Formation of Whiskers and Hillocks on the Surface of Sn-6.6RE Alloys

verfasst von: T.H. Chuang, C.C. Chi, H.J. Lin

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 3/2008

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

As-cast Sn-6.6Ce, Sn-6.6Lu, and Sn-6.6La alloys contain peritectic structures of near β-Sn matrix embedded with CeSn3, Lu4Sn5, and LaSn3 clusters, respectively, among which those of LaSn3 are the smallest in size. After air storage at room temperature, Sn-6.6Ce and Sn-6.6Lu reveal a much higher tendency than Sn-6.6La to form long threadlike whiskers on the surface of CeSn3 phase. Sn-6.6La shows the earlier appearance of coarse hillocks during storage at 150 °C in comparison to the Sn-6.6Ce and Sn-6.6Lu, but these hillocks cease to grow after a short duration. In contrast, the hillocks in Sn-6.6Ce and Sn-6.6Lu can grow to large sizes. This discrepancy correlates to the lower oxidation rate of LaSn3 intermetallic phase than those of CeSn3 and Lu4Sn5, which is attributed to the higher chemical activity of La as compared to Ce and Lu. In addition, the smaller size of the LaSn3 clusters also leads to the lower amount of tin atoms released and lower compressive stress accumulated after oxidation, which result in the slower whisker and hillock growth in Sn-6.6La alloy as compared to those in Sn-6.6Ce and Sn-6.6Lu.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat C.M.L. Wu, D.Q. Yu, C.M.T. Law, L. Wang: J. Mater. Res., 2002, vol. 17 (12), pp. 3146–54CrossRef C.M.L. Wu, D.Q. Yu, C.M.T. Law, L. Wang: J. Mater. Res., 2002, vol. 17 (12), pp. 3146–54CrossRef
2.
Zurück zum Zitat C.M.L. Wu, D.Q. Yu, C.M.T. Law, L. Wang: J. Electron. Mater., 2002, vol. 31 (9), pp. 928–32CrossRef C.M.L. Wu, D.Q. Yu, C.M.T. Law, L. Wang: J. Electron. Mater., 2002, vol. 31 (9), pp. 928–32CrossRef
3.
Zurück zum Zitat Z.G. Chen, Y.W. Shi, Z.D. Xia, Y.F. Yan: J. Electron. Mater., 2002, vol. 31 (10), pp. 1122–28CrossRef Z.G. Chen, Y.W. Shi, Z.D. Xia, Y.F. Yan: J. Electron. Mater., 2002, vol. 31 (10), pp. 1122–28CrossRef
4.
Zurück zum Zitat M.A. Dudek, R.S. Sidhu, N. Chawla: JOM, 2006, vol. 58 (6), pp. 57–62CrossRef M.A. Dudek, R.S. Sidhu, N. Chawla: JOM, 2006, vol. 58 (6), pp. 57–62CrossRef
5.
Zurück zum Zitat T.H. Chuang, S.F. Yen: J. Electron. Mater., 2006, vol. 35 (8), pp. 1621–27CrossRef T.H. Chuang, S.F. Yen: J. Electron. Mater., 2006, vol. 35 (8), pp. 1621–27CrossRef
6.
7.
8.
Zurück zum Zitat N. Vo, M. Kwoka, P. Bush: IEEE Trans. Electron. Packag. Manufact., 2005, vol. 28 (1), pp. 3–9CrossRef N. Vo, M. Kwoka, P. Bush: IEEE Trans. Electron. Packag. Manufact., 2005, vol. 28 (1), pp. 3–9CrossRef
9.
Zurück zum Zitat Constitution of Binary Alloys, M. Hansen and K. Anderko, eds., McGraw-Hill, New York, NY, 1958, pp. 461–62 Constitution of Binary Alloys, M. Hansen and K. Anderko, eds., McGraw-Hill, New York, NY, 1958, pp. 461–62
10.
Zurück zum Zitat Constitution of Binary Alloys, M. Hansen and K. Anderko, eds., McGraw-Hill, New York, NY, 1958, pp. 891–92 Constitution of Binary Alloys, M. Hansen and K. Anderko, eds., McGraw-Hill, New York, NY, 1958, pp. 891–92
Metadaten
Titel
Formation of Whiskers and Hillocks on the Surface of Sn-6.6RE Alloys
verfasst von
T.H. Chuang
C.C. Chi
H.J. Lin
Publikationsdatum
01.03.2008
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 3/2008
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-007-9426-9

Weitere Artikel der Ausgabe 3/2008

Metallurgical and Materials Transactions A 3/2008 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.