Gaytan, B.F. Schuster: Mater. Sci. Eng., 2007, vol. A454–455, pp. 581–89
30.
Zurück zum Zitat S. Pappu, L.E. Murr, S. Sen, D. Kapoor, L.S. Magness: Mater. Sci. Eng. A, 2001, vol. 298, pp. 144–57. CrossRef S. Pappu, L.E. Murr, S. Sen, D. Kapoor, L.S. Magness: Mater. Sci. Eng. A, 2001, vol. 298, pp. 144–57. CrossRef
31.
Zurück zum Zitat E.A. Trillo, E.V. Esquivel, L.E. Murr, L.S. Magness: Mater. Character., 2002, vol. 48, pp. 407–21. CrossRef E.A. Trillo, E.V. Esquivel, L.E. Murr, L.S. Magness: Mater. Character., 2002, vol. 48, pp. 407–21. CrossRef
32.
Zurück zum Zitat R.S. Rinehart, J. Pearson: Explosive Working of Metals, Pergamon, New York, NY, 1963, pp. R.S. Rinehart, J. Pearson: Explosive Working of Metals, Pergamon, New York, NY, 1963, pp.
33.
Zurück zum Zitat S.H. Carpenter: Shock Waves and High-Strain-Rate Phenomena in Metals, M.A. Meyers and L.E. Murr, eds., Plenum Press, New York, NY, 1981, pp. 941–59. S.H. Carpenter: Shock Waves and High-Strain-Rate Phenomena in Metals, M.A. Meyers and L.E. Murr, eds., Plenum Press, New York, NY, 1981, pp. 941–59.
34.
35.
Zurück zum Zitat E.V. Esquivel, L.E. Murr: Mater. Sci. Technol., 2006, vol. 22 (4), pp. 438–52. CrossRef E.V. Esquivel, L.E. Murr: Mater. Sci. Technol., 2006, vol. 22 (4), pp. 438–52. CrossRef
36.
Zurück zum Zitat S. Pappu, C. Kennedy, L.E. Murr, L.S. Magness, D. Kapoor: Mater. Sci. Eng. A, 1999, vol. 262, pp. 115–28. CrossRef S. Pappu, C. Kennedy, L.E. Murr, L.S. Magness, D. Kapoor: Mater. Sci. Eng. A, 1999, vol. 262, pp. 115–28. CrossRef
37.
Zurück zum Zitat S. Pappu, L.E. Murr: Mater. Sci. Eng. A, 2000, vol. 284, pp. 148–57CrossRef S. Pappu, L.E. Murr: Mater. Sci. Eng. A, 2000, vol. 284, pp. 148–57CrossRef
38.
Zurück zum Zitat N.V. Naumovich, A.I. Yadevich, N.M. Chigrinova: in Shock Waves for Industrial Applications, L.E. Murr, ed., Noyes Publications, Park Ridge, NJ, 1988, p. 170. N.V. Naumovich, A.I. Yadevich, N.M. Chigrinova: in Shock Waves for Industrial Applications, L.E. Murr, ed., Noyes Publications, Park Ridge, NJ, 1988, p. 170.
39.
Zurück zum Zitat D.G. Brasher, D.J. Butler, A.W. Hane: in Shock Waves for Industrial Applications, L.E. Murr, ed., Noyes Publications, Park Ridge, NJ, 1988, p. 216. D.G. Brasher, D.J. Butler, A.W. Hane: in Shock Waves for Industrial Applications, L.E. Murr, ed., Noyes Publications, Park Ridge, NJ, 1988, p. 216.
40.
Zurück zum Zitat C.G. Rhodes, M.W. Mahoney, W.H. Bingel, R.A. Spurling, C.C. Bampton: Scripta Mater., 1997, vol. 36, pp. 69–73. CrossRef C.G. Rhodes, M.W. Mahoney, W.H. Bingel, R.A. Spurling, C.C. Bampton: Scripta Mater., 1997, vol. 36, pp. 69–73. CrossRef
41.
Zurück zum Zitat G. Liu, L.E. Murr, C-S. Niou, J.C. McClure, F.R. Vega: Scripta Mater., 1997, vol. 37, pp. 355–59CrossRef G. Liu, L.E. Murr, C-S. Niou, J.C. McClure, F.R. Vega: Scripta Mater., 1997, vol. 37, pp. 355–59CrossRef
42.
Zurück zum Zitat W. Tang, X. Guo, J.C. McClure, L.E. Murr, A. Nunes: J. Mater. Process. Manuf. Sci., 1998, vol. 7, pp. 163–75CrossRef W. Tang, X. Guo, J.C. McClure, L.E. Murr, A. Nunes: J. Mater. Process. Manuf. Sci., 1998, vol. 7, pp. 163–75CrossRef
43.
Zurück zum Zitat L.E. Murr, G. Liu, J.C. McClure: J. Mater. Sci., 1997, vol. 16, pp. 1801–13 L.E. Murr, G. Liu, J.C. McClure: J. Mater. Sci., 1997, vol. 16, pp. 1801–13
44.
Zurück zum Zitat L.E. Murr, G. Sharma, F. Contreras, M. Guerra, S.H. Kazi, M. Siddique, F.D. Flores, D.J. Shindo, K.F. Soto, E.A. Trillo, C. Schmidt, J.C. McClure: Aluminum 2001–Proc. TMS 2001: Aluminum Automotive and Joining Sessions, S.K. Das, J.G. Kaufman, T.J. Lienert eds., TMS, Warrendale, PA, 2001, p. 197. L.E. Murr, G. Sharma, F. Contreras, M. Guerra, S.H. Kazi, M. Siddique, F.D. Flores, D.J. Shindo, K.F. Soto, E.A. Trillo, C. Schmidt, J.C. McClure: Aluminum 2001–Proc. TMS 2001: Aluminum Automotive and Joining Sessions, S.K. Das, J.G. Kaufman, T.J. Lienert eds., TMS, Warrendale, PA, 2001, p. 197.
45.
Zurück zum Zitat R.A. Prado, L.E. Murr, K.F. Soto, J.C. McClure: Mater. Sci. Eng. A, 2003, vol. 349, pp. 156–64CrossRef R.A. Prado, L.E. Murr, K.F. Soto, J.C. McClure: Mater. Sci. Eng. A, 2003, vol. 349, pp. 156–64CrossRef
46.
Zurück zum Zitat P.S. Follansbee: in Metallurgical Applications of Shock-Wave and High-Strain-Rate Phenomena, L.E. Murr, K.P. Staudhammer M.A. Meyers eds., Marcel Dekker, New York, NY, 1986, p. 451. P.S. Follansbee: in Metallurgical Applications of Shock-Wave and High-Strain-Rate Phenomena, L.E. Murr, K.P. Staudhammer M.A. Meyers eds., Marcel Dekker, New York, NY, 1986, p. 451.
47.
Zurück zum Zitat E.V. Esquivel, L.E. Murr: Mater. Sci. Eng. A, 2005, vol. 409, pp. 13–23. CrossRef E.V. Esquivel, L.E. Murr: Mater. Sci. Eng. A, 2005, vol. 409, pp. 13–23. CrossRef
48.
Zurück zum Zitat J.C.M. Li: in Science and Technology of Interfaces, S. Ankem, C.S. Pande, I. Ovid’ko S. Ranganathan eds., TMS, Warrendale, PA, 2002, p. 255. J.C.M. Li: in Science and Technology of Interfaces, S. Ankem, C.S. Pande, I. Ovid’ko S. Ranganathan eds., TMS, Warrendale, PA, 2002, p. 255.
49.
Zurück zum Zitat J.C.M. Li: in Frontiers in Materials Science, L.E. Murr and C. Stein, eds., Marcel Dekker, Inc., New York, NY, 1976, p. 527 J.C.M. Li: in Frontiers in Materials Science, L.E. Murr and C. Stein, eds., Marcel Dekker, Inc., New York, NY, 1976, p. 527
Metadaten
Titel
Dynamic Recrystallization: The Dynamic Deformation Regime
verfasst von
L.E. Murr
C. Pizaña
Publikationsdatum
01.11.2007
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 11/2007
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-007-9185-7

Weitere Artikel der Ausgabe 11/2007

Metallurgical and Materials Transactions A 11/2007 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.